不同干燥过程对超细TiO2粉体性质的影响

考察了采用不同干燥工艺制备的TiO2粉体在粒子形貌、颗粒大小与分布、晶相组成以及比表面积和孔结构等织构和结构性质方面的差异。结果表明，利用常规的干燥方法，由水凝胶脱水所得的颗粒，颗粒间严重团聚，颗粒粒径大且分布不均匀，比表面积和孔体积最小；由醇凝胶直接脱水，则可以显著提高粉体的织构性能．而采用超临界流体干燥法则可以进一步提高粉体的性能，比表面积由水凝胶的4．88m2·g－1增大到113．8m2·g－1，提高了近30倍；孔体积由0．027cm3·g－1增大到0．41cm3·g-1．大约提高了15倍；而且其能够有效地防止粒子间的团聚，较好地保持了湿凝胶的网络结构，使颗粒尺寸降低且分布均匀，可重复性好．     

Green synthesis of supported palladium nanoparticles employing pine needles as reducing agent and carrier: New reusable heterogeneous catalyst in the Suzuki coupling reaction

A green method for the synthesis of supported Pd nanoparticles (NPs) using pine needle extract as the reducing agent and the extracted residue of pine needle (RPN) as the carrier is described. The Pd/RPN nanocomposites were characterized using Fourier transform infrared, UV–visible, inductively coupled plasma atomic emission and X‐ray photoelectron spectroscopies, transmission electron microscopy and X‐ray diffraction. The spherical Pd NPs had a mean particle size of 3.25 nm and were evenly distributed on the RPN surface. More importantly, the Pd/RPN nanocomposite, as a heterogeneous catalyst, presented superior catalytic activity for the Suzuki coupling reaction. The yield of the reaction of 4‐bromotoluene with phenylboronic acid catalyzed by Pd_0.03/RPN reached 98% with low Pd loading (0.1 mmol%) at room temperature for 30 min. In addition, the catalyst could be easily separated by centrifugation and reused at least six times without significant loss of activity.     

Preparation of monodispersed polymer-modified colloidal silica particles of less than 50 nm diameter

The preparation of monodisperse, ultrafine polymermodified colloidal silica, 11 or 42 nm in diameter, were studied. The reaction of the colloidal silica with polymeric silane coupler in 1,2-dimethoxyethane and removal of the unreacted polymer with granular silica gel (10–20 mesh) in acetone gave a suspension of monodisperse composite particles.     

超微粒La-Co氧化物催化剂对柴油机尾气碳黑催化燃烧性能的研究

用有机酸络合法制备了Co3O4，NiCo2O4和LaCo2O43种催化剂。通过程序升温氧化反应(TPO)技术对这3种催化剂进行模拟柴油碳黑催化燃烧反应的活性评价。研究发现以Co3O4为活性成分的催化剂能显著降低碳黑燃烧的温度。以Ni和La部分取代Co3O4后形成的复合氧化物NiCo2O4和混合氧化物LaCo2O4能改进Co3O4的氧化活性。但是NiCo2O4不能改进碳黑在松散接触时的燃烧活性；而混合氧化物LaCo2O4由于形成了超微粒含缺陷的LaCoO3钙钛矿型结构，它具有良好的低温氧化活性和表面原子移动性，因而能显著改进碳黑在松散接触时的燃烧活性。     

Chemical preparation and investigation of Fe-P-B ultrafine amorphous alloy particles

A series of Fe-P-B ultrafine amorphous alloy particles has been prepared by the chemical reduction method The composition and size of the particles have been effectively adjusted.Mossbauer spectroscopy in addition to sonic other techniques has been used to investigate the reaction process,the factors that influence the preparation,the crystallization of the particles,and the interactions between the components within them.The results indicate that the co-deposition of iron,phosphorus and boron atoms in the solution at room temperature forms Fe-P-B amorphous alloy particles,and a preferential bonding of Fe-P bond to Fe-B one exists in the particles.     

水热法合成多金属氧酸盐棒状超细晶体

以SrCl₂·6H₂O、(NH₄)₆P₂Mo₁₈O₆₂·nH₂O为原料，在PEG-600/H₂O微乳体系中于80～130 ℃温度下水热反应8～12 h，从而制得一种多金属氧酸盐棒状超细晶体，组成是Sr₃P₂Mo₁₈O₆₂·nH₂O。该超细晶体具有长棒状形貌、高结晶度且分散性能较好，长度范围在10.0～20.0 μm，径度在1.0～2.0 μm。对反应体系中的PEG-600/H₂O体积比(V_PEC-600∶V_H2O)、水热温度以及(NH₄)₆P₂Mo₁₈O₆₂·nH₂O/SrCl₂·6H₂O质量比(W_POMs∶W_SrCl2·6H2O)3个影响因素进行了探讨，结果表明：V_PEC-600∶V_H2O主要对棒状超细晶体的形貌、长径比以及晶体结晶度有着重要影响，体积比在范围V_PEC-600∶V_H2O=(1.50～2.00)∶1.00有利于大长径比的棒状超细晶体的形成；水热温度则优选80～130 ℃范围，过低则不发生反应，过高则发生了多金属氧酸盐与PEG-600的氧化-还原反应；W_POMs∶W_SrCl2·6H2O基本上不影响超细晶体的形成。还初步探讨了该棒状超细晶体的形成机理。     

中国海大陆架沉积物超细标准物质系列研制

5个中国海大陆架沉积物标准物质的原样分别取自东海和南海,样品风干后,先经球磨制备成200目的均匀粉体,再用气流磨进一步加工成超细粒度的均匀样品.采用激光粒度仪检测了样品的粒度分布,5个样品的平均粒度均小于4 μm(约800目).采用高精度的XRF检验了样品的均匀性并以高灵敏度的ICP-AES、ICP-MS相配合确定了其最小取样量(5 mg).有12个实验室参加了合作定值研究,定值组分均为60个,其中MSCS-1,2分别有50和51个组分定为标准值,MSCS-3,4,5有52个组分定为标准值.全组分百分总和分别为99.9%, 99.9%, 100.4%, 100.1%和99.7%.     

Ce-TiO_x超细粒子的模板法制备及结构研究

利用模板法结合真空干燥技术制备出Ce-TiOx超细粒子,用XRD,TG-DSC,TEM等手段进行表征;以甲基橙溶液的光催化降解测试Ce-TiOx超细粒子的催化活性;考察初始物质的量比及热处理温度对Ce-TiOx超细粒子的结构及光催化活性的影响。结果显示:钛干凝胶经400℃热处理可得结晶度较高的锐钛矿型TiO2,800℃时TiO2转变为金红石相;Ce-Ti干凝胶经800℃热处理可得粒径约为45 nm的类球形颗粒;Ce-TiOx超细粒子中,钛以Ti3O5,Ti6O11,TiO2等多种形式存在,铈以CeO2和Ce7O12的形式存在;稀土铈影响Ce-TiOx超细粒子中钛的价态。     

用于直接合成碳酸二甲酯的新型高活性催化剂 A Novel Highly Active Catalyst for the Direct Synthesis of Dimethyl Carbonate

 将CO2直接合成法和酯交换法相结合,通过超强碱的引入和催化剂的微粉化,制备了一种新型的负载于MgO表面的碱-金属盐路易斯酸双组分催化剂,实现了以CO2,甲醇和环氧丙烷为原料的碳酸二甲酯一步直接合成.     

不同热处理方式对超细粒子K—Co—Mo催化剂性能和结构的影响

以柠檬酸为络合剂,采用溶胶－凝胶法制备Co-Mo超细粒子氧化物,所得干凝胶分别置于空气和氩气中进行粒烧,然后经K2CO3助化后硫化。2使用X射线衍射（XRD）,BET比表面测试和扩展X光吸收精细结构（EXAFS）对样品进行结构表征,同时测试硫化态样品的CO加氢合成低碳混合醇活性。XRD结果表明,在空气中焙烧的样品为单一的CoMoO4物种,其晶粒尺寸约为60nm;在氩气中焙烧的样品,柠檬酸的分解对样品起到还原作用,主要物种为CoMoO3 ,同时存在少量的CoMoO4,晶粒尺寸约为20nm。BET结果表明,在氩气中焙烧的样品具有较大的比表面积。硫化态样品中主要物种为MoS2和Co9S8,此外,还可能存在CoMoS3.13物种,XRD和EXAFS结果均表明,在氩气中焙烧的样品硫化后,其晶粒尺寸相对较小,活性测试结果表明,催化剂晶粒尺寸的降低明显促进了合成醇的活性和选择性的提高。