LD侧面抽运板条激光器热效应分析

针对板状Nd:YLF激光介质,在高斯光束抽运情况下,用ANSYS有限元软件模拟了激光介质的热效应,对激光介质中各点的温度和应力分布进行了分析和比较.研究发现双侧抽运与单侧抽运相比,更易获得对称的温度分布,随着抽运光斑横截面变大,抽运面中心温度变低.同时得到板条的棱边、端角处存在较大热应力,且引入的机械应力不可忽视,因此,激光器运转时此区域需防止断裂.     

煤颗粒热膨胀量与破碎特性的研究

煤颗粒的热膨胀破碎特性直接影响流化床锅炉的运行效率.本文利用热机械分析仪(TMA)测定了不同种类不同密度的型煤和原煤的热膨胀特性,并对部分破碎微观形貌进行了FSEM观察;通过旋转炉内的燃烧试验研究了热膨胀特性和破碎的关系.研究表明,煤颗粒在燃烧过程中其热膨胀破碎主要发生在挥发分析出阶段;内部挥发分的析出会使颗粒内压增大而产生膨胀,进而产生细小裂纹并破碎;挥发分越高,颗粒密度越大,其热膨胀形变率越大,越容易发生破碎现象;主要挥发分析出后热膨胀引起的破碎可以忽略.     

Organo-modified magnesium hydroxide nano-needle and its polystyrene nanocomposite

Acrylic acid modified magnesium hydroxide nano-needles (AA–Mg(OH)₂) had been synthesized by alkaline injected into magnesium chloride solution at about 0°C in the presence of acrylic acid (AA). Then the polystyrene/magnesium hydroxide nano-needles composite (PS/Mg(OH)₂) had been prepared by the radical copolymerization with styrene in toluene system using AA–Mg(OH)₂ as a macro-monomer. The elemental analysis (EA) and Fourier transform infrared (FTIR) analyses show that the polystyrene had been grafted onto the surfaces of the nano-needles (AA–Mg(OH)₂). The nano-needles (AA–Mg(OH)₂) had better dispersibility in polystyrene matrix as observed by transmission electron microscope (TEM) analysis. The thermal behavior analysis results from the differential scanning calorimetry (DSC) indicated that the magnesium hydroxide nano-needles had lower thermal decomposition temperature than that of the polymer matrix and it is expected that the nano-needles prepared by the proposed method could be used as an environmental-friendly flame retardant.     

Sinter-active nanocrystalline CeO<Subscript>2</Subscript> powder prepared by a mixed fuel process: Effect of fuel on particle agglomeration

A modified combustion process, namely a mixed fuel process making use of a mixture of two fuels, such as citric acid and glycine has been developed to prepare nanocrystalline ceria powders. The effect of the mixed fuel and the different fuel to oxidant ratios on the decomposition characteristics of the gels were investigated by simultaneous thermal analysis experiments. It was established from various characterization techniques that the ceria powder prepared through the mixed fuel process has got the optimum powder characteristics, namely, a surface area of 33.33 m²/g and a crystallite size of 14 nm compared to the powders produced through the combustion process using a single fuel like glycine or citric acid. Such powders when sintered at 1250°C resulted in pellets with densities in the range of 94–96% of theoretical density. In this paper, we have carried out systematic studies on the sintering of ceria powders prepared by different approaches. The sintered ceramic from mixed fuel batch, exhibited and retained relative density more than 95% up to 1250°C and this data clearly underscores the ability of this process in developing ceria ceramics with increased stability against reduction.     

Marginal Distributions of Wigner Function in a Mesoscopic L-C Circuit at Finite Temperature and Thermal Wigner Operator

Wigner function in phase space has its physical meaning as marginal probability distribution in coordinate space and momentum space respectively, here we endow the Wigner function with a new physical meaning, i.e., its marginal distributions’ statistical average for q ²/(2C) and p ²/(2L) are the energy stored in capacity and in inductance of a mesoscopic L-C circuit at finite temperature, respectively. PACS numbers: 03.65.-w, 73.21.-b     

Mechanically formed loss-tunable long-period fiber gratings realized on the periodic arrayed metal wires

A new method to tune the peak loss of mechanically formed long-period fiber gratings (MLPFGs) is proposed. Periodic arrayed metal wires are used to obtain the gratings along a single mode fiber (SMF). Self-maintaining gratings are achieved by the bonding force of an UV-adhesive between two glass plates. The initial index modulation formed at room temperature creates a maximum attenuation of −9 dB and −12 dB for coated and uncoated SMF, respectively. By changing the temperature, the peak loss is tuned due to the large thermal expansion of the UV-adhesive. Thermally tunable characteristics caused by the coating layer of the SMF are also described and compared with the results of the device with an uncoated SMF.     

为2007年亚奥赛物理实验命题的体会

笔者被聘为2007年亚奥赛物理实验命题,经过半年多的努力终于将科研成果——激光测温合理地转换为一个奥赛实验试题——干涉法测量玻璃热膨胀系数和折射率温度系数,本文主要介绍了命题过程及体会.     

非晶态As2S8半导体薄膜波导的热处理效应

研究了非晶态As2S8半导体薄膜在热作用下的结构变化效应.采用棱镜耦合技术、喇曼光谱测试技术,确认了As2S8薄膜经热处理后,薄膜密度增高和折射率增大的现象.实验表明,淀积态非晶As2S8半导体薄膜经紫外光饱和照射后,再经退火处理,当光折变在退火温度不低于160℃时,出现不完全可逆现象,可逆程度跟退火温度有关.实验显示,退火态非晶As2S8半导体薄膜在玻璃转化温度130℃时退火处理,光折变存在完全可逆现象.光传输实验显示,热处理后的非晶态As2S8半导体薄膜波导,其传输损耗减小了约4dB/cm.     

掺Sn的In2O3透明导电膜生长优先取向对其光电性能的影响

采用反应热蒸发法制备掺Sn的In2O3(ITO)透明导电膜,系统研究了ITO薄膜生长的优先取向对其光电性能的影响.结果表明,ITO薄膜(400)取向的优先生长对其透过率影响很小,但可明显增加载流子迁移率,从而有效降低了薄膜的方块电阻.在两个相同的薄膜硅/单晶硅太阳能电池上分别沉积(222)和(400)ITO优先取向膜,光电转换效率分别为10.3%和12.9%,表明(400)取向更有利于提高电池效率.经优化,最佳衬底温度(Ts)为225℃,最佳氧流量(fO2)为4sccm.在优化的沉积条件下制备ITO薄膜,其电阻率可达到4.8×10-4Ω·cm,可见波段的透过率大于90%,性能指数为3.8×10-2□/Ω.     

立式上胶实践点滴

文章主要从弓纬控制、风量调整、再生热能式焚烧炉三个方面论述了一些实践经验。