UV‐ignited frontal polymerization of an epoxy resin

By combining frontal polymerization and radical‐induced cationic polymerization, it was possible to cure thick samples of an epoxy monomer bleached by UV light. The effect of the relative amounts of cationic photoinitiator and radical initiator was thoroughly investigated and was related to the front's velocity and its maximum temperature. The materials obtained were characterized by quantitative conversion also in the deeper layers, not reached by UV light. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2066–2072, 2004     

Functionalization of polyethylene/silane copolymers in posttreatment reactions

7‐Octenyldimethylphenylsilane was copolymerized with ethylene via Et(Ind)₂ZrCl₂ methylaluminoxane catalyst system without loss of catalyst activity or decrease in molar mass. The comonomer contents in the polymer samples were at a level of 0.15–1.0 mol % and the reactive phenylsilane groups were posttreated to different alcoxy‐ and halosilane groups, for example, Si? F, Si? Cl, Si? OCH₃, and Si? OCH₂CH₃. The posttreatment reactions had no major effect on the molar masses or on the thermal properties (measured with differential scanning calorimetry) of the copolymers. The reaction pathways were nearly independent of the comonomer contents and the reactions reached 70–100% conversions. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1461–1467, 2004     

Dielectric relaxation analysis of starch oligomers and polymers with respect to their chain length

Starch belongs to the polyglucan group. This type of polysaccharide shows a broad β-relaxation process in dielectric spectra at low temperatures, which has its molecular origin in orientational motions of sugar rings via glucosidic linkages. This chain dynamic was investigated for α(1,4)-linked starch oligomers with well-defined chain lengths of 2, 3, 4, 6, and 7 anhydroglucose units (AGUs) and for α(1,4)-polyglucans with average degrees of polymerization of 5, 10, 56, 70, and so forth (up to 3000; calculated from the mean molecular weight). The activation energy (E_a) of the segmental chain motion was lowest for dimeric maltose (E_a = 49.4 ± 1.3 kJ/mol), and this was followed by passage through a maximum at a degree of polymerization of 6 (E_a = 60.8 ± 1.8 kJ/mol). Subsequently, E_a leveled off at a value of about 52 ± 1.5 kJ/mol for chains containing more than 100 repeating units. The results were compared with the values of cellulose-like oligomers and polymers bearing a β(1,4)-linkage. Interestingly, the shape of the E_a dependency on the chain length of the molecules was qualitatively the same for both systems, whereas quantitatively the starch-like substances generally showed higher E_a values. Additionally, and for comparison, three cyclodextrins were measured by dielectric relaxation spectroscopy. The ringlike molecules, with 6, 7, and 8 α(1,4)-linked AGUs, showed moderately different types of dielectric spectra. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 188–197, 2004     

Heterochain model for simultaneous long‐chain branching and crosslinking. III. Multicomponent polymerization

The matrix formula developed in the context of heterochain theory, M?_w = M?_wp + WF ( I ? M )^?1 S , was applied to describe the molecular weight development during free‐radical multicomponent polymerization. All of the required probabilistic parameters are expressed in terms of the kinetic‐rate constants and the various concentrations associated with them. In free‐radical polymerization, the number of heterochain types, N, needs to be extrapolated to infinity, and such extrapolation is conducted with only three different N values. This matrix formula can be used as a benchmark test if other approximate approaches can give reasonable estimates of the weight‐average molecular weights. The moment equations with the average pseudo‐kinetic‐rate constants for branching and crosslinking reactions may provide poor estimates when the copolymer composition drift during polymerization is very significant. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2801–2812, 2004     

Self-bonding in an amorphous polymer below the glass transition: A T-peel test investigation

Films of amorphous polystyrene (PS) with a weight-average molecular weight (M_w) of 225 × 10³ g/mol were bonded in a T-peel test geometry, and the fracture energy (G) of a PS/PS interface was measured at the ambient temperature as a function of the healing time (t_h) and healing temperature (T_h). G was found to develop with (t_h)^1/2 at T_h = T_g-bulk − 33 °C (where T_g-bulk is the glass-transition temperature of the bulk sample), and log G was found to develop with 1/T_h at T_g-bulk − 43 °C ≤ T_h ≤ T_g-bulk − 23 °C. The smallest measured value of G = 1.4 J/m² was at least one order of magnitude larger than the work of adhesion required to reversibly separate the PS surfaces. These three observations indicated that the development of G at the PS/PS interface in the temperature range investigated (<T_g-bulk) was controlled by the diffusion of chain segments feasible above the glass-transition temperature of the interfacial layer, in agreement with our previous findings for fracture stress development at several polymer/polymer interfaces well below T_g-bulk. Close values of G = 8–9 J/m² were measured for the symmetric interfaces of polydisperse PS [M_w = 225 × 10³, weight-average molecular weight/number-average molecular weight (M_w/M_n) = 3] and monodisperse PS (M_w = 200 × 10³, M_w/M_n = 1.04) after healing at T_h = T_g-bulk − 33 °C for 24 h. This implies that the self-bonding of high-molecular-weight PS at such relatively low temperatures is not governed by polydispersity. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1861–1867, 2004     

Diffraction grating in noncrosslinked polymers

The diffraction efficiency and morphology of the transmission modes of holographic polymer dispersed liquid crystals were studied with respect to the molecular structure of poly(urethane acrylate) (PUA), the film (polymer/liquid crystal) and resin (oligomer/monomer) compositions, and the cell thickness. PUA, based on N‐vinylpyrrolidone and ethyl hexyl acrylate, with low‐molecular‐weight poly(propylene glycol) at a low oligomer content, showed high diffraction efficiency. The results were interpreted in terms of the monomer reactivity and polymer elasticity. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 613–620, 2004     

Determination of the degree of cure under dynamic and isothermal curing conditions with electrical impedance spectroscopy

This article presents a new methodology for the quantitative determination of the progress of the curing reaction of a thermosetting resin, using the results of electrical impedance spectroscopy. The method is an extension of the use of the imaginary impedance maximum as a reaction progress indicator and is based on the demonstration of a close correlation between the reaction rate, as measured by conventional differential scanning calorimetry, and the rate of change of the value of the imaginary impedance spectrum maximum. Tests on a commercial aerospace epoxy resin under both isothermal and dynamic heating conditions with calorimetry and impedance spectroscopy have demonstrated the validity of the method and set the accuracy limits involved. This technique can be used as a real-time online control tool for thermoset composite manufacturing. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 146–154, 2004     

Desorption behavior of a surfactant in a linear low‐density polyethylene blend at elevated temperatures

The desorption behavior of a surfactant in a linear low‐density polyethylene (LLDPE) blend at elevated temperatures of 50, 70, and 80 °C was studied with Fourier transform infrared spectroscopy. The composition of the LLDPE blend was 70:30 LLDPE/low‐density polyethylene. Three different specimens (II, III, and IV) were prepared with various compositions of a small molecular penetrant, sorbitan palmitate (SPAN‐40), and a migration controller, poly(ethylene acrylic acid) (EAA), in the LLDPE blend. The calculated diffusion coefficient (D) of SPAN‐40 in specimens II, III, and IV, between 50 and 80 °C, varied from 1.74 × 10^?11 to 6.79 × 10^?11 cm²/s, from 1.10 × 10^?11 to 5.75 × 10^?11 cm²/s, and from 0.58 × 10^?11 to 4.75 × 10^?11 cm²/s, respectively. In addition, the calculated activation energies (E_D) of specimens II, III, and IV, from the plotting of ln D versus 1/T between 50 and 80 °C, were 42.9, 52.7, and 65.6 kJ/mol, respectively. These values were different from those obtained between 25 and 50 °C and were believed to have been influenced by the interference of Tinuvin (a UV stabilizer) at elevated temperatures higher than 50 °C. Although the desorption rate of SPAN‐40 increased with the temperature and decreased with the EAA content, the observed spectral behavior did not depend on the temperature and time. For all specimens stored over 50 °C, the peak at 1739 cm^?1 decreased in a few days and subsequently increased with a peak shift toward 1730 cm^?1. This arose from the carbonyl stretching vibration of Tinuvin, possibly because of oxidation or degradation at elevated temperatures. In addition, the incorporation of EAA into the LLDPE blend suppressed the desorption rate of SPAN‐40 and retarded the appearance of the 1730 cm^?1 peak. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1114–1126, 2004     

Novel fixed‐site–carrier polyvinylamine membrane for carbon dioxide capture

Fixed‐site–carrier membranes were prepared for the facilitated transport of CO₂ by casting polyvinylamine (PVAm) on various supports, such as poly(ether sulfone) (PES), polyacrylonitrile (PAN), cellulose acetate (CA), and polysulfone (PSO). The cast PVAm on the support was crosslinked by various methods with glutaraldehyde, hydrochloric acid, sulfuric acid, and ammonium fluoride. Among the membranes tested, the PVAm cast on polysulfone and crosslinked by ammonium fluoride showed the highest selectivity of CO₂ over CH₄ (>1000). The permeance of CO₂ was then measured to be 0.014 m³ (STP)/(m² bar h) for a 20 μm thick membrane. The effect of the molecular weight of PVAm and feed pressure on the permeance was also investigated. The selectivity increased remarkably with increasing molecular weight and decreased slightly with increased pressure in the range of 1 to 4 bar. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4326–4336, 2004     

Synthesis and gas barrier characterization of poly(ethylene isophthalate)

Poly(ethylene isophthalate) (PEI) was synthesized for this research with essentially a condensation polymerization of isophthalic acid and ethylene glycol catalyzed by zinc acetate and antimony trioxide. Several samples were obtained, and their characteristics were observed and compared with poly(ethylene terephthalate) (PET). The synthesized PEI samples were chemically identified by ¹H NMR. Thermal analysis with differential scanning calorimetry (DSC) yielded results that indicate the samples were primarily amorphous, with a glass‐transition temperature of 55–60 °C. Molecular weights of these PEI samples were also obtained through intrinsic viscosity measurements (Mark–Houwink equation). Molecular weights varied with conditions of the polymerization, and the highest molecular weight achieved was 21,000 g/mol. Finally, the diffusion coefficient, solubility, and permeability of CO₂ gas in PEI were measured and found to be substantially lower than in PET, as anticipated from their isomeric chemical structures. This is because in PET the phenyl rings are substituted in the para (1,4) positions, which allows for their facile flipping, effectively permitting gases to pass through. However, the meta‐substituted phenyl rings in PEI do not permit such ring flipping, and thus PEI may be more suitable for barrier applications. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4247–4254, 2004