冷却速度对圆形加载路径下A319铝合金多轴疲劳特性的影响

采用MTS809型电液伺服疲劳试验机、扫描电镜研究了不同冷却速度对A319铝合金圆形加载路径下的疲劳特性.结果表明:当冷速为10℃·s-1时,材料中二次枝晶臂间距、硅颗粒及孔洞尺寸较冷速为0.1℃·s-1时要小.二次枝晶臂间距较小时,滞后回线面积小,材料应力应变近乎同相,且附加强化效果明显.不同冷速条件下裂纹萌生位置不同,在冷速为10℃·s-1的材料中,裂纹在大硅颗粒处萌生,随着冷速降低至0.1℃·s-1时,裂纹位于孔洞处萌生.对于A319铸造铝合金来说,冷速的变化对其轴向与切向循环特性并无直接影响,轴向表现为先硬化再软化,切向表现为先硬化后稳定的趋势.     

Sn—Pb合金的三次树枝晶生长

在定向凝固的条件下对Ｓｎ－Ｐｂ合金的三次树枝晶生长进行了研究。探讨纵向和横向生长的三次树枝晶形态，给出了三次枝晶间距与工艺参数即温度梯度和生长速度之间的指数衰减关系。发现纵向和横向三次枝晶在枝晶粗化和间距上存在着明显的差别，并探讨了枝晶爬行对枝晶不对称生长的影响。     

Forming mechanism of refined granular crystalline of Cu70Ni30 alloy by undercooled solidification

Moth glass fluxing and cyclic superheating techniques were adopted to effectively uudercool the Cu₇₀Ni₃₀ alloy in vacuum. Within the undercooling range of 21 K to 270 K, the microstructure evolution ol the alloy was investigated. When the inell was undercooled to △T > △T', (210 K) , the grain refinement took place abruptly, liascd on the observation of the solidified microstructure, the rnierocheinieal-analysis and the calculated results with UCT model, it is found that the secondary grain refinement mechanism consists of two stages. The dendrite is, firstly, broken into hag-ments owing to the stress caused by uneven shrinking during rapid solidilication, then the fragments, under the driving force of surface and strain energies, merge through the migration of l>ouinlaries, i. c. recryslallization, thus leading to the formation of secondary granular-crystalline .     

神经原信息传递可及空间的体积计算

本文提出神经原信息传递可及空间是一个凸多面体．本文也给出了构造该凸多面体、计算其体积的方法，并阐述了此方法的数学依据．     

Phase‐field simulation of dendrite growth under forced flow conditions in an Al–Cu welding molten pool

A quantitative phase‐field model for directional solidification is applied to study dendrite growth under forced flow conditions in an Al‐Cu Gas Tungsten Arc (GTA) welding molten pool. Evolution of the dendrite morphology and the solute field under forced flow conditions is simulated. Growth of columnar grains goes through three periods, including the initial instability period, the competitive growth period and the relatively stable period. The solute segregation, the solute redistribution and the solute concentration in the liquid side of the interface are investigated, respectively. For the given conditions, simulation results are in good agreement with experimental findings.     

Effect of ZrO2 incorporation on the mechanical behavior of an AlSi alloy

AlSi–ZrO₂ composite was prepared by stir casting method using a vortex technique. Micrograph observations exhibit a microstructure containing primary Si particles, eutectic silicon cells and intermetallic particles embedded in a dendritic primary α-phase in both Al–Si and AlSi–ZrO₂ homogenized alloys. Difference in thermal conductivity between the α matrix and the ZrO₂ particles generates a high temperature gradient resulting in an increase in the cooling rate which affects the microstructure and, consequently, the mechanical properties. On the other hand, the difference of the structures and the thermal expansion coefficient between ZrO₂ particles and the matrix generates stress and increases the dislocation density. Presence of the ZrO₂ particles enhances the ductility of the composite materials and reduces its Young's modulus. Addition of the ZrO₂ particles increases the hardness of the composite materials at low aging temperature and reduces it at higher aging temperature.     

三维铜基集流体的构筑及在锂金属电池中的应用

锂金属因其具有超高比容量(3860 mAh·g^-1)以及较低的氧化还原电势(-3.04 V vs 标准氢电极),被认为是下一代高能量密度二次电池的理想负极材料。然而“无宿主”的金属锂在金属/电解液界面层进行沉积/剥离,不可避免地会生长枝晶,不仅使电极表面电流分布不均,同时可能会刺穿电池隔膜而导致电池短路。通过构造三维集流体/锂金属复合负极可以有效调控锂沉积行为并抑制枝晶生长,从而提升电池的库仑效率、循环寿命以及倍率性能,该领域近年来一直都是研究的热点。本文首先总结了基于三维集流体抑制锂枝晶的相关原理和模型;其次针对用于负极的铜基集流体,根据构成三维结构基底单元的维度,总结了三维铜基集流体的制备方法及其在锂金属负极保护方面的应用;最后,对三维集流体构造复合锂负极进行了总结和展望。     

Enhanced Immunosensor Using a Handheld pH Meter for the Point-of-Care,Sensitive Detection of Prostate Specific Antigen

An enhanced handheld pH meter based immunosensor was proposed for point-of-care, quantitative determination of prostate specific antigen (PSA). Monoclonal antibody-functionalized magnetic beads (MB-Ab₁) were prepared to capture PSA in sample, and subsequently bond to polyclonal antibody-immobilized gold nanoparticles-polyamide-amine dendrite-lead ion (GO-PAMAM-Pb²⁺) and dispersed in H₂S solution. Based on negative Gibbs free energy of formation, PbS (solubility product constant K_sp=8.0×10⁻²⁸ was formed by reaction of Pb²⁺ and H₂S. Hence, the pH of solution increased due to the H⁺ appeared, and the resulting pH value was monitored by a handheld pH meter.     

液氮冷却条件下激光快速熔凝Ni-28 wt%Sn合金组织演变

研究了在液氮冷却条件下激光快速熔凝Ni-28 wt%Sn亚共晶合金的组织演化过程. 结果显示, 熔池从上至下可以分为三个区域: 表层为平行激光扫描方向的α-Ni转向枝晶区; 中部为近乎垂直于熔池底部外延生长的α-Ni柱状晶区; 底部为少量的残留α-Ni初生相和大量的枝晶间(α-Ni+Ni₃Sn) 共晶组织. 激光熔凝区组织受原始基材组织的影响很大, 熔池中的α-Ni枝晶生长方向受到了热流方向和枝晶择优取向的双重影响. 与基材中存在的层片状、棒状和少量离异(α-Ni+Ni₃Sn)共晶的混合组织相比, 熔池内的共晶组织皆为细小的规则(α-Ni+Ni₃Sn)层片状共晶, 皆垂直于熔池底部外延生长, 并且从熔池顶部至底部, 共晶层片间距逐渐增大. 分别应用描述快速枝晶生长的Kurz-Giovanola-Trivedi 模型和描述快速共晶生长的Trivedi-Magnin-Kurz模型对熔池表层凝固界面前沿的过冷度进行估算, 发现熔池表层α-Ni 枝晶和(α-Ni+Ni₃Sn)层片共晶的生长过冷度在50.4-112.5 K 之间, 远大于相应深过冷凝固(α-Ni+Ni₃Sn) 反常共晶生长的临界过冷度20 K, 这说明文献报道的临界过冷度并不是反常共晶出现的充分条件.     

移动电磁场下低碳钢凝固过程枝晶破碎临界条件

为了探讨移动电磁场对低碳钢凝固过程枝晶破碎的影响,进行了移动电磁场下的0.22%～0.34%C(质量分数)低碳钢浇铸凝固实验.对不同磁感应强度下铸坯凝固组织进行了观察,考察了二次枝晶分布,凝固过程冷却速度与二次枝晶间距的函数关系.同时考察了移动电磁场对铸坯柱状晶向等轴晶转变(CET)位置的影响,并对钢凝固过程CET发生时的凝固速度和固相率进行了计算.导出了移动电磁场下合金凝固过程枝晶破碎的临界条件,并通过低碳钢作实验验证,得到了低碳钢凝固CET发生时临界固相率和液相平均流速之间的关系.