0Cr18Ni9不锈钢焊接温度场的数值仿真

基于有限元软件SYSWELD对不锈钢0Cr18Ni9平板TIG焊的温度场进行三维动态模拟,得出了瞬态温度场分布图和特征点的热循环曲线,同时也得出了焊缝上任一点的温度变化与相变的关系.与文献资料比较表明,所建立的数值模拟仿真模型可以较好的模拟焊接温度场,为研究焊接过程中的应力应变和减少焊接应力与变形提供了参考依据.     

Reverse-transformation austenite structure control with micro/nanometer size

To control the reverse-transformation austenite structure through manipulation of the micro/nanometer grain structure, the influences of cold deformation and annealing parameters on the microstructure evolution and mechanical properties of 316L austenitic stainless steel were investigated. The samples were first cold-rolled, and then samples deformed to different extents were annealed at different temperatures. The microstructure evolutions were analyzed by optical microscopy, scanning electron microscopy (SEM), magnetic measurements, and X-ray diffraction (XRD); the mechanical properties are also determined by tensile tests. The results showed that the fraction of stain-induced martensite was approximately 72% in the 90% cold-rolled steel. The micro/nanometric microstructure was obtained after reversion annealing at 820-870℃ for 60 s. Nearly 100% reversed austenite was obtained in samples annealed at 850℃, where grains with a diameter ≤ 500 nm accounted for 30% and those with a diameter >0.5 μm accounted for 70%. The micro/nanometer-grain steel exhibited not only a high strength level (approximately 959 MPa) but also a desirable elongation of approximately 45%.     

EIS and XPS studies on passive film of AISI 304 stainless steel in dilute sulfuric acid solution

Electrochemical impedance spectroscopy and XPS studies on AISI 304 stainless steel in naturally aerated 0.5 M H₂SO₄ solution were carried out at room temperature. The valuable model of the metal/solution interphase was established, and the reliable equivalent electrical circuits in the solution were presented. The analysis of the chemical composition of passive film on AISI 304 stainless steel was carried out by XPS. The passive film of AISI 304 stainless steel is composed of oxyhydroxides, Fe₂O_3, FeO, Cr₂O₃, NiO, sulfate, sulfite, and sulfide (FeS, NiS). It is reported that the ferrous sulfide film formed on AISI 304 stainless steel in the dilute sulfuric acid solution. The possible process in which sulfuric acid is reduced to sulfite and sulfide is proposed. The galvanic interaction of sulfide inclusions with the base alloy is introduced. Copyright © 2011 John Wiley & Sons, Ltd.     

Electrochemical and XPS studies on corrosion behaviours of AISI 304 and AISI 316 stainless steels under plastic deformation in sulphuric acid solution

The corrosion behaviours of austenitic stainless steels were investigated by electrochemical methods under plastic deformation with constant strain in the naturally aerated 0.5 M H₂SO₄ + 0.2 M KCl solution at room temperature. The work addresses the influence of plastic deformation and molybdenum element on the corrosion resistance of austenitic stainless steels in the test solution. Electrochemical impedance spectroscopy presents the decreasing charge transfer resistance (R_t) and polarization resistance (R_p) values with the immersion time for AISI 304 stainless steel under constant strain deformation, and the increasing R_t and R_p values with the immersion time for AISI 316 stainless steel. The analysis of the chemical composition of the corrosion products was carried out by XPS. Molybdenum addition in AISI 316 stainless steel affects significantly the corrosion resistance because of its high ability to form Mo (VI) and MoCl₅ insoluble compounds in acid medium. Copyright © 2011 John Wiley & Sons, Ltd.     

Corrosion protection performance of ceria‐copolymer bilayer coating on low nickel stainless steel in 0.5 M H2SO4 medium

In this paper, we have reported the anti‐corrosion performance of ceria / poly (indole‐co‐pyrrole) (Ce/(poly(In‐co‐Py)) bilayer coating on low nickel stainless steel (LN SS). Electrochemical polymerization of (poly (In‐co‐Py)) was achieved on ceria‐coated LN SS (CeO₂/LN SS) in acetonitrile medium containing LiClO₄ (ACN‐LiClO₄) by cyclic voltammetric technique. The coatings were characterized by analytical techniques like Fourier transform infrared spectroscopy, scanning electron microscopy with energy dispersive analysis of X‐ray, respectively. The mechanical behavior of the coatings was studied using peel test, hardness and wear resistance tests. The corrosion defensive performance of this bilayer coating on LN SS was investigated using electrochemical techniques such as potentiodynamic polarization and electrochemical impedance spectroscopy in 0.5 M H₂SO₄. These results show that the bilayer coating on LN SS lowered the permeability of corrosive ions present in the acidic medium and thus acts as a barrier against the attack of corrosive environment. Copyright © 2012 John Wiley & Sons, Ltd.     

Fabrication of high nitrogen austenitic stainless steels with excellent mechanical and pitting corrosion properties

A series of high nitrogen austenitic stainless steels were successfully developed with a pressurized electroslag remelting furnace. Nitride additives and deoxidizer were packed into the stainless steel pipes, and then the stainless steel pipes were welded on the surface of an electrode with low nitrogen content to prepare a compound electrode. Using Si₃N₄ as a nitrogen alloying source, the silicon contents in the ingots were prone to be out of the specification range, the electric current fluctuated greatly and the surface qualities of the ingots were poor. The surface qualities of the ingots were improved with FeCrN as a nitrogen alloying source. The sound and compact macrostructure ingot with the maximum nitrogen content of 1.21wt% can be obtained. The 18Cr18Mn2Mo0.9N high nitrogen austenitic stainless steel exhibits high strength and good ductility at room temperature. The steel shows typical ductile-brittle transition behavior and excellent pitting corrosion resistance properties.     

注射成形316L不锈钢粘结剂热脱脂行为和工艺

对石蜡 ( PW)基多组元粘结剂体系中组元的热脱脂行为和注射成形 316 L不锈钢的热脱脂工艺参数 ,包括样品厚度、温度和升温速率进行了研究。实验表明 ,温度和升温速率控制不当将导致脱脂缺陷的产生 ,温度小于 2 80℃时 ,脱脂量的对数与厚度的倒数成比例。     

反向凝固不锈钢复合带平整轧制有限元解析

利用ＡＮＳＹＳ有限元分析软件对反向凝固不锈钢复合带的平整轧制过程进行了变形 物理场分析,得出了复合带平整轧制时内部各点的塑性应变和应力分布：轧件内存在不均匀变 形,母带的应变大于凝固层,凝固层应变从表面向内部逐渐增大;在轧制变形区内,凝固层的应 力大于母带;轧件的残余应力约为 １９ ＭＰａ．轧制力的解析结果与实测的轧制力基本相符．     

316L不锈钢在Saline溶液中的微动磨蚀行为研究

采用球－平面接触微动磨损试验设备考察了轧制固溶３１６Ｌ不锈钢在Ｓａｌｉｎｅ溶液中的微动磨蚀行为。研究表明,３１６Ｌ不锈钢的微动过程存在显著的阶段性;微动初期为磨合期,第一稳定阶段摩擦副处于高摩擦应力状态,伴随着不锈钢表面缝隙腐蚀与弹塑性损伤的积累;第二过渡阶段和第二稳定阶段不锈钢表面呈微断裂剥层特征,腐蚀引起的微断裂不可忽视,不锈钢微动损伤表面形貌同微动损伤速率之间存在对应关系。     

Structural Characterization by SIMS of Alumina Coatings on Stainless Steel

Al₂O₃ coatings were obtained by the alkoxide route and deposited on stainless steel using the dip coating technique. The starting precursor was aluminum sec-butoxide modified by acrylic acid in order to prevent its precipitation in the presence of water.Useful information for the structural organization of alumina coatings on stainless steel is deduced from SIMS analysis. SIMS data reveal that the coating structure brings into play two different layers: an outer alumina layer that is more or less doped, mainly by iron, and an internal layer corresponding to the alumina/steel interphase. Beneath the interphase, the presence of an oxidized steel layer on the substrate surface is detected.Whatever the coating, the alumina/steel interphase exhibits a nearly constant thickness. On the other hand, a thickness variation of the oxidized steel layer is observed between samples under study: this thickness increases with the curing time of the coating.