Electrochemical Preparation of WO_3 Nanowire Arrays

1 Results Ordered WO3 nanowires arrays have been fabricated by electrochemical deposition with anodic aluminum oxide (AAO) templates and annealing the W nanowire arrays in air at 400 ℃. The morphology and the chemical composition of WO3 nanowires arrays were characterized by Scanning Electron Microscopy (SEM),Transmission Electron Microscopy (TEM), X-ray Photoelectron Spectroscopy (XPS), and X-ray diffraction (XRD). The results show that the diameters of the WO3 nanowires are about 90 nm, which is in go...     

贫水电解质体系制备多孔阳极氧化铝模板的研究

在有机溶剂为主的含草酸电解质中,研究了大孔径有序度高的阳极氧化铝(AAO)的一步法电化学制备.实验证实,电解质中水含量的降低能够有效抑制铝的电氧化速率和溶解速率,使得其氧化膜孔道的生长能够稳定进行,所得到的六方孔道排列有序度明显高于纯水溶剂制备的电解质体系下的产物.考察了水含量、有机溶剂种类以及电解质浓度对AAO模板孔道形貌的影响.结果表明,有机溶剂贫水电解质体系使得电氧化电压的选取范围比水溶液电解质体系更宽,孔径连续可调,反应条件温和.该方法适合于制备均匀大孔径的AAO模板.     

纳米级铝阳极氧化膜的形成机理及结构调整

从纳米级阳极氧化铝(AAO)膜对应用的重要性入手，主要简述AAO膜的制备、形成机理、自结构特点及结构调整方法。     

金纳米线阵列的制备及其光学性能研究

采用二次阳极氧化法制备了高度有序的多孔氧化铝模板,并基于该氧化铝模板,采用脉冲直流电化学沉积的方法制备了金纳米线阵列.利用扫描电子显微镜（SEM）、透射电子显微镜（TEM）和X线衍射仪（XRD）对所制备的金纳米线的形貌及晶体结构进行分析.结果表明：不同的沉积电压下制备的金纳米线具有不同的生长取向性,当沉积电压为3V时制备出的金纳米线沿[200]方向具有明显的生长取向性.利用紫外-可见光谱（UV-Vis）对金纳米线阵列光学性能进行研究,发现金纳米线的等离子体共振吸收峰随着沉积电压的增大先蓝移而后发生红移.     

Molecular Dynamics in 1- and 2-D Confinement as Studied for the Case of Poly(Cis-1,4-Isoprene)

Broadband Dielectric Spectroscopy (BDS) is used to probe the molecular dynamics of Type A polymer, poly(cis-1,4-isoprene), when confined in the 1-dimensional (1D) exploring space of thin layers and the 2-dimensional (2D) constraining geometry of unidirectional anodic aluminum oxide (AAO) nanopores. For both cases, it was observed that the structural relaxation remains bulk-like in its mean relaxation rate, although the distribution of its relaxation times is broadened in 2D confinement. Furthermore, the fluctuation of the end-to-end vector is interrupted, with the 1D case being relatively less pronounced. By this clear-cut comparison, it is demonstrated that the effects of confinement on molecular dynamics depend, inter alia, on the dimensionality of the restricting space.     

多孔氧化铝模板催化制备定向碳纳米管阵列

Well-aligned open-ended multi-walled carbon nanotube (MWCNT) arrays were prepared via chemical vapor deposition (CVD) method in porous anodic aluminum oxide (AAO) templates without depositing any transition metals as catalyst. Effects of the CVD temperature and heat treatment were studied in detail.Well-aligned open-ended MWCNT arrays were obtained at the CVD temperature above 600 ℃; when CVD temperature is reduced to around 550 ℃, CNTs, CNFs and other structures existed at the same time; no CNTs or carbon nanofibres (CNFs) could be found as the CVD temperature is below 500 ℃, and only amorphous carbon in the porous AAO template was found. Experimental results showed that the AAO template is catalytic during the CVD process, and it has the following two effects: to catalyze thermal decomposition of acetylene and to catalyze conversion of carbon decomposed from acetylene into CNTs or CNFs. Heat treatment could improve the graphitization degree, but it might also introduce new defects.     

Fabrication and magnetic properties of Co nanowire arrays of different crystal structures

It is important to find some developing high-density magnetic recording materials in magnetic recording field with the development of information and technique, in which vertical magnetic recording is a very important way and has received considerable attention[1—3]. The vertical magnetic recording materials require high squareness, suitable coercivity, and small size of storage element[4]. Someone used nanoporous anodic aluminum oxide as templates to fabricate uniform arrays of multi magneti…     

Y2O3:Eu3+纳米线阵列的制备与表征

Y2O3:Eu3+红色荧光粉由于色纯度高、化学性质稳定和量子效率接近100%而广泛用于荧光灯和投影电视等方面.近年来,Y2O3:Eu3+的大量研究工作主要集中于纳米粉末的制备方法及其与体相材料不同的发光特性[1～3].最近,有关Y2O3:Eu3+及其稀土化合物的纳米管、纳米线和纳米带一维材料的制备成为研究热点.Wu Changfeng等[4,5]利用表面活性剂合成了Y2O3 : Eu3+纳米管.激光格位选择激发测试结果表明,Eu3+在纳米管中占据3个不同的格位,其611 nm处的红色发光峰出现了宽化.He Yu等[6]采用水热法及退火处理制备出了Y2O3:Eu3+纳米带,发现Eu3+的发射峰不仅宽化,而且出现了625 nm的新峰.Li Yadong等[7～9]采用水热法制备了稀土氧化物、硫氧化物和氢氧化物等的纳米线和纳米管,并探索了其形成机理,同时发现Y2O3S : yb3+,Er3+具有上转换的性质.     

具有平整表面的定向纳米碳管膜的制备

为了获得表面平整的定向纳米碳管，通过化学及物理的方法将纳米碳管膜进行反转，使其原来的AAO模板底面成为新的表面，用溶液逐步去除表面的铝和氧化铝后，获得了平整的定向纳米碳管膜表面，从而可将其作为工作面使用. 还比较了5％NaOH和6%H₃PO₄＋1.8%H₂CrO₄溶液去除氧化铝的效果.     

利用模板法制备Ag纳米线

利用阳极氧化铝（AAO）作为模板,制备出高定向的Ag纳米线．Ag纳米线的形貌由环境扫描电镜证实,并通过X-射线能谱（EDX）、X-射线粉末衍射谱（XRD）测试手段进行了表征．