乙醇 /水混合溶剂沉淀制备纳米BaF2及粒径控制

采用水和乙醇混合溶剂沉淀的方法制备了不同粒径的BaF₂纳米粉体。用XRD、TEM和FSEM表征了粉体的粒径和形貌。研究了陈化时间、水和乙醇的体积比对BaF₂纳米粉体的粒径和形貌的影响。结果表明，随混合溶剂中乙醇含量升高，沉淀粒径减小。BaF₂沉淀粒径的倒数和溶剂介电常数的倒数呈线性关系，据此关系可以控制BaF₂纳米粉体的粒径。     

CaO和NaCl焙烧混合稀土精矿过程中的分解反应

用XRD和TG-DTA热分析技术, 研究了含独居石和氟碳铈镧矿的混合稀土精矿在100～1000 ℃焙烧过程中, 添加CaO, NaCl时, REPO4和REFCO3的分解反应. 研究结果表明: 不添加CaO和NaCl时, 仅在377～450 ℃范围内存在REFCO3的分解反应, 其产物是REOF, RE2O3, 以及Ce2O3进一步的氧化产物CeO2, 而REPO4不分解; 添加CaO后在660～750 ℃之间, CaO有3种分解作用: (1) CaO分解REPO4, 其产物是RE2O3和Ca3(PO4)2. (2) CaO分解REOF, 其产物是RE2O3和CaF2. (3) CaO和REOF的分解产物CaF2共同作用分解REPO4, 其分解产物为RE2O3, Ca5F(PO4)3; 添加CaO, NaCl后, 混合精矿的分解率明显提高, NaCl的作用是为反应体系提供了液相, 促进了固相反应物间的传质过程, 加快了反应速度. 与此同时NaCl还可能参加了CaO分解REPO4的反应.     

TiCl4-Cr还原偶联活泼卤化物及芳醛、芳酮的研究

低价钛化合物在有机合成和有机反应中有着广泛的应用。我们曾研究了低价钛对α,α,α-三卤甲基苯的脱卤偶联、对2,2-二芳     

Progress on phthalocyanine-conjugated Ag and Au nanoparticles: Synthesis,characterization, and photo-physicochemical properties

Phthalocyanine (Pc) complexes are an important class of dyes with numerous (e.g., biological, photophysical, and analytical) applications. Among the methods used to improve the properties of these complexes, one should mention the introduction of different substituents, variation of the central metal ion, ligand exchange, and conjugation to nanomaterials (e.g., carbon-based nanomaterials and metal nanoparticles (NPs)). This work briefly reviews Pc complex conjugation to Ag and Au NPs, highlights the different NP shapes, and discusses the diversity of conjugation approaches. Moreover, the use of UV–Vis spectroscopy, powder X-ray diffraction, X-ray photoelectron spectroscopy, transmission electron microscopy, atomic force microscopy, dynamic light scattering and Fourier transform infrared spectroscopy to characterize Pc-NP hybrids is summarized. The effect of conjugation on Pc photo-physicochemical properties (fluorescence, singlet oxygen generation, triplet state formation, and optical limiting behavior) is discussed, and future perspectives for the synthesis and applications of new hybrids are provided.     

Tetragonal low-temperature structure of LiAl

The cubic face-centered structure of LiAl (, at ) transforms into a tetragonal body-centered structure (I4₁/amd, , at ). This first-order phase transition at about during heating is probably the reason for the so-called “ anomalies” in some physical properties like specific heat, electrical resistivity and nuclear-spin lattice relaxation. This transition seems to be correlated with the composition Li:Al of the alloy and the amount of Li vacancies.     

高效液相色谱法测定糙米粉中的维生素

高效液相色谱法测定糙米粉中的维生素吴红京，唐根源，王勇（中国科学院福建物质结构研究所福州３５０００２）（福建药品检验所福州３５０００１）１前言众所周知，糙米粉有很高的营养价值，含有人体必需的多种维生素。用高效液相色谱法（ＨＰＬＣ）和薄层色谱法（ＴＬＣ...     

Preparation of Fe/B powders by mechanical alloying

Steels with a high boron content are valuable as a neutron shield in waste containers and as control absorbers in nuclear reactors. The purpose of this study was to obtain by mechanical alloying an iron powder with 50% boron (by weight) and then powder-metallurgy materials. The elementary powders were mixed in a high-energy mill for 36 h in an inert atmosphere. Samples were withdrawn at intervals, and the powder was characterized by differential thermal analysis, X-ray diffraction and electron microscopy. The Fe/B powders withdrawn at different intervals of milling were diluted with further additions of iron up to a final content of 10% boron. The mixtures were uniaxially compacted at 500 MPa; their green density was verified, and they were sintered in argon at 1150°C. Their physical properties (density and dimensional change) and bending strength were evaluated and microstructural studies and fracture tests were performed.     

纳米晶掺钇硬质合金粉末的制备

采用高能球磨法制备了纳米晶掺Y硬质合金粉末。用XRD，SEM和DTA等分析检测手段，研究了纳米晶掺Y硬质合金粉末的结构、形貌和相的变化。结果表明：高能球磨45h，可获得晶粒尺寸约为8nm的掺Y硬质合金粉末；微量Y的加入，有利于硬质合金粉末晶粒的细化；在25～45h范围内，随着高能球磨时间的延长，粉末晶粒尺寸减小，且掺Y硬质合金粉末的晶粒尺寸比未掺Y的硬质合金粉末晶粒尺寸要细一倍；高能球磨25h，粉末中Co的X射线衍射峰消失。高能球磨掺Y硬质合金粉末的DTA曲线在626℃出现了1个尖锐的放热峰。高能球磨掺Y硬质合金粉末固结之后，其合金晶粒细小，机械性能较好。     

Analysis of highly resolved x‐ray photoelectron Cr 2p spectra obtained with a Cr2O3 powder sample prepared with adhesive tape

By using modern XPS systems it is possible to obtain spectra with well‐resolved spin orbit, multiplet and field splitting even with powder samples mounted using adhesive tape. Measurement of Cr₂O₃ powder with the latest generation of XPS spectrometers, which are able to analyse non‐conductive powders with ultimate energy resolution, revealed multiplet splitting features and satellite emission in the Cr 2p spectrum. Therefore, peak‐fit analysis of Cr 2p XPS spectra of Cr(III) compounds requires a more appropriate approach and common practice has to be reconsidered. One possible way to analyse this spectrum is proposed, based on the experimental and theoretical work of other authors. Copyright © 2004 John Wiley & Sons, Ltd.     

The preparation of thick-film glass capillary columns

A detailed method for the routine preparation of glass capillary columns is presented. The method consists of coating a glass tube with quartz powder prior to pulling the tube into a capillary. The inner surface of the capillary consists of an even distribution of quartz particles fused to the walls. This surface has been found readily deactivated by standard procedures and ideal for the preparation of thick-film glass capillary columns. The method has been thoroughly tested in two independent laboratories to ensure that the procedures described are reproducible.