红磷增效Al（OH）3／Mg（OH）2阻燃的聚丙烯结晶形态

借助宽角Ｘ－射线衍射、差热分析、偏光显微镜对红磷增效Ａｌ（ＯＨ）ａ和Ｍｇ（ＯＨ）２混合填充的阻燃聚丙烯体系的结晶形态进行了研究。发现这种体系中不仅出现ａ型而且还出现β型聚丙烯晶体。β型晶体可能是由于Ａｌ（ＯＨ）ａ和Ｍｇ（ＯＨ）ａ协同诱发而生成的。     

机械球磨与反应烧结合成Sr2CeO4发光体的研究

Sr₂CeO₄ phosphor was synthesized by mechanical milling and reactive sintering in this work. The solid state reaction of SrCO₃and CeO₂ (2∶1) started at about 850 ℃ and completed at 1 000 ℃ for about 4 h. Two types of formation mechanism of Sr₂CeO₄ were proposed. When the starting powder mixture was fired above 1 000 ℃, the unstable intermediate phase SrCeO₃was developed, which then reacted with SrCO₃to form the final product Sr₂CeO₄, however, SrCO₃and CeO₂ converted directly to Sr₂CeO₄ at a lower temperature. The XRD results showed the crystal structure of Sr₂CeO₄ was orthorhombic. The emission spectra displayed a broad band with maximum at about 465 nm. The mechanical milling of starting power mixture and the sintering temperature had no effect on this emission spectra.     

在肽库中进行小肽筛选的初步研究

以合成六肽ＤＧＧＳＡＡ为模型对在噬菌体肽库中进行小肽筛选做了初步研究。结果表明，含有可形成氢键和离子键残基的小肽能够在噬菌体肽库中进行筛选。并用明显提高了筛选的专一性。     

水溶性高聚物的研究进展

自八十年代初，水溶性高聚物再次成为高分子科学研究热点，评述了水溶性高聚物，特别是疏水缔合型改性水溶性高聚物的最新进展。     

银微电极微分电位溶出分析法研究

本文首次报道了银微电极微分电位溶出分析法。用化学刻蚀法方便地制作了银微电极，用于ＤＰＳＡ具有背景值低，分辨率好、精密度及灵敏度高，在不搅拌，仅需一定酸度而酸度而无其它介质的条件下就能测试等优点，对人工试样及自来水样分析，结果令人满意。     

POLYMERIZATION OF OCTAFLUOROCYCLOBUTANE IN GLOW DISCHARGE Ⅱ. ESCA AND IR CHARACTERIZATION OF POLYMER STRUCTURE*

In a capacitively coupled discharge with external electrodes, He, H_2, N_2 or Ar were used as plasmagas, polymerization of octafluorocyclobutane was carried out under different conditions by varyingdischarge power, pressure, plasma gas and plasma-gas/monomer ratio. Structure of polymerizedproducts was characterized by IR spectroscopy and ESCA measurement. It was found that therewere six elements in the products, i.e. C, F, Si, O, N and H. The probably existed groups in poly-mers wer investigated. By analyzing the resolved peaks of C_(1S) region in ESCA spectra, effect of thereaction conditions on degree of branching of the polymerized products and the relationship of thepolymer structure wth the mechanism of the competitive ablation and polymerization process werestudied. In addition, polymer deposition process occurring in glow discharge was discussed.