通过热重实验和扫描电子显微等方法，研究了４种触头用银合金粉末的氧化性能及氧化后的组织结构。发现Ａｇ－Ｓｎ－ＲＥ合金粉末氧化以后，在粉末表层形成一层纯银层，其组织结构理想；它的氧化性能最好，适于制备触头材料。Ａｇ－Ｓｎ－ＲＥ合金粉末的优良氧化性能与其氧化后理想的组织结构有关。稀土元素可以降低合金粉末的氧化温度，其它影响作用有待于进一步研究。     

包覆Y(OH)3的球形Ni(OH)2的电化学性能

利用软嵌式粉末电极技术研究了Y(OH)3包覆对球形Ni(OH)2电化学性能的影响. 循环伏安结果表明, 在球形Ni(OH)2的氧化过程中存在Ni(Ⅲ)和Ni(Ⅳ)的两步氧化反应, 产生的Ni(Ⅳ)不稳定, 能分解产生NiOOH和氧气, 所以可将Ni(Ⅲ)→Ni(Ⅳ)看作副反应. Y(OH)3包覆层对Ni(OH)2氧化过程后期的副反应, 特别是Ni(Ⅲ)→Ni(Ⅳ)具有较好的抑制作用. 由包覆后的Ni(OH)2制成的模拟电池表现出很好的高温性能, 在1C充放电条件下, 当Y的摩尔分数为1.61%时, 在60 ℃时所对应的容量保持率可达到25 ℃的92.7％; 当Y的摩尔分数仅为0.55 %时, 在60 ℃时所对应的质量比容量也可达到241.3 mA·h/g.     

Kristallstrukturanalyse von Ammonium-catena-polyphosphat II mit Röntgenpulvertechniken

Crystal Structure Determination of Ammonium catena-Polyphosphate II by X-Ray Powder Techniques The first structure determination of one of the five modifications of ammonium-catena-polyphosphate was performed using X-ray powder diffraction data. (NH₄PO₃)_nII is formed by phase transformation of (NH₄PO₃)_nI which on its part is obtained by condensation of NH₄H₂PO₄ at 200°C in presence of urea. Modification II crystallizes in P2₁2₁2₁ (a = 1 207.9(1), b = 648.87(8), c = 426.20(4) pm; Z = 4; 291 observed reflections; R(p) = 0.089; R(wp) = 0.111; R(I, hkl) = 0.088). The chain-anion runs parallel to the shortest axis, the period of identity is two. The ammonium ion is surrounded by a distorted tetrahedron of oxygen atoms (N? O-distances range from 285 to 292 pm, hydrogen bonds of middle strength).     

溶胶-凝胶法合成纳米铬酸锶镧的工艺研究

以硝酸镧、硝酸铬、硝酸锶为原料，乙二醇为分散剂，柠檬酸为胶溶剂，用溶胶-凝胶法合成纳米级的铬酸锶镧粉体。利用TG，DSC，XRD分析研究了粉料的晶化过程。利用HREM分析了煅烧温度、含锶量对粉料粒径的影响。研究表明，获得纳米晶的最佳烧结温度在800℃。随着锶掺杂量的增加，粉料的粒径逐渐变小。     

纳米晶复合Nd2Fe14B/α-Fe合金制备与磁性能的研究

采用熔体快淬及晶化处理工艺制备Nd11Fe71Co8V1.5Cr1B7.5纳米晶合金。经21m·s-1快淬及640℃ 4min晶化处理后,制成的粘结磁体的磁性能最佳,为:Br=0.64T,JHc=903.5kA·m-1,(BH)max=71kJ·m-3。添加Cr元素可提高内禀矫顽力,从而提高最大磁能积。     

钙钛矿型LaNiO3、LaMnO3的形成条件

用混合硝酸盐分解法和柠檬酸络合法分别制取了单一钙铁矿型多晶粉末LaNiO_3和LaMnO_3. XRD分析表明LaNiO_3的形成经历了混合氧化物转化为LaNiO_3的同相反应; 而LaMnO_3晶相直接由无定形相转化而来。根据DTA、TG、IR分析两者的形成, NO_3~-离子都起了重要作用. 同时讨论了络合剂柠檬酸的作用.     

In situ neutron powder diffraction investigation of the hydration of tricalcium aluminate in the presence of gypsum

The hydration of a 1:3 molar ratio of tricalcium aluminate, Ca₃Al₂O₆, to gypsum, CaSO₄·2D₂O, was investigated at temperatures of 25, 50, and 80 °C using time-of-flight powder neutron diffraction combined with multiphase Rietveld structural refinement. It was shown that ettringite, Ca₆[Al(OD)₆]₂(SO₄)₃·∼26D₂O, was the first and only hydration product of the system, in contrast to a prior investigation which suggested the occurrence of a precursor phase prior to the formation of ettringite. Kinetics data showed that the hydration reaction is very sensitive to temperature: hydration at 25 °C was characterized by a single kinetic regime while hydration at higher temperatures consisted of two distinct kinetic regimes. The presence of two kinetic regimes was attributed to a change in either the dimensionality of the growth process or a change in the rate controlling mechanism in the hydration reaction.     

Structural and electrical changes in NdSrNiO4−δ by substitute nickel with copper

A novel series of the formula NdSrNi_1−xCu_xO_4−δ were synthesized for various values of x ranging from 0 to 1 in 1 atm of O₂ gas flow using conventional solid-state methods and were characterized by powder X-ray diffraction and electrical resistivity measurements. The compounds have been shown to adopt the K₂NiF₄-type structure. The oxygen stoichiometry of the compounds was determined from thermo-gravimetric analysis (TGA). An analysis of the micro-structure of the neodymium strontium nickel copper oxide is described. All the samples were semi-conducting from room temperature down to 77 K. The effect of Cu²⁺ incorporation on the structural and electrical properties of NdSrNi_1−xCu_xO_4−δ, 0?x?1, are discussed in terms of Jahn-Teller distortion of the (Ni/Cu)O₆ octahedra and mixed valence character of copper.     

配位-沉淀法制备Ni(OH)2和NiO超微粉

本工作采用配位 -沉淀法成功的制备了薄片形氢氧化镍和氧化镍超微粉末 ,通过 XRD、TG-DTA、IR及 TEM等实验手段对超微粉的组成结构进行分析表征。     

The ordered phase of methylammonium lead chloride CH3ND3PbCl3

The perovskite-structured compound methylammonium lead chloride orders into a low-temperature phase of space group Pnma, in which at 80 K each of the orthorhombic axes , and is doubled with respect to the room temperature disordered cubic phase (). The structure was solved by ab initio methods using the programs EXPO and FOX. This unusual cell basis for space group Pnma is not that of a standard tilt system. This phase, in which the methylammonium ions, are ordered shows distorted octahedra. The octahedra possess a bond angle variance of 60.663°² and a quadratic elongation of 1.018, and are more distorted than those in the ordered phase of methylammonium lead bromide. There is also an alternating long and short Pb-Cl bond along a, due to an off-center displacement of Pb within the octahedron. This suggests that the most rigid unit is actually the methylammonium cation, rather than the PbCl₆ octahedra, in agreement with existing spectroscopic data.