Microstructure of polymers obtained by cationic polymerization of endo-dicyclopentadiene

endo-Dicyclopentadiene (DCPD) was polymerized by various cationic initiating systems in different solvents. IR and ¹H NMR results show that four types of structural units are formed due to the corresponding addition modes: the addition on the norbornenic (NB) double bond generates unit I and rearranged unit II, while the addition on the cyclopentenic (CP) double bond produces unit III and rearranged unit IV. The reaction medium has a stronger effect on the microstructure of the polymer (PDCPD) than initiating systems. The polymers prepared in toluene and n-hexane contain all four structural units, while the polymer produced in methylene chloride is composed of structural units II and IV. © 1996 John Wiley & Sons, Inc.     

T10A钢成型模具的失效分析及热处理工艺的改进

结合T10A钢胶木成型模具的具体工作条件、性能要求和失效形式,采用性能(硬度)测试和金相显微分析等研究手段,分析了T10A钢胶木成型模具失效的主要原因,在失效分析和试验研究的基础上,有针对性的改进了T10A钢胶木成型模具的热处理工艺.研究结果表明,通过优化和改进模具的热处理工艺及其参数,有效地改善了胶木成型模具的使用性能,提高了模具的使用寿命.     

CuO添加对0.2(Na0.5La0.5)TiO3+0.8CeO2复合介质陶瓷微波性能影响的研究

采用固相合成法制备CuO掺杂的0.2(Na0.5La0.5)TiO3 0.8CeO2复合微波介质陶瓷材料.研究了CuO对该复合体系的烧结性能、微观结构和微波介电性能的影响.研究表明,CuO有效地降低了该复合体系的烧结温度,改善了体系的微观结构.随CuO含量的增加,体系的介电常数εr和Qf值均不断下降.当CuO的掺入量为0.25%(质量分数),在1 400℃烧结,保温2.5 h的条件下,在该复合体系中可得到εr=39.1,Qf=15130 GHz的最佳微波介电性能.     

基于同步辐射原位CT的水牛角结构性能关系研究

为探究水牛角的结构性能关系,基于上海同步辐射光源搭建了高分辨原位CT系统,对水牛角角鞘进行初始表征和准静态压缩下的实时表征,并通过Top-Hat方法提取了角鞘内孔洞三维形貌.结果显示,水牛角角鞘孔隙率在1％左右,椭圆柱状孔洞沿牛角生长方向排列成线,首尾相连却并未连通,均匀分布在波浪状片层之间.孔洞特征椭球的轴长分布满足...     

稀土氧化物对氧化铝复相陶瓷显微结构和力学性能的影响

研究了Y2O3,CeO2,La2O3等稀土氧化物及复合稀土氧化物对热压烧结法制备氧化锆增韧氧化铝复相陶瓷力学性能和显微组织的影响.结果表明,适量的稀土氧化物添加剂可改善氧化铝陶瓷的显微结构,加速烧结,有利于致密化并保持较好的力学性能.不同稀土氧化物及添加量对氧化铝陶瓷的显微结构和力学性能具有不同的影响.     

CuPCr钢显微组织对全浸海水腐蚀行为的影响

为考察CuPCr型耐海水腐蚀钢不同显微组织的腐蚀行为,采用热轧后不同冷却方式分别获得贝氏体和铁素体+珠光体组织,进行模拟海水腐蚀的全浸加速腐蚀实验,并利用失重法测量腐蚀速率,采用SEM,XRD和电化学方法评价钢的腐蚀行为.结果表明:贝氏体组织能够在更短时间内形成比较致密的锈层,其耐蚀性能明显优于铁素体和珠光体组织.碳元素在贝氏体中的均匀分布减少了微电池数量,因而能够降低钢的腐蚀电流密度.     

Effects on the evolution of microstructure and properties of low-silicon cast aluminum alloys in service

ABSTRACT

The microstructure evolution and property change of four kinds of low silicon cast aluminum alloy exposed to heat for 0–50?h at 200°C were studied by means of Brinell hardness test, tensile property test, friction and wear property test and XRD analysis. The results show that with increasing thermal exposure time, the tensile strength of each group of samples decreased and the amount of wear increased. The tensile strength of samples with more Si content decreased slowly. When the time increased to 50?h, the increase of wear loss was the largest. The hardness of samples after thermal exposure increases compared with that before thermal exposure. The residual stress of (311) diffraction crystal surface of AlSi3.5Mg0.66 under different thermal exposure time was measured. The type of residual stress changed from residual tensile stress to residual compressive stress after thermal exposure. There is an abnormal phenomenon that the hardness of the sample increased and the amount of wear increased, and it is evident that the distribution of residual stress was inhomogeneous after thermal exposure. It is found that with increasing thermal exposure time to 50?h, the average lattice distortion ε of the low-index crystal plane and the high-index crystal plane in the aluminum alloys gradually increased.     

计及相变微结构演化的形状记忆合金本构描述

基于对NiTi形状记忆合金的实验观察及有限元分析,考虑两相间的应变不协调关系,采用应变修正法建立了计及片层状微结构的本构模型,本模型考虑了两相间的相互约束,及其约束随微结构演化的变化规律.研究了NiTi形状记忆合金微圆管在拉伸和扭转下的响应特性.计算结果与实验结果的对比表明所建本构模型较好地描述了伪弹性响应尤其是较好地描述了拉伸实验过程中的应力跌落现象.     

厚度对ZnS薄膜结构和应力的影响

用射频磁控溅射法在单晶Si基片上制备了4种不同厚度的ZnS膜,采用XRD和光学干涉相移法对薄膜的微结构和应力进行研究。结构分析表明,不同厚度的ZnS膜均呈多晶状态,并有明显的(220)晶面择优取向,晶体结构为立方晶型(闪锌矿)结构;随着薄膜厚度的增加,平均晶粒尺寸随之增大;薄膜的晶格常数在不同厚度下均比标准值稍大。应力分析表明,随着膜厚的增加,ZnS膜的应力差减小,在厚度为768 nm时的选区范围内应力差最小,应力分布较均匀。     

不同微结构纳米碳纤维电极的氧还原性能

采用催化化学气相沉积法制备了3种不同微结构的纳米碳纤维,利用高分辨透射电子显微镜和比表面测试等表征手段对纳米碳纤维的微结构和织构进行了分析;采用电化学循环伏安法对不同微结构纳米碳纤维电极的氧还原反应起始电位、峰电位和峰电流等参数进行了考察,并与石墨电极的氧还原性能进行了比较。结果表明:纳米碳纤维具有良好的氧化还原性能,微结构对纳米碳纤维的氧还原反应性能有着重要影响,这可能与不同微结构的纳米碳纤维具有不同的比表面和孔结构以及表面化学性能有关;同时纳米碳纤维也具有较好的电容性能。