SYNERGISTIC MODIFICATION OF EPDM AND CROSSLINKING AGENT IN IMMISCIBLE BLENDS OF POLYVINYL CHLORIDE WITH LOW DENSITY POLYETHYLENE

The synergism of ethylene-propylene-diene monomer copolymer （EPDM） and dicumyl peroxide （DCP, a crosslinking agent） in low density polyethylene （LDPE）/poly（vinyl chloride） （PVC） blends was investigated. When EDPM and DCP are added to the blends simultaneously, the tensile properties could be improved significantly, especially for the blends with LDPE matrix. For example, incorporation of 10/1 （mass ratio） EPDM/DCP improves the tensile strength of the LDPE/PVC （mass ratio 80/20） blend from 7.9 MPa to 8.5 MPa and the elongation at break from 25% to 503%. Results from selective extraction, phase-contrast microscopy and thermal analysis reveal that the improvement in the tensile properties of the blends with LDPE matrix is principally due to the formation of a fine crosslinking network of the LDPE and EPDM phase. The outstanding modification effect of EPDM is explained by its dual functions： molecular entanglement with LDPE and the enhanced efficiency of DCP in the blends.     

微交联聚合物降滤失剂的合成与性能

针对深井、超深井钻井液体系中的降滤失剂受长时间高温、高矿化度作用易降解的问题，以氮丙啶与3-氯丙烯反应制得-N-烯丙基氮丙啶（ALAI）； ALAI与乙二胺反应制得四烯基交联剂单体（EAAD）； EAAD与丙烯酰胺（AM）和2 丙烯酰胺基-2-甲基丙磺酸（AMPS）发生水溶液自由基共聚反应，合成了微交联共聚物降滤失剂(PAAT)，其结构和性能经¹H NMR, IR和TG-DTG表征。结果表明：PAAT可抗220 ℃高温，在高温、高矿化度条件下可维持钻井液的滤失量与流变性能，API滤失量均低于4.0 mL，高温高压滤失量均小于13.0 mL。     

流变学法研究部分水解聚丙烯酰胺/Cr(III)交联反应I.浓度的影响

采用流变学法系统地考察了部分水解聚丙烯酰胺（HPAM）/Cr(III)交联体系的 反应动力学。HPAM溶液的粘性模量G”大于弹性模量G’,且其数值随时间不发生变 化,体系为粘性溶液。而HPAM/Cr(III)体系的G’和G”的数值都随时间变化,G” 在反应开始阶段大于G’,当反应进行一段时间后,G’超过G”占据主要地位,体 系成为弹性体系。交联过程可分为三个阶段：第一上升阶段,平缓上升阶段和第二 上升阶段。利用G’～ t曲线可以推测反应机理。实验发现成胶速率随反应物HPAM 和Cr(III)的浓度的增加而增加,而成胶时间缩短。在羧基浓度过量的情况下,交 联反应对Cr(III)浓度的反应级数是1。凝胶的有效弹性交联密度随聚合物浓度的增 加而增,且随凝胶反应的进行而增加。凝胶的交联点间的平均分子量随Cr(III)浓 度的增加和交联反应的进行而下降。     

不同交联度的杜仲胶的红外光谱研究

研究了不同交联度的杜仲胶在室温及加热后红外光谱的变化规律．发现在室温下测定的样品红外光谱在低波数内对应链段变形振动的几个特征峰、加热后会消失或弥散，而交联度的改变对其影响不大，即使材料中结晶完全消失而变成高弹态．因此，推测这些特微峰的存在，应该和杜仲胶弹性网络中交联点间链段存在着明显的构象规整性有关．     

以交联聚乙烯醇为载体的离子交换剂对蛋白质的分离性能

本文对阴离子交换剂ＤＥＡ—ＰＶＴ常压液相离子交换色谱分离蛋白质的性能、分离条件进行了探讨。结果表明其对蛋白质的分离性能良好，容易洗脱。与载体交联聚乙烯醇相比，ＤＥＡ—ＰＶＴ对蛋白质的非特异性吸附明显降低。     

接枝和交联对纳米Si02改性NR／PP共混型热塑弹性体的影响

动态硫化制备纳米二氧化硅（SiO2）改性天然橡胶，聚丙烯共混型热塑性弹性体（NR/PPTPE）．研究了马来酸酐，苯乙烯，过氧化二异丙苯（MAH／St／DCP）多单体“就地”熔融接枝、交联对TPE力学性能、耐溶剂性能和耐热变形性能的影响，并用SEM分析了TPE的断面形貌．结果表明：纳米SiO2和MAH／St／DCP的最佳质量分数分别为0．03和0．0375／0．0188／0．00375时，MAH／St／DCP接枝、交联改性NR／PP／纳米SiO：TPE的力学性能、耐溶剂性能和耐热变形性能最佳．MAH／St／DCP“就地”接枝、交联通过细化交联NR分散相、改善交联NR分散的均匀性和增加两相之间的共交联，使NR与PP两相界面结合强度明显提高，NR／PPTPE的综合性能得到明显的改善．     

A fibrous hypercrosslinked sorbent prepared on PP-ST-DVB matrix via post-crosslinking reaction

A fibrous sorbent possessing abundant micropore structure was firstly prepared via post-crosslinking reaction on the PP-ST-DVB original fiber. Its micromorphology and sorptive properties were investigated, and the results demonstrated that the novel fibrous hypererosslinked sorbent has narrow pore-size distribution, small average porous radius （1.90 nm）, high specific surface area （362.31 m^2/g）, and fine sorptive properties for small organic molecules.     

羟基锆及锆铝交联粘土的合成与表征

制备了锆交联粘土和锆铝交联粘土。锆交联粘土制备条件的研究表明，直接用ＺｒＯＣｌ２．８Ｈ２Ｏ水溶液作交联剂，延长老化时间和增大交联剂浓度有利于制备大比表面积高温有序的锆交联粘土。     

SYNTHESIS AND FLUORESCENCE STUDY OF St／DVB COPOLYMERS LABELLED WITH PYRENE GROUPS

Two kinds of St/DVB copolymer beeds containing(1-pyrenyl) formyl and (1-pyrenyl) methyl groups respectively have been synthesized by both functionalization and copolymerization.The fluorescence spectra of the swollen polymers synthesized are similar in shape to those of the corresponding model compounds,while the intensity ratio of excimer to monomer shows clear dependence on the contents of the pyrene groups.     

铝交联皂石的合成和表征及催化性能

用XRD、化学分析、IR、MASNMR、TPD等手段表征了合成皂石及其铝交联物的结构。结果表明:皂石的交联密度与四面体层电荷和交联条件(Al/土比)有关。在乙醇氨化反应中,交联皂石显示了较好的催化活性和选择性。皂石的交联密度与液相产物分布的关系表明层柱材料对此反应具有择形催化作用。醇氨化反应可能是在吸附态NH_3和气相醇分子间进行的。