INFLUENCE OF DIALKYLZINC IN RARE-EARTH TERNARY CATALYST ON THE COPOLYMERIZATION OF CARBON DIOXIDE AND PROPYLENE OXIDE

Rare-earth ternary catalysts Y（CCl3COO）3-ZnR2-glycerin were prepared for the copolymerization of carbon dioxide and propylene oxide （PO）, where dialkylzincs （ZnR2） were diethylzinc, di（n-propyl）zinc, di（n-butyl）zinc, di（i-propyl）zinc, di（i-butyl）zinc, di（s-butyl）zinc,respectively. The Y（CCl3COO）3-ZnR2-glycerin catalysts displayed the highest catalytic activity at the molar ratio of Y（CCl3COO）3：ZnR2：glycerin = 1：20：10. In the same copolymerization condition, catalysts containing dialkylzincs with branched alkyl group showed lower catalytic activity than that with primary alkyl group. For those catalysts including dialkylzincs with primary alkyl group, their catalytic activity decreases with increasing number of carbon atom in the alkyl group with the following sequence： Y（CCl3COO）3-ZnEt2-glycerin 〉 Y（CCl3COO）3-Zn（n- Pr）2-glycerin〉Y（CCl3COO）3-Zn（n-Bu）2-glycerin. However, the alkyl group in the dialkylzinc does not influence the insertion of PO into the propagation chain end.     

PET导电纤维的制取及研究

以过氧化二苯甲酰为引发剂,使丙烯睛在涤沦(PET)纤维上接枝共聚。接枝纤维在含铜化合物,含硫还原剂溶液中反应,制备PET导电纤维。讨论了影响接枝共聚的各种因素,选择出最佳聚合条件。对该纤维的导电成份和结构以及性能进行了研究。     

[Mn(H_2P_2O_7)_3]~(3-)引发淀粉与丙烯腈接枝聚合反应的动力学研究

以[Mn(H_2P_2O_7)_3]~(3-)为引发剂,研究了丙烯腈与玉米淀粉的接枝共聚反应。由实验结果求出了反应速率与引发剂浓度、单体浓度、淀粉浓度和反应温度的关系,推导并验证了接枝反应动力学模型,探讨了反应机理,求得了接枝反应活化能。     

聚四氢呋喃/聚苯乙烯交联嵌段及接枝共聚物的合成与阻尼性能

Carboxyl vinyl terminated polytetrahydrofuran macromers and telechelic oligomers were synthesized from hydroxyl terminated polytetrahydrofuran by end group conversion. From these macromers or telechelic oligomers and styrene polytetrahydrofuran/polystyrene segmented and graft copolymers were synthesized and the effects of molecular structure on the damping properties of those copolymers were also studied.     

稀土-噻吩甲酰三氟丙酮-4,4′-联吡啶-N,N′-二氧化物三元配合物的合成与表征

首次合成了稀土－噻吩甲酰三氟丙酮（ＴＴＡ）－４，４′－联吡啶－Ｎ，Ｎ′－二氧化物的三元配合物，通过元素分析，确定其组成为：Ｌｎ（ＴＴＡ）３０．５（４，４′－ｂｉｐｙＮ２Ｏ２），通过紫外、红外以及热谱分析，讨论了它们的物理化学性质。     

二氧化碳—环氧丙烷—甲苯二异氰酸酯的三元共聚

二氧化碳和环氧丙烷(PO)在阴离子配位催化剂,如二乙基锌和等摩尔的水作用下,可接式(1)发生共聚。但产物聚丙撑碳酸酯(PPC)的热稳定性较差。改进途径之一是在反应中引入甲苯二异氰酸酯(TDI)进行三元共聚。本文报导在双金属阴离子配位催化剂PBM存在下合成一种热稳定性优于PPC的聚碳酸酯聚氨酯(PCPU)的研究结果(式2)。     

乙烯基硅烷-丙烯酸酯乳液共聚动力学研究

以乙烯基三乙氧基硅烷(VTES)、丙烯酸酯为单体,乙氧基醇磺基琥珀酸二钠(A—102)为乳化剂,合成了有机硅改性丙烯酸酯共聚乳液。研究了乳化剂、引发剂、VTES、反应温度以及功能性单体甲基丙烯酸羟乙酯(HEMA)对乳液共聚反应速率的影响。结果表明:聚合速率随乳化剂浓度、引发剂浓度、HEMA浓度的增大及反应温度的升高而增大,但随VTES浓度增大而逐渐减小。由实验得出恒速阶段聚合反应速率R_p与乳化剂浓度C_E、引发剂浓度C_1及有机硅单体浓度C_(VTES)的关系为R_p∝C_E~(0.35)C_I~(0.48)C_(VTES)~(-0.64),表观活化能E_a为81.1kJ·mol~(-1)。     

芳香共聚酯B-N多种向列织构的形态研究

从一种聚芳酯B-N得到了丝状(包括细丝和粗丝)、纹影状和大理石纹状等与小分子向列液晶相似的多种织构。由于样品淬火后晶片装饰在织构上而不影响分子取向矢的分布,因而可以用化学刻蚀和电镜技术揭示其向错和取向矢图。电镜和光学显微镜的结果相互补充,表明了细丝和粗丝状织构的分子取向矢分布很不相同,是两种不同的织构,而粗化始于第二熔融降温。在这些向列织构中分别发现了S=±(1/2)和s=+1的向错的例子和平面内微区转向壁的证据。     

GMA熔融接枝EPDM的研究

以甲基丙烯酸缩水甘油酯（ＧＭＡ）为接枝单体，过氧化二异丙苯（ＤＣＰ）为引发剂，对三元乙丙胶（ＥＰＤＭ）进行了熔融接枝，在烃链上引入极性基团，以改善ＥＰＤＭ与极性聚合物的相容性。用差示扫描量热计（ＤＳＣ）研究了ＧＭＡ的聚合温度，用富里叶红外（ＦＴ－ＩＲ）、凝胶渗透色谱（ＧＰＣ）对接枝产物进行了表征。实验结果表明，产物的接枝率和凝胶量可以通过反应条件（温度、时间、反应物组成及加料方式）来控制。