Structural and electrical properties of crystalline (1−x)Ta2O5−xTiO2 thin films fabricated by metalorganic decomposition

Polycrystalline (1−x)Ta₂O₅−xTiO₂ thin films were formed on Si by metalorganic decomposition (MOD) and annealed at various temperatures. As-deposited films were in the amorphous state and were completely transformed to crystalline after annealing above 600 °C. During crystallization, a thin interfacial SiO₂ layer was formed at the (1−x)Ta₂O₅−xTiO₂/Si interface. Thin films with 0.92Ta₂O₅–0.08TiO₂ composition exhibited superior insulating properties. The measured dielectric constant and dissipation factor at 1 MHz were 9 and 0.015, respectively, for films annealed at 900 °C. The interface trap density was 2.5×10¹¹ cm⁻² eV⁻¹, and flatband voltage was −0.38 V. A charge storage density of 22.8 fC/μm² was obtained at an applied electric field of 3 MV/cm. The leakage current density was lower than 4×10⁻⁹ A/cm² up to an applied electric field of 6 MV/cm.     

Co-doped In2O3 thin films: Room temperature ferromagnets

Laser-ablated Co-doped In₂O₃ thin films were fabricated under various growth conditions on R-cut Al₂O₃ and MgO substrates. All Co:In₂O₃ films are well-crystallized, single phase, and room temperature ferromagnetic. Co atoms were well substituted for In atoms, and their distribution is greatly uniform over the whole thickness of the films. Films grown at 550 °C showed the largest magnetic moment of about 0.5 μ_B/Co, while films grown at higher temperatures have magnetic moments of one order smaller. The observed ferromagnetism above room temperature in Co:In₂O₃ thin films has confirmed that doping few percent of magnetic elements such as Co into In₂O₃ could result in a promising magnetic material.     

Preparation and characterization of iron oxide thin films by spray pyrolysis using methanolic and ethanolic solutions

Iron oxide thin films have been obtained by spray pyrolysis using 100% methanolic and ethanolic solutions of iron tri-chloride. The films were deposited onto ITO-coated glass substrates. The preparative conditions have been optimized to obtain compact, pin-hole-free and smooth thin films which are adherent to the substrate. The structural, morphological and compositional characterizations have been carried out by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray analysis. The films deposited using ethanolic solution results into pure hematite; α-Fe₂O₃ thin films, however, films deposited using methanolic solution consists of hematite and maghemite-c phases of iron oxide. The films are nanocrystalline with particle size of 30-40 nm. The optical absorbance of the film was of the order of 10⁵ cm⁻¹. The optical band gap of films was found to be 2.26 and 2.20 eV for the films deposited using methanolic and ethanolic solutions, respectively.     

A novel approach to thermal Analysis of Thin films

A novel instrument is described called the Thin film Analyser (TFA) which quantitatively measures changes in mechanical and rheological properties of drying films in-situ on a test panel. It is based around a simple force-sensing device, capable of carrying various probes, which can be positioned in anX-Y plane over the panel. Temperature control is achieved by means of a heating block under the sample. By imposing a thermal gradient along the block, measurements can be obtained at a series of temperatures in a single experiment. Several applications of the TFA to the drying of curable and latex-based coatings are discussed, as well as some more specialized uses. The TFA concept represents a novel approach to the thermal analysis of thin films.The authors gratefully acknowledge the design, engineering and software development work of the Instrument Group at ICI Paints, in particular John Hayton, Neil Burrows, Tony Evans and Ian Francis, who have now built three versions of the TFA.     

Polyolefins with controlled environmental degradability

Antioxidants and stabilisers, developed to increase the durability of polyolefins, in combination with prooxidant transition metal complexes provide industrial products with widely variable but controlled lifetimes. The low molar mass oxidation products formed during photo-oxidation and thermal oxidation are biodegradable and oxo-biodegradable polyolefins are now widely used in agricultural applications and in degradable packaging as examples. The scientific basis for the performance of oxo-biodegradable materials is explained with reference to naturally occurring macromolecules. Comparison with hydro-biodegradable materials is made and the need is demonstrated for performance standards to be developed that mimic nature's resource recovery mechanism, that of oxo-biodegradation.     

Morphological and chemical study of the initial growth of CdS thin films deposited using an ammonia-free chemical process

We study the initial growth stages of CdS thin films deposited by an ammonia-free chemical bath deposition process. This ammonia-free process is more environmentally benign because it reduces potential ammonia release to the environment due to its high volatility. Instead of ammonia, sodium citrate was used as the complexing agent. We used atomic force microscopy (AFM), Rutherford backscattering (RBS) and X-ray photoelectron spectroscopy (XPS) to investigate the morphological and chemical modifications at the substrate surface during the first initial stages of the CdS deposition process. Additionally, X-ray diffraction (XRD) and optical transmission spectroscopy measurements were carried out to compliment the study. XPS results show that the first nucleation centers are composed by Cd(OH)₂ which agglomerate in patterns of bands, as demonstrated by AFM results. It is also observed that the conversion to CdS (by anionic exchange) of the first nucleus begins before the substrate surface is completely covered by a homogenous film.     

MEASUREMENTS OF Fe AND Cu K-Shell IONIZATION CROSS SECTIONS BY SLOW ELECTRON IMPACT

ＭＥＡＳＵＲＥＭＥＮＴＳＯＦＦｅＡＮＤＣｕＫ－ＳｈｅｌＩＯＮＩＺＡＴＩＯＮＣＲＯＳＳＳＥＣＴＩＯＮＳＢＹＳＬＯＷＥＬＥＣＴＲＯＮＩＭＰＡＣＴＬｉＴａｉｈｕａＡｎＺｈｕＬｕｏＺｈｅｎｇｍｉｎｇＣｅｎｔｅｒｆｏｒＲａｄｉａｔｉｏｎＰｈｙｓｉｃｓ，Ｉｎｓ...     

Chemical synthesis of p-type nanocrystalline copper selenide thin films for heterojunction solar cells

Nanocrystalline thin films of copper selenide have been grown on glass and tin doped-indium oxide substrates using chemical method. At ambient temperature, golden films have been synthesized and annealed at 200 °C for 1 h and were examined for their structural, surface morphological and optical properties by means of X-ray diffraction (XRD), scanning electron microscopy and UV-vis spectrophotometry techniques, respectively. Cu_2−xSe phase was confirmed by XRD pattern and spherical grains of 30 ± 4 - 40 ± 4 nm in size aggregated over about 130 ± 10 nm islands were seen by SEM images. Effect of annealing on crystallinity improvement, band edge shift and photoelectrochemical performance (under 80 mW/cm² light intensity and in lithium iodide electrolyte) has been studied and reported. Observed p-type electrical conductivity in copper selenide thin films make it a suitable candidate for heterojunction solar cells.     

Characteristics of Ti0.97Co0.03O2:Sb0.01 dilute magnetic semiconducting thin films deposited at 500 °C by pulsed laser deposition

Epitaxial Ti_0.97Co_0.03O₂:Sb_0.01(TCO:Sb) films were deposited on R-Al₂O₃ (1 1 0 2) substrates at 500 °C in various deposition pressures by pulsed laser deposition. The solubility of cobalt within the films increases with decreasing deposition pressure at a deposition temperature of 500 °C. The TCO:Sb films deposited at 5×10⁻⁶ Torr exhibit a p-type anomalous Hall effect having a hole concentration of 6.1×10²²/cm³ at 300 K. On the other hand, films deposited at 4×10⁻⁴ Torr exhibits an n-type anomalous Hall effect having an electron concentration of about 1.1×10²¹/cm³. p- or n-type DMS characteristics depends on the change of the structure of TCO:Sb films and the solubility of Co is possible by controlling the deposition pressure.     

In‐line monitoring of UV photopolymerization with a quartz crystal resonator

An in‐line monitoring device using a quartz crystal resonator for thin film polymerization was proposed, and its performance has been evaluated by implementing in the UV polymerization of 2‐hydroxyethyl methacrylate with a photoinitiator of 1‐chloroanthraquinone. Because the variation of resonant resistance of the resonator is proportional to the square root of viscosity change that is closely related to the polymerization degree, the resistance can be used as a measure of the polymerization degree. The resistance measurements were compared with the outcome of instrumental analyses of polymerization degree using an FTIR spectrometer and a gel permeation chromatograph. The experimental results showed that the resistance measurements were consistent with the experimental outcome of the instrumental analyses, and this indicates the effectiveness of the proposed device. Owing to the simplicity and availability of the resonator system, its wide utilization in the monitoring of a variety of film polymerization processes, including photoresistor application, is expected. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2428–2439, 2006