Gain Characteristics of Er^3＋-Doped Phosphate Glass Fibres

An erbium-doped phosphate glass fibre has been drawn by the rod-in-tube technique in our laboratory. The gain for the Er^3＋-doped phosphate glass fibre with different pump powers and with different input signal wavelengths is investigated. The 2.2-cm-long fibre, pumped by a single-mode 980-nm fibre-pigtailed laser diode, can provide a net gain per unit length greater than 1.SdB/cm. The pump threshold is about 50mW at the wavelength of 1534nm, and below 70roW at 1550nm. The gain linewidth of the Er^3＋-doped phosphate glass fibre is greater than 34 nm and can cover the C band in optical communication networks.     

Spectroscopic properties of neodymium-doped tellurite glass fiber

Nd~(3+)-doped tellurite glass and a single mode tellurite glass fiber with a core diameter of 8 μm were prepared in this work. The 1.33-μm emission from the ~4F_(3/2)→~4I_(13/2) transition of Nd~(3+) with a spectral bandwidth of 55 nm in tellurite glass fiber is observed. The lifetime of 164 μs of ~4F_(3/2) level and quantum efficiency of about 100% are obtained.     

Broadband 1.5-um emission of erbium-doped TeO_2-WO_3-Nb_2O_5 glass for potential WDM amplifier

Erbium-doped glass showing the wider 1.5-um emission band is reported in a novel oxide system TeO2-WO3-Nb2O5 and their thermal stability and optical properties such as absorption, emission spectra, cross-sections and fluorescence lifetime were investigated. Compared with other glass hosts, the gain bandwidth properties of Er3+ in TWN glass is close to that of bismuth glasses, and larger than those of tellurite, germanate, silicate and phosphate glasses. The broad and flat 4I13/2-4I15/2 emission and the large stimulated emission cross-section of Er3+ ions around 1.5um can be used as host material for potential broadband optical amplifier in the wavelength-division-multiplexing (WDM) network system.     

Amplified spontaneous emission properties of a single mode Er3+-doped tellurite fiber

Spectral characteristics of the amplified spontaneous emission(ASE)from a novel single mode Er3+ doped tellurite fiber with D-type cladding is reported in this letter.When pumped at 980 nm,an ASE source that has nearly a 100-nm flat FWHM bandwidth is obtained with a fiber length of 30-60 cm. Variation of ASE spectra with pump powers and fiber lengths are measured.Output power up to 2.0 mW is obtained with a launched pump power of 660 mW.     

Three-level all-fiber laser at 915 nm based on polarization-maintaining Nd~(3+)-doped silica fiber

Nd3+-doped fiber lasers at around 900 nm based on the 4F3/2→4I9/2 transition have obtained much research attention since they can be used as the laser sources for generating pure blue fiber lasers through the frequency doubling.Here,an all-fiber laser at 915 nm was realized by polarization-maintaining Nd3+-doped silica fiber.A net gain per unit length of up to 1.0 dB/cm at 915 nm was obtained from a 4.5 cm fiber,which to our best knowledge is the highest gain coefficient reported in this kind of silica fiber.The optical-to-optical conversion efficiency varies with the active fiber length and the reflectivity of the output fiber Bragg grating(FBG),presenting an optimal value of 5.3%at 5.1 cm fiber length and 70%reflectivity of the low reflection FBG.Additionally,the linear distributed Bragg reflector short cavity was constructed to explore its potential in realizing single-frequency 915 nm fiber laser.The measurement result of longitudinal-mode properties shows it is still multi-longitudinal mode laser operation with 40 mm laser cavity.These results indicate that the Nd3+-doped silica fiber could be used to realize all-fiber laser at 915 nm,which presents potential to be the seed source of high-power fiber laser.     

掺铒重金属氧氟硅铋酸盐玻璃的光谱性质

研究了重金属氧氟硅铋酸盐玻璃 (50-x)SiO2 xBi2O3 50PbF2(x=0, 3, 5, 8, 10, 13, 15 mol%)中Er3+离子的吸收光谱、荧光光谱、荧光半高宽、荧光 寿命和热稳定性能.应用Judd Ofelt理论计算了玻璃的强度参数Ωt(t=2,4,6)，应用 McCumber计算了能级4I13/2→4I15/2跃迁的受激发射截面. 结果发现荧光半高宽与Ω6有较大联系，Ω6越大，荧光半高宽越宽.对Er3+ 关键词： 重金属氧氟硅铋酸盐玻璃 光谱性质 Er3+离子 Judd Ofelt参数     

Comparative study of spectroscopic properties of Er^3＋／Yb^3＋-codoped tellurite glass and fibres under 980nm excitation＊

A tellurite fibre of TeO_{2}－ZnO－La_{2}O_{3}－Li_{2}O glass codoped with 20000 ppm ytterbium and 5000 ppm erbium was fabricated by the suction casting and rod-in-tube technologies. The absorption spectrum of Er^{3+}/Yb^{3+} -codoped bulk glass has been measured. From the Judd－Ofelt intensity parameters, the spontaneous emission probability and radiative lifetime τ_{rad} of Er^{3+}:{}^{4}I_{13/2}→{}^{4}I_{15/2} transition for the bulk glass have been calculated. The emission fluorescence spectra and lifetimes around 1.5μm, and subsequent upconversion fluorescence in the range of 500－700nm were measured in fibres and compared with those in bulk glass. The changes in amplified spontaneous emission with fibre length and pumping power was also measured. It was found that the emission spectrum from erbium in fibres is almost twice as broad as the corresponding spectrum in bulk glass when pumped at 980nm.     

Er3+离子掺杂钡镓锗玻璃上转换发光机理研究

研究了Er³⁺离子掺杂钡镓锗玻璃的吸收光谱、拉曼光谱和上转换光谱.分析了Er³⁺离子在钡镓锗玻璃中的上转换发光机理.结果表明：玻璃的最大声子能量为828cm^-1，紫外截止波长为275nm.采用800nm和980nmLD激发玻璃样品，在室温下观察到强烈的上转换绿光和红光发射.随着Er³⁺离子浓度的增加，绿光发光强度先增加后减小，而红光发光强度呈单调递增趋势.能量分析表明：800nmLD激发产生的绿光主要源于Er³⁺离子4I_13/2能级的激发态吸收过程；红光发射主要源于Er³⁺离子4I_13/2能级与4I_11/2能级之间的能量转移过程.980nmLD激发产生的绿光主要源于Er³⁺离子4I_11/2能级之间的能量转移过程；而红光发射主要源于Er³⁺离子4I_13/2能级与4I_11/2能级之间的能量转移过程和4I_13/2能级的激发态吸收过程.通过量子效率分析，发现采用800nmLD激发Er³⁺离子掺杂浓度为1mol% 的样品时，上转换绿光发光效率最高. 关键词： 上转换发光机理 3+离子掺杂')" href="#">Er³⁺离子掺杂 钡镓锗玻璃     

Intense Green Upconversion Luminescence in Er^3＋：Yb^3＋ Codoped Fluorophosphate Glass Ceramic Containing SrTe5O11 Nanocrystals

Er^3＋ ：Yb^3＋ codoped tellurite-fluorophosphate （TFP） glass ceramic exhibits much stronger upconversion luminescence. The intensity of the 540nm green light and 651 nm red light of the TFP glass ceramic is 120 times and 44 times stronger than that of the fluorophospahte （FP） glass, respectively. XRD analysis shows that the nanocrystal in TFP glass ceramic is SrTe5O11. TFP glass ceramic also displays much higher upconversion fluorescence lifetime and crystallization stability. The narrow and strong peak at 540nm is very ideal for practical upconversion luminescence realization. This work is a new trial for exploring non-PbF2 involved nanocrystal upconversion glass ceramics.     

Tm3+/Yb3+共掺氧卤碲酸盐玻璃上转换发光研究

研究了Tm3+/Yb3+共掺氧卤碲酸盐玻璃的上转换发光光谱,分析了TmO3量对Tm3+/Yb3+共掺氧卤碲酸盐玻璃上转换发光的影响机理.结果表明:在Tm3+/Yb3+共掺氧卤碲酸盐玻璃的上转换发光中,Tm3+存在较强的浓度猝灭效应.随Tm2O3含量增加,Tm3+的上转换蓝光和红光强度先增加,后降低,在0.1 mol% Tm2O3达到最大.该结果有助于进一步提高Tm3+的上转换发光效率.