本文报导了以玻碳电极为基体的１：１２硅钼杂多阴离子薄膜化学修铈电极的制备及其电化学特性。并应用于导数伏安法测定。在４．０×１０￣（－３）ｍ０ｌ／Ｌ（ＮＨ＿４）＿６ＭＯ＿７Ｏ＿（２４）－６．８×１０￣（－２）ｍｏｌ／ＬＮａ＿３Ｃｉｔ－０．４８ｍｏｌ／ＬＮＨＯ＿３体系中，硅浓度在８．３×１０￣（－７）～１．７×１０￣（－３）ｍｏｌ／Ｌ范围内与峰电流呈良好线性关系，检测限为８．０×１０￣（－７）ｍｏｌ／Ｌ。对可溶性硅（以ＳｉＯ＿２计）为２４５．０５ｍｇ／Ｌ的黑液，稀释１０倍后，取２．００ｍＬ平行测定９次，ＲＳＤ为０．５８％，加标回收率在９７．３％～１０４．４％间。     

涂层对热电偶热电性能及大气中寿命的影响

在难熔金属热电偶表而施加涂层的目的,旨在使原仅限和真空、中性及还原气氛中测量的热电偶能在大气中使用.本文讨论涂层对难熔金属热电偶在氧化气氛的"热电势—温度","热电势—时间"的关系及其寿命的影响.具有涂层的W/M.热电偶在氧化气氛(常压下1500℃取得263小时±1%t的最高记录,而W-Re热电偶存1500℃试验的前70小时偏差也在1%t内.而没有涂层的热电偶仅支持数分钟便破坏.     

有机硅氨基酸衍生物的研究

本文利用含氢有机硅化合物与含双键的氨基酸酯的加成反应,合成了5种新的有机硅氨基酸衍生物。介绍了一种合成N-烷基取代氨基酸酯的新方法。对新化合物进行了元素和光谱分析鉴定。     

四环素类抗菌素碱性降解荧光增敏作用研究

四环素类抗菌素的碱性溶液(KOH)在沸水浴中加热一定时间而发生降解,其降解物的荧光激发光谱和发射光谱均发生改变,且荧光强度较四环素类抗菌素本身的天然荧光增强5～190倍,认为发生了分子内亲核断环反应,生成具有内酯结构的降解物,此降解物内酯结构中氧原子上孤对电子与共轭π电子相互作用.使分子中共轭电子体系的离域性增大,荧光增强.     

A novel trilinear decomposition algorithm： Three-dimension non-negative matrix factorization

Non-negative matrix factorization(NMF)is a technique for dimensionality reduction by placing non-negativity constraints onthe matrix.Based on the PARAFAC model,NMF was extended for three-dimension data decomposition.The three-dimension non-negative matrix factorization(NMF3)algorithm,which was concise and easy to implement,was given in this paper.The NMF3algorithm implementation was based on elements but not on vectors.It could decompose a data array directly without unfolding,which was not similar to that the traditional algorithms do.It has been applied to the simulated data array decomposition andobtained reasonable results.It showed that NMF3 could be introduced for curve resolution in chemometrics.     

桑蚕丝素蛋白初始结构对其矿化作用的影响

以碱金属离子诱导桑蚕丝素蛋白溶液发生构象转变, 研究了蛋白质初始结构对其矿化作用的影响. FT-IR, XRD和SEM等测试结果显示, 未经任何处理的桑蚕丝素蛋白溶液矿化后形成片状复合物, 其无机相以二水磷酸氢钙(DCPD)为主; 而经过K^＋和Na^＋金属离子处理后, 桑蚕丝素溶液的结构由无规线团/螺旋构象向β-折叠发生转变, 矿化后成纤维状, 并相互结合呈现纳米级的三维多孔结构, 其无机相以热力学稳定的羟基磷灰石(HA)为主. 可以认为, 丝素蛋白结构转化为较伸展的β-折叠后, 使得更多的亲水基团暴露在外面, 在丝素蛋白分子不断凝聚成纤过程中, HA结晶快速生长并附着在这些微纤上, 最终形成纤维状的丝素蛋白/HA复合物. 该结果为阐明蛋白质的生物矿化过程及其调控机理提供了理论依据, 同时可以从矿化复合物的形成来反映这些微量元素可能对骨组织形成的影响, 为临床骨组织的修复提供一定的参考.     

Use of Silicon Substituents in the Syntheses of Natural and Non-natural Molecules

Trimethylsilyl groups have been used in our research as a director as well as a bulky and lipophilic group in our quest for natural and non-natural molecules.     

Phenylsulfonic Acid Functionalized Mesoporous Silica Catalyzed Transetherification of Alcohols with Dimethoxymethane

Phenylsulfonic acid functionalized mesoporous silica was synthesized by condensation of tetraethylorthosilicate with phenyltrimethoxysilane, and then sulfonation using 30% fuming sulfuric acid. The material was characterized using FT‐IR, DSC, XPS, TEM and N2 adsorption/desorption measurements. DSC revealed that sulfonic acid group of the catalyst was decomposed at 354.8°C, indicating that the catalyst exhibited high thermal stability. XPS showed that there existed three kinds of different silicon species on surface of the catalyst. The catalytic performance of the catalyst was evaluated using transetherification of alcohols with dimethoxymethane. It was found that among primary alcohols, the selectivities of the two long‐chain alcohols for n‐dedocanol and n‐tetradecyl alcohol were higher than 97.0% at the conversions of 43.6% and 65.3%, respectively, while the selectivities of the short‐chain alcohols except for n‐hexanol were less than 90.0% at the conversions of over 80.0%. Due to steric barrier, the secondary alcohols such as iso‐butanol and cyclohexanol afforded conversions of 79.4% and 60.5%, and the selectivities of the two alcohols were more than 90.0%. The sequence in conversion of the substituted phenols is as follows: p‐nitrophenol>p‐fluorophenol≥p‐bromophenol>p‐cresol>m‐cresol.     

钛硅分子筛的结构表征及催化性能研究

以ＴＰＡＢｒ为模板剂，氨水等为碱源合成了钛硅分子筛ＴＳ－１，并利用ＸＲＤ，ＩＲ，元素分析，ＵＶ－ＶＩＳ，热分析等手段对合成的分子筛进行了表征，通过丙烯环氧化反应合成的ＴＳ－１催化性能。结果结果，ＴＳ－１凝胶与产品的硅钛与基本一致；随着硅钛比的降低，ＴＳ－１由单斜晶系过渡为正交晶系，在硅钛比为１２９－１６．７的范围内，随着进入骨架的钛量增加，单胞体积增大；