TDI三聚体的合成研究

以一种碱金属羧酸盐K-1000作为甲苯二异氰酸酯(TDI)三聚反应的催化剂合成了以TDI三聚体为主要成分的多异氰酸酯固化剂。对合成工艺条件进行了探讨。结果表明,将反应温度控制在35℃,催化剂K-1000用量为0.06%时,用苯甲酰氯作为阻聚剂可得到性能基本稳定的TDI三聚体产品。     

烷基季铵盐插层剂的合成及应用

Three novel intercalation agents were synthesized for the first time, which arose from oleic acid diethylenetriamine or triethylenetetramine 3 - chloro - 2 - hydroxypropy trimethylammonium choride (CHPTA) and chloroethanol. Organophilic vermicullites were synthesized from sodium type vermiculite by cation exchange with new intercalation agents. The results of X - ray diffraction study showed that the gallery distance of the organophilic vermiculite was enlarged from 1 nm to 5 nm or more. A new idea of making design for intercalation agent was provided.     

硼酸酯偶联剂的合成与表征

通过分子结构设计，合成了一种氮一硼内配位结构的硼酸酯偶联剂，解决了硼酸酯水解稳定性差的问题，同时分子结构中含有氨基、丁氧基等活性基团。用傅立叶变换红外光谱对硼酸酯进行了结构表征，讨论了原料配比、合成工艺等对硼酸酯收率及反应速率的影响，并通过实验确定了最佳配方及工艺。对硼酸酯的物理性能、溶解性、水解稳定性及对硼酸铝晶须的表面处理效果进行了表征。结果表明：合成的硼酸酯偶联剂由于具有氮-硼内配位作用，表现出优良的水解稳定性，并且硼酸酯偶联剂对硼酸铝晶须具有良好的表面改性效果。     

SYNTHESIS, CROSSLINKING MECHANISM AND PROPERTIES OF A POLYACRYLATE/POLYURETHANE COMPOSITE COATING

A polyacrylate/polyurethane (P(A) / P(U)) composite coating has been prepared bycrosslinking an acetoacetylated polyacrylate with a vinylic group terminated polyurethaneat room temperature. A model Michael reaction between ethyl acetoacetate (EAA) andmethyl acrylate (MA) was designed to study the crosslinking mechanism. It was foundthat the two active hydrogen atoms in acetoacetyl group can both add to vinylic groupsand the yield of mono- and bis-adducts are much affected by the molar ratio of acetoacetylto vinylic groups. Higher crosslinking degree and better properties could be obtained withdecreasing the molar ratio of the two active groups from 1/1 to 0.6/1 in the compositecoatings.     

Gelation in free-radical terpolymerization of poly(allyl methacrylate) crosslinked polymer nanosphere with allyl benzoate and vinyl benzoate

Microgel-like poly(allyl methacrylate) (PAMA nanosphere) was prepared by the emulsion polymerization of AMA as the reactive crosslinked polymer nanosphere with abundant pendant allyl groups. The terpolymerization of PAMA nanosphere with allyl benzoate (ABz) and vinyl benzoate (VBz) was conducted in bulk using benzoyl peroxide as initiator at 80 °C. The gelation depended on the feed ABz/VBz molar ratio since the molecular weights of resulting poly(ABz-co-VBz)s that act as the bridges increased with an increase in the mole fraction of VBz in the feed monomer. Beyond the gel point, the sol was rapidly incorporated into the gel and the increasing tendency of the gel fraction became steeper from 70 to 95 mol% of VBz as a reflection of increased chain length of bridge between PAMA nanospheres. Moreover, the swelling ratio became lower with increasing the mole percentage of VBz in the feed monomer. These results would support the preferential incorporation of PAMA nanosphere into the gel and the longer bridge can capture more nanospheres to give a much shrunken gel.     

橡胶增韧环氧树脂机理的研究

本文研究了固化剂种类、环氧基体平均网链长度和分散相与基体间键合情况对体系韧性等的影响.结果说明,基体平均网链长度是一个更为重要的影响因素.分散相与基体间的化学键合也是重要的.文中对橡胶增韧环氧树脂的机理提出了见解.在交联密度较低的材料中,在橡胶颗粒附近叠加的应力场诱发下发生纵深度较大的断裂过程.分散相与基体间的化学键合增大该应力场强度有利于加大断裂过程区.     

PHEMA hydrogels obtained by a novel low-heat curing procedure with a potential for in situ preparation

In this work, we report on poly(2-hydroxyethyl methacrylate) (PHEMA) hydrogels obtained by a low heat curing reaction. These materials are suitable for in situ preparation and therefore endowed with a potential for several biomedical applications. The novel procedure adopted involves as the first step the synthesis of a soluble oligomeric PHEMA precursor containing polymerizable functions as side substituents. As the second step, the precursor is dissolved in equal amounts of 2-hydroxyethyl methacrylate (HEMA) and water, to form a viscous but still injectable syrup. A low temperature water soluble initiator is then added. The curing reaction starts promptly and is completed within few minutes. During the entire process the internal temperature never rises above 40 degrees C. Preliminary mechanical characterizations performed on the hydrogels in their water-swollen state and diffusion tests in absorption/desorption experiments clearly indicated that on all respects the novel hydrogels are comparable with conventional PHEMA hydrogels obtained according to literature from HEMA in the presence of divinyl crosslinkers. However, the much shorter curing time combined with the far lower curing temperature endow the new hydrogels with a higher potential in view of specific surgical requirements, and particularly for in situ preparation.     

手性液晶掺杂剂（S）—4‘—辛氧基—4—（2—酰氧基—丙氧基）联苯的合成

手性液晶掺杂剂（Ｓ）┐４┐辛氧基┐４┐（２┐酰氧基┐丙氧基）联苯的合成马汝建李培荣国斌＊（华东理工大学化学系上海２００２３７）关键词铁电液晶材料，手性液晶掺杂剂，合成，手征性１９９７－０２－０３收稿，１９９７－０８－０７修回铁电液晶显示器所用的材料...     

The effect of grass fiber filler on curing characteristics and mechanical properties of natural rubber

Natural rubber is reinforced with a novel type of grass fiber (Cyperus Tegetum Rox b). The effects of fiber loading of different mesh sizes on curing characteristics and mechanical properties of grass fiber filled natural rubber composite are studied. Since 400 mesh grass fiber loaded natural rubber composite shows superior mechanical properties, therefore the effect of silane coupling agent was studied for this particular composite. Here composites were prepared by using water leached grass fiber. Optimum cure time increases with the increase in fiber loading but the change in scorch time is less. The same trend of increase in optimum cure time is observed in the presence of Si69. But the value is higher compared to that of rubber composite without Si69. With increase in the fiber loading, modulus and hardness of the composite increases but tensile strength decreases. The mechanical properties of the composite, namely moduli at 200 and 300% elongation and hardness increase in the presence of Si69 but tensile strength is less compared to that of the composite without Si69. Elongation at break is not much affected due to the presence of Si69. Copyright © 2004 John Wiley & Sons, Ltd.     

SYNERGISTIC MODIFICATION OF EPDM AND CROSSLINKING AGENT IN IMMISCIBLE BLENDS OF POLYVINYL CHLORIDE WITH LOW DENSITY POLYETHYLENE

The synergism of ethylene-propylene-diene monomer copolymer （EPDM） and dicumyl peroxide （DCP, a crosslinking agent） in low density polyethylene （LDPE）/poly（vinyl chloride） （PVC） blends was investigated. When EDPM and DCP are added to the blends simultaneously, the tensile properties could be improved significantly, especially for the blends with LDPE matrix. For example, incorporation of 10/1 （mass ratio） EPDM/DCP improves the tensile strength of the LDPE/PVC （mass ratio 80/20） blend from 7.9 MPa to 8.5 MPa and the elongation at break from 25% to 503%. Results from selective extraction, phase-contrast microscopy and thermal analysis reveal that the improvement in the tensile properties of the blends with LDPE matrix is principally due to the formation of a fine crosslinking network of the LDPE and EPDM phase. The outstanding modification effect of EPDM is explained by its dual functions： molecular entanglement with LDPE and the enhanced efficiency of DCP in the blends.