Depth profiling of latex blends of fluorinated and fluorine‐free acrylates with laser‐induced secondary mass spectrometry

We explored phase separation and self‐assembly of perfluoroalkyl segments at the surface of polymer films obtained from latices of semifluorinated acrylate copolymers and the corresponding latex blends of nonfluorinated and semifluorinated polyacrylates. With laser‐induced secondary mass spectrometry the fluorine distribution was measured after annealing above the minimum film‐forming temperature of the polymers up to a depth of several micrometers. Depth profiles of a semifluorinated acrylate homopolymer and latex blends thereof with fluorine‐free alkylacrylates with 25, 50, and 75 mol % semifluorinated acrylate as well as a copolymer comprised of alkyl acrylate and semifluorinated acrylate (50/50 mol %) were investigated. In the case of latex blends containing both semifluorinated polyacrylates and fluorine‐free or low‐fluorine polymers, self‐assembly accounted for enrichment of the perfluoroalkyl segments at the surface. Coatings exhibiting low surface energy and having a substantially reduced total fluorine content were obtained. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 360–367, 2003     

电化学沉积Cu-In-Se薄膜

采用电化学沉积方法在钼箔上制备Cu-Se、In-Se和Cu-In-Se薄膜,对电沉积的工艺参数进行了测试,发现Cu-In-Se是一种诱导共沉积,虽然沉积膜不具备化学计量比,但具有一定的光电性能.     

Ethylene–propylene copolymerization with bis(β‐enaminoketonato) titanium complexes activated with modified methylaluminoxane

Ethylene–propylene copolymerization, using [(Ph)NC(R₂)CHC(R₁)O]₂TiCl₂ (R₁ = CF₃, Ph, or t‐Bu; R₂ = CH₃ or CF₃) titanium complexes activated with modified methylaluminoxane as a cocatalyst, was investigated. High‐molecular‐weight ethylene–propylene copolymers with relatively narrow molecular weight distributions and a broad range of chemical compositions were obtained. Substituents R₁ and R₂ influenced the copolymerization behavior, including the copolymerization activity, methylene sequence distribution, molecular weight, and polydispersity. With small steric hindrance at R₁ and R₂, one complex (R₁ = CF₃; R₂ = CH₃) displayed high catalytic activity and produced copolymers with high propylene incorporation but low molecular weight. The microstructures of the copolymers were analyzed with ¹³C NMR to determine the methylene sequence distribution and number‐average sequence lengths of uninterrupted methylene carbons. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5846–5854, 2006     

Graft polymerization of vinyl monomers inside macroporous polyacrylamide gel,cryogel, in aqueous and aqueous‐organic media initiated by diperiodatocuprate(III) complexes

Graft polymerization initiated by diperiodatocuprate(III) complex (Cu(III)) initiator was found to be an effective and convenient method for graft polymerization of vinyl monomers onto macroporous polyacrylamide gels, the so‐called cryogels (pAAm‐cryogels). The effect of time, temperature, monomer and initiator concentration during the graft polymerization in aqueous and aqueous‐organic media was studied. The graft polymerization of water‐soluble monomers as [2‐(methacryloyloxy)ethyl]‐trimethylammonium chloride, 2‐hydroxyethyl methacrylate, N‐isopropylacrylamide, and N,N‐dimethylacrylamide proceeds with higher grafting yield in aqueous medium, as compared with that in aqueous‐organic media. Graft polymerization in aqueous‐organic media such as water–DMSO solutions allows grafting of water‐insoluble monomers such as glycidyl methacrylate and N‐tert‐butylacrylamide with high grafting degrees of 100 and 410%, respectively. It was found that the deposition of initiator on the pore surface of cryogels promoted graft polymerization by facilitating the formation of the redox couple Cu(III)‐acrylamide group. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1952–1963, 2006     

Singlewall carbon nanotubes covered with polystyrene nanoparticles by in‐situ miniemulsion polymerization

This work is to make carbon nanotubes dispersible in both water and organic solvents without oxidation and cutting nanotube threads. Polystyrene‐singlewall carbon nanotube (PS‐SWNT) composites were prepared with three different methods: miniemulsion polymerization, conventional emulsion polymerization, and mixing SWNT with PS latex. The two factors, crosslinking and surface coverage of PS are important factors for the mechanical and electrical properties, including dispersion states of SWNT in various solvents. The PS‐SWNT composite prepared via a conventional emulsion polymerization showed SWNT bundles entirely covered with PS, whereas the PS‐SWNT composite prepared via a miniemulsion polymerization showed SWNT partially covered with crosslinked PS nanoparticles. The method of mixing SWNTs with PS latex did not show the well dispersed state of carbon nanotubes because PS was not crosslinked and was dissolved in a solvent, and nanotubes separated from PS precipitated. So the PS nanoparticle‐SWNT composite had lower electrical resistance, and higher mechanical strength than the other composites made by the latter two methods. As the amount of SWNT increases, the bare surface area of SWNT increases and the electrical conductivity increases in the composite made by the miniemulsion polymerization. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 573–584, 2006     

Precise synthesis of porphyrin array scaffolding polyisocyanides

Aryl isocyanides bearing free‐base and metallo‐porphyrins were prepared and polymerized with a Pd–Pt μ‐ethynediyl complex as the initiator to give polymers with narrow polydispersity indices. The molecular weights of the resulting polymers were precisely controlled by the initial feed ratio of the porphyrin monomer to the initiator. The UV–VIS spectra suggested that the porphyrin pendants are regularly arranged to form stacked columns. Metallo‐porphyrin polymers were also prepared by reacting free‐base porphyrin polymers with metal salts. The successive reactions of free‐base and zinc‐porphyrin monomers resulted in the formation of diblock polymers. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 585–595, 2006     

Stereocontrol of diene polymers by topochemical polymerization of substituted benzyl muconates and their crystallization properties

We report the stereocontrol of diene polymers by the topochemical polymerization of alkoxy-substituted benzyl muconates in the solid state. A monomer stacking structure is controlled by the weak intermolecular interactions in the monomer crystals, depending on the structure and position of the alkoxy-substituent. The translational and alternating types of molecular stacking structures in a column provide diisotactic and disyndiotactic polymers, respectively, by the solid-state polymerization under UV and γ-ray irradiation. On the other hand, the meso and racemo structures of the resulting polymers are determined by the molecular symmetry of the used muconate monomers. The various substituted benzyl ester polymers are transformed into the same ethyl ester polymers with the four types of tacticities. The structure and crystallization behavior of the substituted benzyl ester polymers as well as the ethyl ester polymers have been revealed in detail. We clarify the effects of the tacticity on the crystallization property of the stereoregular polymuconates. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4952–4965, 2006     

Synthesis and characterization of poly(ethylene oxide‐co‐ethylene carbonate) macromonomers and their use in the preparation of crosslinked polymer electrolytes

Methacrylate‐functionalized poly(ethylene oxide‐co‐ethylene carbonate) macromonomers were prepared in two steps by the anionic ring‐opening polymerization of ethylene carbonate at 180 °C, with potassium methoxide as the initiator, followed by the reaction of the terminal hydroxyl groups of the polymers with methacryloyl chloride. The molecular weight of the polymer went through a maximum after approximately 45 min of polymerization, and the content of ethylene carbonate units in the polymer decreased with the reaction time. A polymer having a number‐average molecular weight of 2650 g mol^?1 and an ethylene carbonate content of 28 mol % was selected and used to prepare a macromonomer, which was subsequently polymerized by UV irradiation in the presence of different concentrations of lithium bis(trifluoromethanesulfonyl)imide salt. The resulting self‐supportive crosslinked polymer electrolyte membranes reached ionic conductivities of 6.3 × 10^?6 S cm^?1 at 20 °C. The coordination of the lithium ions by both the ether and carbonate oxygens in the polymer structure was indicated by Fourier transform infrared spectroscopy. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2195–2205, 2006     

Synthesis and characterization of model 3‐miktoarm star copolymers of poly(dimethylsiloxane) and poly(2‐vinylpyridine)

3‐Miktoarm star copolymers, 3μ‐D₂V, with two poly(dimethylsiloxane) (PDMS) and one poly(2‐vinylpyridine) (P2VP) arm, were synthesized by using anionic polymerization–high vacuum techniques and (chloromethylphenylethyl)methyl dichlorosilane, heterofunctional linking agent, with two SiCl groups and one CH₂Cl group. The synthetic strategy involves the selective reaction of the two ? SiCl groups with PDMSOLi living chains, followed by reaction of the remaining chloromethyl group with P2VPLi. Combined molecular characterization results (size exclusion chromatography, membrane osmometry, and ¹H NMR spectroscopy) revealed a high degree of structural and compositional homogeneity. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 614–619, 2006