石墨和纳米碳中缺陷和电子密度随温度的变化

测量了石墨和纳米碳在不同温度下的正电子寿命谱,研究了石墨和纳米碳中缺陷和电子密度随温度的变化.结果表明,纳米碳中缺陷的开空间和缺陷浓度分别大于和高于石墨晶体;纳米碳的平均自由电子密度低于石墨晶体.当温度从25K升至295K时,石墨和纳米碳中的平均自由电子密度随温度的升高而下降:石墨晶体中的自由电子密度随温度的升高变化较小;纳米碳的自由电子密度随温度的升高变化较大.随着温度的升高,石墨和纳米碳中的热空位数量增多,而且这些空位可迁移至微孔洞的内表面使微孔洞的开空间增大.     

粉末微波滤波器的制备和特性

利用通电导线的电磁感应和铜粉的趋肤效应,试制了在超导量子计算实验系统中使用的粉末微波滤波器.滤波器的频率响应随频率升高而平缓下降,在1GHz左右衰减至-80dB.我们分析了滤波器的原理,并通过改变参数对滤波器性能的变化进行了详细的研究.     

直接置换法制备包覆型纳米铜-银双金属粉末

 以AgNO₃为主盐,采用直接置换法初步制备了包覆型纳米铜-银双金属粉末,分析了工艺条件对包覆效果的影响,并用透射电子显微镜、X射线能量色散谱仪和X射线衍射仪进行了表征。实验结果表明：纳米铜-银双金属粉末为包覆型结构,平均粒径约70 nm,分散性较好,表面银的原子分数达到74.28%。在洗涤过程中加入一定量的保护剂,有效解决了纳米铜粉的氧化问题。     

纳米晶ZrO2:Er3+-Yb3+的制备及其室温上转换发射

用化学共沉淀法制备了ZrO₂:Er³⁺-Yb³⁺纳米晶粉体，所制备的纳米晶粉体具有较强的室温上转换发射和红外发射.研究了样品的晶体结构和上转换发光性质随着Yb³⁺掺杂浓度和煅烧温度的变化关系.通过X射线衍射谱分析发现，经800℃煅烧2h后得到的ZrO₂:Er³⁺-Yb³⁺纳米晶是四方相和单斜相的混合结构，经950℃煅烧2h后得到的样品以单斜相为主，随着Y     

Disordered Magnetic Phase in Partially Oxidized Bulk Nanocrystalline Iron

Magnetically frozen partially disordered state was observed in nanocrystalline bulk iron prepared by ball-milling of microcrystalline Fe. Role of nanostructure and oxidized fraction is pointed out. Altough we have found a small constituent which is proportional to 1/T in the ZFC curve, the magnetization scaling with T ^3/2 at high fields and the hysteretic behavior in FC-ZFC curves signalizes the presence of frozen ferromagnet at low temperatures.     

Structure refinement of sub-cubic-mm volume sample at high pressures by pulsed neutron powder diffraction: application to brucite in an opposed anvil cell

Neutron powder diffraction measurements of 0.9 mm³ of mixture of deuterated brucite and pressure medium were conducted at pressures to 2.8 GPa, using an opposed anvil cell and a medium-resolution diffractometer at Japan Proton Accelerator Research Complex pulsed neutron source. Spurious-free diffraction patterns were successfully obtained and refined to provide all structural parameters including Debye–Waller factors. Tilting of hydroxyl dipoles of brucite toward one of the three nearest-neighbor oxygen anions was confirmed to be substantial at pressure as low as 1.5 GPa. By this application, technical feasibility to analyze such a small sample has been newly established, which would be useful to extend the applications of neutron diffraction at high pressures.     

Model of heating and ignition of conductive polydisperse powder in electrostatic discharge

Heating of a conductive polydisperse powder by electrostatic discharge (ESD) is modelled numerically. Powder packing is described using a discrete element model; powder resistance is defined by geometry of particle contacts and properties of plasma produced by electrical breakdown between neighbour particles. A set of parametric calculations in combination with experimental data is used to determine necessary adjustable model parameters. The model predicts the temperature for each powder particle resulting from its heating by the ESD current. Location and packing of individual particles within the powder affects greatly their achieved temperatures and thus the likelihood of ignition. Consistently with experiments, a trend showing that smaller particles are generally heated to higher temperatures at a given ESD energy is detected for coarser powders; this trend becomes less clear for finer powders with particle sizes less than the breakdown distance given by the Paschen curve in air. Comparison of the experimental data and calculations suggests that the transition from single particle to cloud combustion occurs when the distance between the particles ignited by ESD becomes close to the flame size for the individual burning particle. This distance, inversely proportional to the number of ignited particles, is primarily determined by the ESD energy.     

Optical and structural properties of nanocrystalline PbS thin film grown by CBD on Si(1 0 0) substrate

PbS nanocrystalline thin film was prepared by chemical bath deposition on Si(1?0?0) substrate at bath temperatures of 25, 45 and 65 °C. Triethanolamine was added to the aqueous solution, which decreased the grain size and increased the luminescence of the nanocrystalline PbS thin film. PbS nanocrystals were identified using XRD, TEM and AFM. The crystalline size of the PbS film deposited at different bath temperatures was estimated by XRD and TEM to be 7–12 nm. The growth mechanism of the PbS crystallites were described at different bath temperatures. The confinement was reflected in the absorption spectra, photoluminescence excitation and photoluminescence spectra. The luminescence of Si(1?0?0) substrate and PbS nanocrystalline film deposited on Si(1?0?0) were compared, and the results revealed that the PbS nanocrystals altered and notably enhanced the emission features of the Si(1?0?0) substrate. The shifting of the maximum photoluminescence emission wavelength of PbS nanocrystals with a change in bath temperature and the variation in photoluminescent intensity of PbS nanocrystals prepared at 25 °C versus deposition time were investigated. A single-peak fit of a Gaussian function was employed to discern the photoluminescence of PbS on Si(1?0?0) substrate.     

碳酸钾与魔芋精粉添加量对苦荞挂面品质的影响

按苦荞心粉65%、面粉30%、谷朊粉3.5%、食盐1.5%的比例,添加碳酸钾和魔芋精粉,通过均匀试验探讨制作高含量苦荞挂面配方以及干燥方式对苦荞挂面质量的影响。试验表明:添加碳酸钾和魔芋精粉可以降低苦荞挂面的熟断条率和烹饪损失率,延长苦荞挂面的烹调时间;碳酸钾和魔芋精粉添加量为苦荞心粉、面粉、谷朊粉、食盐总质量的0.30%和0.60%时,可以保证苦荞挂面的质量。     

铝粉点火微观机理的光谱研究

 铝粉是一种含能高的材料,它被广泛地添加到含能材料中。利用3台单色谱仪和OMA谱仪等多种谱仪技术,研究了铝粉在几种不同环境下的快速反应微观特性。研究表明：铝粉冲击波点火的临界条件和铝粉的物理状态相关。微米铝粉点火的临界温度为2 100 K,它接近Al₂O₃的熔化温度。它表明,在空气中容易氧化的微米铝粉点火,必须使铝粉表面的氧化层熔化。在气相反应中,微米铝粉和氧的反应是主要的;和水的反应是次要的。减小微米铝粉的颗粒尺寸,可以明显提高快速反应温度。 含铝复合燃料中的液体燃料反应后的铝粉才能参与反应;铝粉添加至气相反应介质后将明显提高反应温度。