Evidences of phase separation in moisture‐cured poly(urethane urea)s by means of temperature modulated differential scanning calorimetry

The degree of phase separation in several moisture‐cured poly(urethane urea)s (PUUs) was studied by FTIR spectroscopy, wide angle X‐ray diffraction (WAXD), and temperature‐modulated differential scanning calorimetry (TMDSC). This latter technique was shown to be particularly useful in analysing the degree of phase separation in PUU polymers. Both phase mixing and phase segregation coexisted in the PUUs and the degree of phase separation increased as the urea hard segment (HS) content in the PUU increased. The maximum solubility of urea HSs into the polyol soft segments (SSs) was achieved for 50 wt % urea HS content in diol‐based PUUs, whereas for triol‐based PUUs the highest solubility between HS and SS was reached for lower urea HS amount. Finally, the higher the urea HS content the higher the extent of phase separation in the PUU. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 3034–3045, 2007     

碳纳米管阵列、捆束的三步升温工艺制备及其形貌与结构

使用结构简单的单温炉设备，通过三步升温热解二茂铁、三聚氰氨混合物方法，在二氧化硅、多晶陶瓷基底上分别合成了碳纳米管阵列、碳纳米管捆束.使用扫描电子显微镜、透射电子显微镜、电子能量损失谱和x射线光电子能谱对合成样品进行了结构和成分分析.结果显示：两种基底上合成的纳米管均为多壁纯碳管；生长于光滑二氧化硅表面的碳纳米管具有高度取向性和一致的外径，长度为10—40μm.碳纳米管采取催化剂顶端生长模式并展示出类杯状形貌；生长于粗糙多晶陶瓷表面的碳纳米管捆束随机取向，碳纳米管直径为15—80nm，长度在几百微米，展示 关键词： 碳纳米管 热解法 三步升温工艺     

Influence of transition metal ions on the textural properties of alumina and aluminasilicates

Accelerated phase transformations and chemical reactions of metastable aluminas and kaolinite, doped with Cu^{2 +}, Mn^{3 +}/Mn^{2 +} and Fe^{3 +}/Fe^{2 +} ions, are accompanied with accelerated decrease of surface area and pore volume values. The phenomena in metal ion doped samples are explained by a catalytic mechanism, in terms of the Jahn-Teller effect. This revised version was published online in June 2006 with corrections to the Cover Date.     

Anti-BZ-Structure in Effect Algebras

The definitions of sharply approximating effect algebras, anti-BZ-effect algebras, central approximating effect algebras, and S-anti-BZ-effect algebras are given, the relationships between sharply approximating effect algebras and anti-BZ-effect algebras, between central approximating effect algebras and anti-BZ-effect algebras are established, and the set of anti-BZ-sharp elements in S-anti-BZ-effect algebras is proved to be an orthomodular lattice.     

LES of turbulent heat transfer: proper convection numerical schemes for temperature transport

Large eddy simulations of two basic configurations (decay of isotropic turbulence, and the academic plane channel flow) with heat transfer have been performed comparing several convection numerical schemes, in order to discuss their ability to evaluate temperature fluctuations properly. Results are compared with the available incompressible heat transfer direct numerical simulation data. It is shown that the use of regularizing schemes (such as high order upwind type schemes) for the temperature transport equation in combination with centered schemes for momentum transport equation gives better results than the use of centred schemes for both equations. Copyright © 2004 John Wiley & Sons, Ltd.     

Photorefractive Four-Wave Mixing Switches Utilizing Pockels Effect -Longitudinal and Lateral Switches-

We carried out detailed calculations for photorefractive wave-mixing switches based on one of three crystals with high electro-optic coefficients, namely, BaTiO₃, Strontium Barium Niobate (SBN (0.75)), and Potasium Sodium Strontium Barium Niobate (KNSBN). A comparison of results for the three crystals shows that a 0_-cut BaTiO³ crystal is suitable for a longitudinal switch and requires a voltage of about 80 for a 2-mm-thick crystal to induce sufficient phase mismatch. The electrodes must be transparent for the incident and diffracted beams. A 45_-cut SBN (0.75) crystal, however, is suitable for a lateral switch and requires a voltage of about 150 for a 1-mm-wide crystal. The electrodes do not need to be transparent.     

Negative luminescence in semiconductors: a retrospective view

Twenty-five years ago, we introduced the phenomenon of negative luminescence (NL) into semiconductor physics. This paper provides an overview of work conducted to develop this fundamental concept. Initially, we consider the first-principle approach to radiation interaction with basic matter and the major properties of NL. Then we describe the problems of NL direct measurements in homogeneous materials and structures. Finally, we emphasize the use of NL approach in applications involving devices for infrared (IR) wavelength (3–12 μm) high-temperature (300–400 K) optoelectronics. Our subjects will include NL IR emitting diodes, radiative coolers, IR dynamic scene simulators, light up-conversion devices, and the Stealth effect in IR.     

Ultrafast softening in InMnAs

We have used two-color time-resolved magneto-optical Kerr effect spectroscopy to manipulate and detect dynamic processes of spin/magnetic order in a ferromagnetic semiconductor InMnAs. We observed ultrafast photo-induced “softening” (i.e., transient decrease of coercivity) due to spin-polarized transient carriers. This transient softening persists only during the carrier lifetime (2 ps) and returns to its original value as soon as the carriers recombine to disappear. Our data clearly demonstrates that magnetic properties, e.g., coercivity, can be strongly and reversibly modified in an ultrafast manner. We attribute the origin of this unusual phenomenon to carrier-mediated ferromagnetic exchange interactions between Mn ions. We discuss the dependence of data on the pump polarization, pump intensity, and sample temperature. Our observation opens up new possibilities for ultrafast optical manipulation of ferromagnetic order as well as providing a new avenue for studying the dynamics of long-range collective order in strongly correlated many-body systems.     

穆斯堡尔谱法及其应用

文章简介了穆斯堡尔效应、穆斯堡尔谱的产生以及穆斯堡尔效应的应用 ,说明它不仅在理论上具有深刻的意义 ,又有着广泛的应用价值 .     

Self-bonding in an amorphous polymer below the glass transition: A T-peel test investigation

Films of amorphous polystyrene (PS) with a weight-average molecular weight (M_w) of 225 × 10³ g/mol were bonded in a T-peel test geometry, and the fracture energy (G) of a PS/PS interface was measured at the ambient temperature as a function of the healing time (t_h) and healing temperature (T_h). G was found to develop with (t_h)^1/2 at T_h = T_g-bulk − 33 °C (where T_g-bulk is the glass-transition temperature of the bulk sample), and log G was found to develop with 1/T_h at T_g-bulk − 43 °C ≤ T_h ≤ T_g-bulk − 23 °C. The smallest measured value of G = 1.4 J/m² was at least one order of magnitude larger than the work of adhesion required to reversibly separate the PS surfaces. These three observations indicated that the development of G at the PS/PS interface in the temperature range investigated (<T_g-bulk) was controlled by the diffusion of chain segments feasible above the glass-transition temperature of the interfacial layer, in agreement with our previous findings for fracture stress development at several polymer/polymer interfaces well below T_g-bulk. Close values of G = 8–9 J/m² were measured for the symmetric interfaces of polydisperse PS [M_w = 225 × 10³, weight-average molecular weight/number-average molecular weight (M_w/M_n) = 3] and monodisperse PS (M_w = 200 × 10³, M_w/M_n = 1.04) after healing at T_h = T_g-bulk − 33 °C for 24 h. This implies that the self-bonding of high-molecular-weight PS at such relatively low temperatures is not governed by polydispersity. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1861–1867, 2004