排序方式: 共有5条查询结果,搜索用时 6 毫秒
1
1.
High temperature characteristics of bilayer epitaxial graphene field-effect transistors on SiC Substrate
下载免费PDF全文
![点击此处可从《中国物理 B》网站下载免费的PDF全文](/ch/ext_images/free.gif)
In this paper,high temperature direct current(DC) performance of bilayer epitaxial graphene device on SiC substrate is studied in a temperature range from 25℃ to 200℃.At a gate voltage of-8 V(far from Dirac point),the drainsource current decreases obviously with increasing temperature,but it has little change at a gate bias of +8 V(near Dirac point).The competing interactions between scattering and thermal activation are responsible for the different reduction tendencies.Four different kinds of scatterings are taken into account to qualitatively analyze the carrier mobility under different temperatures.The devices exhibit almost unchanged DC performances after high temperature measurements at 200℃ for 5 hours in air ambience,demonstrating the high thermal stabilities of the bilayer epitaxial graphene devices. 相似文献
2.
Radio-Frequency Performance of Epitaxial Graphene Field-Effect Transistors on Sapphire Substrates
下载免费PDF全文
![点击此处可从《中国物理快报》网站下载免费的PDF全文](/ch/ext_images/free.gif)
We report dc and the first-ever measured small signal rf performance of epitaxial graphene field-effect transistors (GFETs), where the epitaxial graphene is grown by chemical vapor deposition (CVD) on a 2-inch c-plane sapphire substrate. Our epitaxial graphene material has a good flatness and uniformity due to the low carbon concentration during the graphene growth. With a gate length Lg = 100 nm, the maximum drain source current Ids and peak transconductance gm reach 0.92 A/mm and 0.143 S/mm, respectively, which are the highest results reported for GFETs directly grown on sapphire. The extrinsic cutoff frequency (fT) and maximum oscillation frequency (fmax) of the device are 12 GHz and 9.5 GHz, and up to 32 GHz and 21.5 GHz after de-embedding, respectively. Our work proves that epitaxial graphene on sapphire substrates is a promising candidate for rf electronics. 相似文献
3.
化学气相沉积(CVD)法是制备大面积、高质量石墨烯材料的主要方法之一,但存在衬底转移和碳固溶等问题,本文选用蓝宝石衬底弥补了传统CVD法的不足。利用CVD法在蓝宝石衬底上生长石墨烯材料,研究生长温度对石墨烯表面形貌和晶体质量的影响。原子力显微镜(AFM)、光学显微镜(OM)、拉曼光谱和霍尔测试表明,低温生长有利于保持材料表面的平整度,高温生长有利于提高材料的晶体质量。研究氢气和碳源对蓝宝石衬底表面刻蚀作用机理,发现氢气对蓝宝石衬底有刻蚀作用,而单纯的碳源不能对衬底产生刻蚀效果。在1200 ℃下,直径为50 mm的晶圆级衬底上获得平整度和质量相对较好的石墨烯材料,室温下载流子迁移超过1000 cm2·V-1·s-1。 相似文献
4.
陷阱效应导致的电流崩塌是制约GaN基微波功率电子器件性能提高的一个重要因素,研究深能级陷阱行为对材料生长和器件开发具有非常重要的意义.随着器件频率的提升,器件尺寸不断缩小,对小尺寸器件中深能级陷阱的表征变得越发困难.本文制备了超短栅长(Lg=80 nm)的AlGaN/GaN金属氧化物半导体高电子迁移率晶体管(MOSHEMT),并基于脉冲I-V测试和二维数值瞬态仿真对器件的动态特性进行了深入研究,分析了深能级陷阱对AlGaN/GaN MOSHEMT器件动态特性的影响以及相关陷阱效应的内在物理机制.结果表明,AlGaN/GaN MOSHEMT器件的电流崩塌随着栅极静态偏置电压的增加呈非单调变化趋势,这是由栅漏电注入和热电子注入两种陷阱机制共同作用的结果.根据研究结果推断,可通过改善栅介质的质量以减小栅漏电或提高外延材料质量以减少缺陷密度等措施达到抑制陷阱效应的目的,从而进一步抑制电流崩塌. 相似文献
5.
氮化镓(GaN)器件的自热问题是目前限制其性能的关键因素,在GaN材料上直接生长多晶金刚石改善器件的自热问题成为研究的热点,多晶金刚石距离GaN器件工作有源区近,散热效率高,但多晶金刚石和GaN材料热失配可能会导致GaN电特性衰退.本文采用微波等离子体化学气相沉积法,在2 in (1 in=2.54 cm)Si基GaN材料上生长多晶金刚石.测试结果显示,多晶金刚石整体均匀一致,生长金刚石厚度为9—81 μm,随着多晶金刚石厚度的增大, GaN (002)衍射峰半高宽增量和电性能衰退逐渐增大.通过激光切割和酸法腐蚀,将Si基GaN材料从多晶金刚石上完整地剥离下来.测试结果表明:金刚石高温生长过程中,氢原子对氮化硅外延层缺陷位置有刻蚀作用形成孔洞区域,刻蚀深度可达本征GaN层;在降温过程,孔洞周围形成裂纹区域.剥离下来的Si基GaN材料拉曼特征峰峰位, XRD的(002)衍射峰半高宽以及电性能均恢复到本征状态,说明多晶金刚石与Si基GaN热失配产生应力,引起GaN晶格畸变,导致GaN材料电特性衰退,这种变化具有可恢复性,而非破坏性. 相似文献
1