天然橡胶/杜仲胶复合材料的制备及其阻尼性能研究

在天然橡胶(NR)中引入杜仲胶(EUG),以环氧化天然橡胶(ENR)/受阻酚AO-80(质量比为25∶20)为阻尼相,制备了NR/EUG/ENR/AO-80复合材料,并测定了复合材料的硫化特性、力学性能、结晶性能与动态力学性能。结果表明：复合材料在常温范围内具有较高的损耗因子与较宽的阻尼温域,当NR与EUG的质量比为60∶40时复合材料具有最大的损耗因子峰值,并且随着EUG含量的增加,总体上复合材料在常温范围内的储能模量逐渐增大;复合材料的玻璃化转变温度出现在-60℃附近,并且随着EUG含量的增加,复合材料开始出现EUG结晶的熔融峰,结晶度和熔融温度逐渐增大。扫描电子显微镜(SEM)测试结果表明复合材料的断面较为平整,ENR改善了两相的相容性;透射电子显微镜(TEM)测试结果表明NR与EUG两相之间具有明显的分界。复合材料在低应变下表现出高柔性的特点,同时具有较高的拉伸强度和拉断伸长率。     

松脂的催化歧化反应产物的气相色谱-质谱分析

采用气相色谱-质谱技术对松脂的催化歧化新工艺的反应产物进行分析,共分离出45个峰,鉴定出其中的38个化合物,并发现松脂歧化产物中歧化松节油的主要成分为对伞花烃,含量为16.26%;歧化松香的主要成分为脱氢枞酸和氢化树脂酸,其含量分别为41.58%和21.43%。在此基础上对松脂歧化反应过程进行了初步探讨,认为松脂原料中的酸性物质发生分子间氢转移反应,萜烯烃的存在促进了脱氢反应的进行;在树脂酸提供的酸性环境下松脂原料中中性油的主要成分双环单萜烯发生开环异构形成单环单萜烯,单环单萜烯再进行催化脱氢转化为对伞花烃。分析结果表明,直接以松脂为原料进行催化歧化反应可同时获得特级歧化松香和高含量的对伞花烃。     

羟丙基香豆胶的合成及结构表征

以天然香豆胶为原料,环氧丙烷(EP)为非离子醚化剂,NaOH为催化剂,异丙醇为分散剂制备了非离子型羟丙基香豆胶(HPFG).用MORGAN串联法测定HPFG的取代度(DS),研究了EP用量、NaOH用量、反应温度和反应时间对HPFG表观黏度和DS的影响.结果表明:当反应温度50℃,反应时间3 h,m(香豆胶)∶m(EP)∶m(异丙醇)∶m(NaOH)=1∶0.5∶1.7∶0.04时,制得的产品能满足油田工业评价指标要求,即表观黏度()η=560～1 000 mPa.s(w(HPFG)=1%)、DS=0.16～0.20,并用13C NMR进行表征.     

接枝杜仲胶改性沥青路用性能

为了进一步完善SBS改性沥青性能,降低合成高分子改性剂受原油价格和产量的影响程度,在天然高分子材料杜仲胶上接枝能与沥青氮基反应的官能团马来酸酐,形成一种新的天然沥青改性剂接枝杜仲胶.分析了接枝杜仲胶的生成方法与改性沥青的机理,根据杜仲胶接枝产物的红外光谱,确定了接枝产物的物理表征.将接枝杜仲胶与SBS复合后改性沥青,进行了沥青和沥青混合料的高低温和老化性能试验.试验结果表明:当小于2%掺量的接枝杜仲胶加入SBS改性沥青后能提高其高温和抗老化性能,不降低低温性能,而且1.5%掺量接枝杜仲胶对SBS改性沥青性能提高最为明显;接枝杜仲胶取代一部分SBS后,沥青混合料除了低温性能相当外,强度、高温和水稳性能均得到不同程度的提高.接枝杜仲胶取代一部分SBS后不降低而是增强了改性沥青的使用品质,也减少了合成高分子材料的用量.     

生物胶改良黏土抗崩解特性试验研究

为研究生物胶对黏土抗崩解性的影响,采用黄原胶、瓜尔胶及黄原胶与瓜尔胶质量比为1∶1混合的复合胶对黏土进行改良,通过抗崩解试验,探究生物胶的含量和种类、压实度对改良黏土抗崩解特性的影响规律,并结合扫描电镜试验进一步分析了生物胶的改良机理。结果表明:生物胶通过增强土体颗粒之间黏聚力增强改良黏土的抗崩解特性,其崩解破坏过程可分为稳定前崩解阶段、稳定崩解阶段及稳定后崩解阶段;随着生物胶含量的增大,改良黏土稳定前崩解阶段延长,崩解速率减缓,崩解率降低;复合胶改良黏土抗崩解特性在质量分数大于1.0%后强于单一生物胶;随着压实度的提升,试样抗崩解特性明显改善。     

Impacts of Gum Arabic and Polyvinylpyrrolidone (PVP) with Salicylic Acid on Peach Fruit (Prunus persica) Shelf Life

Peaches are grown in many Egyptian orchards for local and global fresh market sales. The interior fruit tissue breakdown (IFTB), often resulting in decayed peaches, is a severe problem during marketing. Therefore, to minimize FTB of peaches, in this study, gum arabic (GA) and polyvinylpyrrolidone (PVP) were mixed with different concentrations of salicylic acid (SA) (0, 1, and 2 mM) and were applied as edible coating to extend the shelf life of peach fruits. Mature peaches were selected and harvested when peaches reached total soluble solid content (SSC: 8.5%) and fruit firmness of about 47 N. Fruits were coated and stored at room temperature (26 ± 1 °C and air humidity 51 ± 1%) for 10 days during two seasons: 2020 and 2021. Fruit coated with GA/PVP-SA 2 mM showed a significant (p < 0.05) inhibition in degrading enzyme activities (CWDEs), such as lipoxygenase (LOX), cellulase (CEL), and pectinase (PT), compared to uncoated and coated fruits during the shelf-life period. Hence, cell wall compartments were maintained. Consequently, there was a reduction in browning symptoms in fruits by inhibiting polyphenol oxidase (PPO) and phenylalanine ammonia-lyase (PAL) activities. Thus, the fruit skin browning index showed almost no symptoms. The lipid peroxidation process and ionic permeability declined as well. The result suggests that, by applying GA/PVP-SA 2 mM as an edible coating, fruit tissue breakdown can be minimized, and the shelf life of peach can be extended up to 10 days without symptoms of tissue breakdown.     

桃胶多糖酸水解的规律

为有效控制桃胶多糖的水解,以桃胶多糖为原料,用DNS法测定其在pH=1及不同水解温度和时间下的单糖的含量,进而计算出水解度. 结果表明桃胶多糖的酸水解属于拟一级反应类型;在70、75、80、85、90、95 ℃反应时其表观反应速率常数分别是1.72×10-5 s-1 、 3.74×10-5 s-1 、 5.77×10-5 s-1 、 9.41×10-5 s-1、 1.45×10-4 s-1、 2.23×10-4 s-1 ,其水解反应的表观活化能是1.03×105 J·mol-1,反应的表观频率因子是9.72×1010. 在实验温度范围内反应速率常数温度的升高而增大,且两者之间的关系符合Arrhenius公式. 总结出桃胶多糖酸水解反应的Arrhenius公式是k=9.72×1010exp(-1.03×105/RT),进而得到水解度为1-1/exp{[9.72×1010exp(-1.03×105/RT)]t}     

再生FCC废触媒负载镍催化松脂加氢过程优化及其产物分析

为了达到FCC（重油流态化催化裂化）废触媒再生利用变废为宝的目的,以再生FCC废触媒负载镍为催化剂进行松脂加氢反应性能以及生成产物成分的研究。采用4因素4水平正交实验考察了温度、压力、催化剂用量、反应时间对反应转化率的影响以及自制催化剂的重复使用效果,利用气-质联用、气相色谱和紫外分光光度法测定产物的组成。结果表明,松脂加氢反应最优反应条件为：温度200℃,压力6 MPa,催化剂用量5 wt％,反应时间为100 min。气-质联用分析结果表明,松脂加氢反应产物中残留的未反应组分枞酸的含量为1.20 wt％,发生异构化副产物组分去氢枞酸的含量为8.06 wt％。气相色谱和紫外分析结果表明,反应产物中枞酸含量小于2 wt％,去氢枞酸的含量小于10 wt％,含量均符合氢化松香国家标准GB/T14020-2006特级产品的质量技术指标。催化剂重复使用7次后加氢转化率和选择性分别仅减小1％和0.9％,可见催化剂性能稳定且寿命较长。     

可降解瓜尔胶载药微胶囊的聚乙二醇修饰

通过将三聚磷酸纳溶液滴加到阳离子瓜尔胶和聚乙二醇(PEG)混合水溶液中,利用多糖聚电解质的离子凝胶化反应首次制得经PEG修饰的可降解瓜尔胶微胶囊,并用扫描电镜对其表面形态和粒径大小进行了考察;通过对不同浓度牛血清白蛋白和阿司匹林二种模型药物的负载实验,发现修饰后的微胶囊比未经修饰的微胶囊有增大的负载百分率和载药量.     

海砂型氯离子与水泥胶体的结合和机理

为了研究海砂中氯离子对钢筋混凝土结构耐久性影响,分析氯离子对结构中钢筋的腐蚀作用,将海砂引入氯离子的形式从传统的内掺型中剥离出来,采用NaCl溶液浸泡河砂模拟海砂,研究氯离子与水泥胶体的结合机理,并结合SEM微观实验和EDS的元素扫描结果,对氯离子在砂子周围的发布、结合规律作了描述.实验表明:水泥稳定后与氯离子的结合率在60%左右,海砂型与内掺型氯离子结合、传播方式有所不同,海砂型引入的氯离子存在一个从海砂表面到水泥凝胶内部的渗透过程,在此基础上提出海砂型氯盐侵蚀的概念,基于微观试验结果讨论了其结合和传播机理.