1.
研究了Pd部分替代Mg对Mg0.9-xTi0.1PdxNi(x=0.04~0.1)贮氢合金腐蚀性能的影响.利用机械合金化方法制备了Mg0.9-xTi0.1PdxNi(x=0.04~0.1)贮氢合金.XRD和TEM分析表明经120 h球磨后该合金完全非晶化.循环充放电测试结果表明,Pd的替代有效地延长了Mg0.9-xTi0.1PdxNi(x=0.04~0.1)合金的循环寿命.采用开路电位测量,阳极极化,电化学阻抗和X射线光电子能谱研究了该合金的腐蚀行为.结果表明,随着Pd含量增加,合金腐蚀电位正移,初始腐蚀电流下降,腐蚀电流增加的速度变缓.采用本文提出的等效电路模型较好地拟合了合金的电化学阻抗谱.分析表明,随着Pd含量的增加,合金表面钝化膜厚度和电阻逐渐增大.X射线光电子能谱分析表明,Pd的加入减弱了合金在充放电过程中的氧化程度.当Pd含量达到0.1时,Mg0.9-xTi0.1PdxNi(x=0.04~0.1)合金的耐腐蚀性能最好,其放电容量保持率最高. 相似文献
2.
Mg-based hydrogen storage alloys Mg0.9Ti0.1-xZrxNi (x=0.02, 0.04, 0.06) were successfully prepared by means of mechanical alloying (MA). The effects of Zr addition on the discharge capacity and the cycle performance of the Mg-based electrodes were also studied. It was found that the discharge capacities were improved with addition of a small amount of Zr and the cycle performances of the alloy were stabilized with the addition of Ti. The effects of surface modification or coating on the properties of Mg0.9Ti0.06Zr0.04Ni were also studied. The results indicated that coating with graphite improved both the discharge capacity and cycle life of the amorphous Mg0.9Ti0.06Zr0.04Ni electrode. 相似文献
3.
用机械合金化法合成了Mg0.9Ti0.1Ni0.9X0.1(X=Mn,
Zn, Co, Fe)系列合金. X射线衍射(XRD)结构分析表明, 用X部分替代Ni后,
促进了Mg0.9Ti0.1Ni合金的非晶化过程. 用Co和Fe部分替代Ni提高了合金的放电容量,
但却降低了合金的循环稳定性. 用Zn和Mn部分替代Ni提高了合金电极的循环寿命,
尤其是Mg0.9Ti0.1Ni0.9Zn0.1合金电极经10个充放电循环后,
其放电容量仍可达到313.8 mA·h/g. 对添加Co后的合金进行p-c-T测试发现,
Mg0.9Ti0.1Ni0.9Co0.1合金的吸放氢容量明显比Mg0.9Ti0.1Ni合金高,
这与电化学所测到的结果一致. 相似文献
4.
以合成的氯代二异丙基膦为原料, 利用电化学全氟化方法, 得到全氟二异丙基膦酸锂(Li[(C3F7)2PF4]), 并对其物理和电化学性能进行了研究. 相似文献
5.
The layered trivanadate, LiV3O8, was prepared by sol-gel method with LiOH, V2O5 and H2O2 as initial reagents. The materials at different heat treatment conditions were characterized by XRD and TG-DTA. Their electrochemical behaviors were studied by galvanostatic charge-discharge and cyclic voltammetry. The results show that LiV3O8 prepared by sintering at 300 ℃ for 16 h has higher capacity, and its initial discharge capacity is 333.1 mAh·g-1, and maintains a discharge capacity of 302.8 mAh·g-1 after 10 cycles at 0.2 C and the voltage range of 1.8~4.0 V. 相似文献
6.
我国金属氢化物化学研究 总被引:6,自引:0,他引:6
综述了我国金属氢化物化学的发展。我国是从50年代中期开始研究离子型金属氢化物的合成、性能和应用的,发展了一些合成方法,获得了多项中国专利。储氢合金的化学研究是70年代中期开始的。在储氢合金的化学合成、吸放氢热力学与动力学、储氢合金氢化催化和电化学方面都有较深入的研究,特别是储氢电极合金电化学及其在Ni/MH可逆电池中的应用研究,在国家863计划强有力的支持下,某些方面进入了国际先进行列。 相似文献
7.
8.
新型镁基储氢合金的合成及电化学性能的研究 总被引:17,自引:1,他引:16
用扩散法成功地合成了Mg1.5Al0.5-xNiVx(x=0,0.1,0.2,0.3,0.4)系列合金。XRD结构分析表明,合金中出现一个新的物相,其化学式为Mg3AlNi2,属立方晶系,Fd3m空间群,新相具有很好的电化学性能。钒的添加使合金的容量进一步提高。未经任何预处理的Mg1.5Al0.3V0.2Ni合金的最大放电容量达到333mA·h·g-1(50mA·g-1,-0.5Vvs.Hg/HgO).Al对六方晶系Mg2Ni合金结构中Mg的部分取代对于延长合金的循环寿命有重要作用。 相似文献
9.
选用非晶态的Mg0.9Ti0.1Ni0.85Co0.15合金粉末与石墨粉及镍粉进行球磨表面包覆。SEM分析结果表明,己包覆石墨和镍粉的合金表面上吸附着一层小的颗粒,形成薄层将原来的合金表面包覆起来。使用XPS分析了合金表面元素。结果表明,包覆石墨粉后,合金表面碳元素的质量分数和原子分数均增加,Mg的质量分数从22.74%减小至22.23%,原子分数从36.43%减小到32.94%,从而减小了Mg在碱液中的腐蚀几率,提高合金的抗腐蚀性能;包覆镍粉后,合金表面Ni的质量分数由59.89%增加到60.04%,原子分数由40.63%增加到41.02%,形成合金表面富Ni的保护层,提高了合金的抗腐蚀性能。充放电循环测试表明,循环30周后,包覆石墨粉的合金电极容量保持率为32.05%,包覆镍粉的合金电极容量保持率为41.26%,而未包覆的电极容量保持率仅为17.88%。合金电极极化曲线测试结果表明,石墨或镍粉的包覆提高了Mg0.9Ti0.1Ni0.85Co0.15合金电极的循环稳定性和在KOH碱液中的抗腐蚀性能。 相似文献
10.