金属PTC陶瓷复合材料结构及其导电机理

研究了金属ＰＴＣ陶瓷复合材料的电学性能和其材料组分。结果表明，掺入金属的ＰＴＣ陶瓷材料经氮气中烧结，然后在空气中进行热处理，材料表面形成高势垒层，金属ＰＴＣ陶瓷复合材料的室温电阻较ＰＴＣ的陶瓷高。样品之中存在大量不同类型的极化，在低温时样品电阻较高，温度增加后，大量各种类型离子极化出现，在变价金属铁的变价导电作用下，削弱表面势垒，使金属ＰＴＣ陶瓷复合材料电阻降低，表现出ＮＴＣ现象。在电场作用下，正负电荷、晶粒畸变和空位缺陷等产生空间电荷极化使金属ＰＴＣ陶瓷复合材料有较高介电常数。介电损耗（ｔｇδ）频谱和介电δ温度谱上都出现一个介电峰，其主要原因是跃迁极化，金属阳离子由一个位置跃迁到另一个位置，在介电损耗所对应的频率和温度时出现跃迁极化率最大     

Dehydration and dehydroxylation of reduced charge montmorillonite

Reduced charge montmorillonites (RCM) were prepared by the thermal treatment of lithiumsaturated montmorillonite. Samples prepared by mild thermal treatment with lithium contained more water sorbed than the original montmorrilonite. When RCMs were prepared, part of the lithium cations reacted with hydroxyl groups in the octahedral sheet and released protons, which reacted with the structure. Acid treatment probably enhanced the surface area. which was reflected in the amount of water sorbed. Deprotonation of hydroxyl groups was proved by the measurements of the ignition loss. The heating of lithium saturated montmorillonite at higher temperatures brough about the collapse of the interlayers and a decrease in the amount of water sorbed.     

采用热处理方法提高MEH-PPV单层聚合物有机发光二极管发光性能的研究

对以MEH－PPV为发光层的单层聚合物有机发光二极管（OLED）器件在最佳条件下进行真空热处理，并用金相显微镜观察施加电压后器件的阴极表面形貌。发现处理后的器件阴极表面的气泡及黑斑明显减少。器件的发光性能显著提高。与未经处理的器件相比，最大相对发光强度提高了一个数量级、启亮电压降低了2．0V，半寿命提高了12．7倍。初步分析表明热处理方法提高器件发光性能的主要原因在于有效地减少了器件在工作过程中由于焦耳热产生的某些气体，从而减少阴极表面气泡及黑斑的出现，另一方面，热处理方法也增强了有机发光层与阴极接触界面的结合力，提高电子注入水平。     

新型处理药剂（EP-110）处理各种重金属离子的实验研究

各行各业生产过程中会产生大量废水,重金属离子污染物是其中的重要控制指标,传统的处理方法不能完全解 决这类污染。本文通过大量的实验数据,对新型的处理药剂(EP-110)处理各种重金属离子的性能做了全面的测试、分析,并 提出了使用方法。     

A comparative study of the silent discharge treatment of saturated and unsaturated hydrocarbon polymers

Dielectric barrier air discharge treatment of polyethylene, polypropylene, polyisobutylene, polystyrene, and polyisoprene substrates has been characterized by x-ray photoelectron spectroscopy (XPS). The relative reactivities of these polymers towards silent discharge oxidation are rationalized in terms of ozone molecules interacting with an excited surface. © 1994 John Wiley & Sons, Inc.     

Towards understanding the increase in strength of thermotropic polyesters with heat treatment

Thermotropic copolyester fibers of oxynaphthoate and oxybenzoate have been subjected to conditions that promote solid-state polymerization as well as annealing. The annealing process causes the crystals to perfect with a simultaneous increase in heat of fusion and melting temperature. Solid-state polymerization, a reaction rate-controlled process, causes the polymer viscosity average molecular weight to increase by chain extension from about 14,000 g/mole to more than 87,000 g/mole with a simultaneous impressive increase in tenacity from about 10 g/d (1.2 GPa) to almost 30 g/d (3.7 GPa). To understand the changes in mechanical properties, we have modeled the fiber structure as short rod-like molecules poorly bonded to a continuous matrix of parallel molecules. Lengthening of the reinforcing molecules facilitates better transfer of load from matrix to molecules, resulting in higher tenacity fibers. © 1994 John Wiley & Sons, Inc.     

铸造铝合金(ZL109)激光表面处理

采用功率为2kW级CO_2连续可调式横流激光光源,对不同涂层的ZL109试样表面进行了激光熔凝的实验研究。     

半导体元件清洗技术浅谈

随着社会的进步和科学技术的迅猛发展,对洗净技术的要求也越来越高。清洗方式多种多样,但最主要的是突出在喷射清洗和超声波清洗两大方面,应用于全国各行各业,并且也得到了明显进步。     

A Micellar Route to Ordered Arrays of Magnetic Nanoparticles: From Size‐Selected Pure Cobalt Dots to Cobalt–Cobalt Oxide Core–Shell Systems

Starting with Co‐salt‐loaded inverse micelles, which form if the diblock copolymer polystyrene‐block‐poly(2‐vinylpyridine) is dissolved in a selective solvent like toluene and CoCl₂ is added to the solution, monomicellar arrays of such micelles exhibiting a significant hexagonal order can be prepared on top of various substrates with tailored intermicellar distances and structure heights. In order to remove the polymer matrix and to finally obtain arrays of pure Co nanoparticles, the micelles are first exposed to an oxygen plasma, followed by a treatment in a hydrogen plasma. Applying in‐situ X‐ray photoelectron spectroscopy, it is demonstrated that: 1) The oxygen plasma completely removes the polymer, though conserving the original order of the micellar array. Furthermore, the resulting nanoparticles are entirely oxidized with a chemical shift of the Co 2p_3/2 line pointing to the formation of Co₃O₄. 2) By the subsequent hydrogen plasma treatment the nanoparticles are fully reduced to metallic Co. 3) By exposing the pure Co nanoparticles for 100 s to various oxygen partial pressures pequation/tex2gif-inf-5.gif, a stepwise oxidation is observed with a still metallic Co core surrounded by an oxide shell. The data allow the extraction of the thickness of the oxide shell as a function of the total exposure to oxygen (pequation/tex2gif-inf-7.gif × time), thus giving the opportunity to control the ferromagnetic–antiferromagnetic composition of an exchange‐biased magnetic system.     

浅谈集成电路的废气处理

集成电路的工业废气有含氟化物、硫酸雾的酸性废气,含氨的碱性废气,含异丙醇、光刻胶的有机废气,含SiO_2的含尘废气,以及含硅烷、磷烷的工艺尾气等,这些工业废气中大部分成分是有毒有害的,必须进行有效的处理才能排入大气中。主要讨论上述工业废气的分类、处理方式、应用范围及应用实例等。