Magneto-resistance above 300 K in nano-crystalline Co–Ag metastable solid solutions

A series of nano-crystalline Co_xAg_100−x solid solutions have been prepared by NaBH₄ reduction of the corresponding metal salts at room temperature in Ar gas flow. Alloys heat-treated at 600 °C in Ar/H₂ (5%) show the evolution of metastable fcc Co precipitates in Ag. Magnetic studies indicate that all the compositions are ferromagnetic with Curie temperatures >400 K. For a nominal composition of Co₆₀Ag₄₀, heat-treated at 600 °C, an effective negative magneto-resistance (MR) ratio of the order of ∼21% at 350 K, at 2 T is observed. This could arise from the influence of magnetic field on the electron–phonon scattering effects near to T_c and to the spin-mixing scattering by magnons.     

Thickness-dependent crystallization behavior of fast-growth phase-change amorphous films

The crystallization behavior of amorphous films embedded in substrates with thickness of several nanometers is investigated based on a thermodynamic model. It is found that there is an optimum layer thickness where the crystallization speed of the films is maximized with the lowest energy barrier for crystallization. This is induced by an energetic change from glass/substrate interface energy to crystal/substrate interface energy as the crystal size is larger than the film thickness during the crystallization. Thus, the crystallization speed in thin films is affected by its thickness.     

Fe-Cr-V-Ni-Si-C系多元合金的原子间互作用势的构建及应用

使用第一性原理赝势方法及量子化学从头算方法计算的物理量以及最小二乘法拟合的数据构建了多元合金Fe-Cr-V-Ni-Si-C系的原子间互作用势,并利用该原子间互作用势计算了实验合金N5(Fe9.07Cr7.56V0.8Ni0.49 Mo0.96Mn1.52Si3.3C),N6(Fe9.65Cr7.72V1.17Ni0.50Mo0.91Mn1.42Si3.3C),N7(Fe9.81Cr7.65V1.58Ni0.46Mo0.86Mn1.35Si3.3C),N8(Fe10.05Cr7.59V2.24Ni0.40M 关键词： F-S多体势 多元合金 第一性原理     

Ti-45at.% Al合金定向凝固过程中显微组织演化的计算机模拟

采用基于溶质扩散控制模型CA方法对Ti-45at.% Al合金定向凝固过程中显微组织演化过程进行了数值模拟.模拟结果表明,在温度梯度较高时,初生晶核间距无论大小,均可通过分枝或竞争生长而使一次胞晶/枝晶间距得到调整.在抽拉速度一定情况下,随着温度梯度增加,胞晶/枝晶间距减小,在温度梯度一定情况下,随着抽拉速度增大,观察到胞晶/枝晶混合结构,混合结构区随温度梯增大而增大,模拟结果与实验观察相符合. 关键词： Ti-45at.% Al合金 定向凝固 组织演化 数值模拟     

微尺度型腔内液态金属流动规律模拟研究

修正了传统的Navier-Stoke方程,并利用修正后的方程与Fluent软件对微尺度型腔内Zn-Al合金微流动规律进行了数值模拟.模拟结果表明：液态金属在微尺度管道内的流动规律在管径为0.5mm时出现临界状态,管径越细,速度附面层相对厚度就越大.同时,微管流动存在着宏观流动中没有的“凸进效应”,且随着入口压力增大,流动前沿自由液面的凸进效应减弱.在流动前沿区域和上游区域之间出现负压力梯度区,且管径越细越明显. 关键词： 微管道 微流动 Zn-Al合金     

爆轰驱动破片二次排布技术探索性研究

To study the warhead by explosively loaded fragments, generating new damage model, a kind of at the bottom of explosives loaded directly tungsten alloy fragments is designed, using nine square format arranged in a manner, and by target as the witness of their damage mode. Via explosively loaded , in target a cross pattern on the way damage is obtained, and damage diameter is about 22. 5 times the diameter of the charge, increasing the damage of the target area. About designing warhead, that is a very promising way, also a new model of damage is in assessment mode, the work is worth further study.     

ICP-AES法测定高温合金中5种非金属元素

本文研究了快速测定高温合金中5种非金属元素(As、B、P、Se、Si)的分析方法,以满足高温合金行业对非金属元素检测的需求。利用王水和高氯酸对高温合金进行酸溶解,并系统研究了基体元素和共存元素对分析元素谱线的光谱干扰情况,同时进行了分析谱线的选择。5种非金属元素的检出限在5.5 ～ 11.9 ug/ml,5次数据的相对标准偏差(RSD,n=5)为0.9 % ～ 7 %,各元素的回收率在96 % ～ 102 %之间,该方法适用于高温合金中非金属元素的测定。     

冷风油雾润滑对TC4铣削过程刀-屑摩擦的影响

通过钛合金TC4的铣削实验,研究冷风油雾润滑介质特性及其施加方式对刀具-切屑摩擦行为的影响.冷风油雾喷嘴布置在刀具将要切入工件前的空行程中,其润滑效果最好.当出油量增加到一定值(约12mL·h-1)时,刀具-切屑平均摩擦系数不再发生明显变化.随着钛合金TC4铣削速度的提高,冷风干切削的平均摩擦系数增大,而冷风油雾切削的平均摩擦系数变化不明显,且远低于冷风干切削的平均摩擦系数.结果表明:油雾载体速度和刀具转速存在一定的匹配关系,使润滑效果达到最优.     

振动对ZL205A合金偏析组织及硬度的影响

为了解决ZL205A合金铸件产生偏析缺陷等问题，进一步明确振动对偏析组织及硬度的影响规律，采用电磁式振动台作为振动源，探究了振动频率、振幅、振动时间对合金偏析组织占比及硬度的影响情况。结果表明，振动频率在25~55 Hz内变化时，随着振动频率的增加，偏析组织占比呈现先减小、后增加的趋势，硬度呈现先增大、后减小的趋势；振幅由1 mm增加到4 mm的过程中，偏析组织占比逐渐减少并趋于稳定，硬度呈现先减小、后增大的趋势；振动时间由30 s增加至75 s时，偏析组织占比呈现增加趋势并最终趋于稳定，硬度呈现先减小、后增大的趋势。振动频率对合金偏析组织和硬度的影响最为显著，振动时间和振幅的影响次之，此外，偏析组织的析出也会影响合金硬度。研究结果为明确ZL205A合金在振动条件下凝固组织的变化规律、提高铸件质量提供了理论参考。     

Heusler合金Fe_2VAl的晶体结构与热电性能研究

采用真空电弧熔炼和放电等离子烧结技术制备了Full-Heusler合金Fe_2VAl,利用XRD、XPS对合金的物相结构与成分进行表征,在300～800K温度区间内测试了合金的Seebeck系数、电阻率、热导率等热电参数,并将实验结果与基于L2_1有序结构Fe_2VAl合金的模拟计算值进行了比较。结果表明,实验所制的合金样品中Fe、Al、V原子比接近于2∶1∶1,基本满足Fe_2VAl合金的成分配比;结合XRD衍射谱及10K下合金的饱和磁矩可知,所制合金样品中除了完全有序的L2_1结构相外,还存在部分的B2相。另一方面,基于热电性能测试结果可知,所制Fe_2VAl合金表现出典型的n型半导体特性,其Seebeck系数和电阻率随着温度的升高而降低,这与利用VASP和BoltzTraP软件包结合计算得到的L2_1结构Fe_2VAl合金的热电参数随温度(300～800K)的变化趋势相符合;合金的热导率随着温度的升高呈先降低后升高的趋势,在500K附近具有极小值,而无量纲参数热电优值ZT在500K附近达到最大值,约为0.052。