用烷基诱导效应指数I和RX分子中质子亲合原子X所带电荷qx及元素电负性XN与 脂肪胺，醇、醚的气相质子亲合PA进行关联，结果表明，脂肪胺，醇、醚的气相碱 性可以用下式定量描述：PA(kJ.mol^-1)-2732.0333-2457.1510∑I-1492.2351qx- 732.6277XN利用上式对64种化合物的气相碱性进行预测，平均相对误差为0．34％ ，预测值和实验值的偏差均在实验误差范围内。     

Preliminary Study on the Effect of pH on Thermal Transformation of Some Diphasic Al2O3-SiO2 Gels

Diphasic Al₂O₃-SiO₂ gels have been synthesized by hydrolyzing ethyl orthosilicate at three different pH ranges in presence of colloidal boehmite. Result shows that dominant mullitization process are sensitive to pH of the gelation process. At highly acidic pH range, solid state reaction between corundum and cristobalite occurs, and develops liquid phase for mullite nucleation. At moderately acidic pH, nucleation and crystallization are most operative for nucleation in aluminosilicate matrix. In highly basic pH region, Al-Si spinel phase develops by incorporation of Si in aluminous phase as intermediary phase. Polymorphic transformation of it may be the cause of sudden mullitization. The changes in crystallization sequence in three distinct processes may be due to variation in the nature and size of silicic acid particle formed by hydrolysis and condensation of TEOS at different pH.     

Phase transitions in ternary caesium lead bromide

Phase transitions in ternary caesium lead bromide (CsPbBr₃) were studied by means of DSC, TMA and high temperature X-ray diffraction. The samples were prepared from the solution by water evaporation and from the melt. on the DSC curves as well as on the temperature dependence of the lattice constants of CsPbBr₃ only two effects were found belonging to the earlier published phase transitions at 88 and 130°C and no further effects. Linear thermal expansion coefficient α of individual CsPbBr₃ modifications were calculated from both TMA and high temperature X-ray diffraction. The structural parameters of the room temperature orthorhombic phase were refined and the results are presented. CsPbBr₃ prepared from the solution contained about 10% of CsPb₂Br₅ and so the DSC curve of pure CsPb₂Br₅ was also measured and an effect at a temperature of 68.5°C was found. This revised version was published online in July 2006 with corrections to the Cover Date.     

SPME – A valuable tool for investigation of flower scent

A novel Headspace Solid Phase Microextraction (HS‐SPME) protocol is proposed for the analysis of floral scent. Volatile compounds emitted from the flower are collected on a Carboxen/PDMS fiber for 1 hour, transferred to the GC, and analyzed by GC/MS. The method completely eliminates the use of organic solvents, does not require special instrumentation, and may readily be performed in the field without access to mains electricity and other energy supplies. The method is robust, sensitive, and reduces the sampling stress on the investigated plant. Since enzymatic reactions in living flowers may cause changes in the composition of emitted fragrance, dried rosemary (Rosmarinus officinalis L.) was used as a stable standard for the method development and optimization. In addition, grape wine was also suggested as homogeneous, bio‐compatible, and relatively stable standard of pronounced and typical scent for the same purpose. The optimized method was used for the comparative investigation of the fragrances emitted by two different species – Lathyrus vernus (L.) and Orchis pallens (L.). Several monoterpenes (C10 compounds) were found as the main fragrance components of lathyrus, while sesquiterpenes (C15 compounds) were typical for the orchid.     

Design and self-assembly of ditopic and tetratopic cavitand complexes

The self-assembly of open ditopic and tetratopic cavitand complexes has been investigated by using monofunctionalized cavitand ligands and suitable metal precursors. In the case of ditopic complexes, self-assembly protocols, leading exclusively to the formation of both thermodynamically stable cis-Pt square-planar complexes 8 and 9 and the kinetically inert fac-Re octahedral complex 14, have been elaborated. The use of cis-[Pt(CH3)CN)2Cl2] as metal precursor led to the formation of monotopic trans-10 and ditopic trans-11 cavitand complexes, while cis-[Pt(dmso)2Cl2] afforded both cis-13 and trans-11 isomers. The self-assembly of tetratopic cavitand complexes has been achieved by using mononuclear [Pd(CH3CN)4(BF4)2] and dinuclear [M2(tppb)(OTf)4] (19: M = Pt; 20: M = Pd) metal precursors. Only the tetratopic dinuclear complexes 21 and 22 were stable. The ligand configuration with two phosphorus and two cavitand ligands at the metal centers is the most appropriate to build tetratopic cavitand complexes with sufficient kinetic stability.     

Formation and Crystallization Behavior of Gels in the Na2O-SiO2-TiO2-ZrO2 System

SiO₂-TiO₂-ZrO₂ and 5Na₂O·95(SiO₂ + TiO₂ + ZrO₂) gels were synthesized and role of Na₂O in gel formation and crystallization behavior of gels were studied. From Si(OC₂H₅)₄, Ti(iso-OC₃H₇)₄, Zr(n-OC₃H₇)₄ and NaOCH₃ solutions in EtOH without H₂O, transparent and opaque gels were obtained. Opaque bulk gels, rich in TiO₂ or ZrO₂ composition in Na₂O containing SiO₂-TiO₂-ZrO₂ system, contain agglomerated spherical particles of diameter small <10 m, in contrast with opaque gels having large particles <30 m in alkali-free SiO₂-TiO₂-ZrO₂ system. Crystallization temperature (Tc) was measured by DTA on dried gels. Compared with the alkali-free SiO₂-TiO₂-ZrO₂ gels, 5 mol% Na₂O containing gels gave lower Tc in SiO₂ rich compositions and higher in TiO₂ rich or ZrO₂ rich compositions.     

Thermal analysis study of the effect of molecular weight on constrained amorphous phase in poly(phenylene sulfide)

We report a thermal analysis study of the effect of molecular weight on the amorphous phase structure of poly(phenylene sulfide), PPS, crystallized at temperatures just above the glass transition temperature. Thermal properties of Fortron PPS, having viscosity average molecular weights of 30000 to 91000, were characterized using temperature modulated differential scanning calorimetry (MDSC). We find that while crystallinity varies little with molecular weight, the heat capacity increment at the glass transition decreases as molecular weight decreases. This leads to a smaller liquid-like amorphous phase, and a larger rigid amorphous fraction, in the lower molecular weight PPS. For all molecular weights, constrained fraction decreases as the scan rate decreases.This research is supported by the U. S. Army Research Office through contract DAAH04-96-1-0009. The authors thank Hoechst Celanese for providing different molecular weight Fortron samples and Dr. George Collins for providing sample information. The authors acknowledge the assistance of Elizabeth Oyebode and Leonardo Grimaldi with sample preparation and MDSC work.     

N-Nosyl-α-amino acids in solution phase peptide synthesis

A highly efficient and practical synthesis of peptides in solution phase has been developed. The procedure is based on the use of p-nitrobenzenesulfonyl (nosyl) group for the protection of the amino function of α-amino acids. Every step of the procedure, protection of the amino function by the nosyl group, formation of the peptide bond, and removal of the sulfonamide group, is characterized by high yields and excellent purity of the final products. The described strategy allows the preparation of short peptide sequences keeping the chiral integrity of amino acid precursors. Compatibility of nosyl group with the side-chain protecting groups used in Fmoc-based strategy is demonstrated. The method here presented is an alternative strategy that could provide advantages for future peptide synthesis.     

SOLID PHASE SYNTHESIS OF ISOXAZOLINES

The solid-phase synthesis of isoxazolines on 2-polystyrylsulfonamidoethanol resin isreported. 2-Polystyrylsuifonamidoethanol resin 1 was reacted with acryloyl chloride to afford2-polystyrylsulfonylamidoethyl acrylate resin 2, which was further reacted with brominatedaldoximes by [3+2] cycioaddition to give isoxazoline resin 4. Resin 4 was treated with aqueous 6mol/L HCI solution to obtain isoxazolines in good yield and purity.     

Adsorption of the Ternary Liquid Mixture Ethanol/n-Octane/n-Hexadecane onto Activated Carbon: I. The Adsorption Excess of the Ternary Mixture and of Its Binary Combinations

The adsorption isotherms of the binary mixtures of ethanol/n-Octane, ethanol/n-hexadecane and n-octane/n-hexadecane onto the activated carbon TA 95 were measured at 278 K, 288 K, 298 K and 308 K and described with mathematical functions. About 300 experimental values of the adsorption excess of the ternary mixture ethanol/n-octane/n-hexadecane onto activated carbon TA 95 at 298 K were measured by gas chromatography inside the ternary triangle. The ternary miscibility gap was determined at three temperatures. A good representation of the ternary data and the calculated activity coefficients (using the UNIFAC model) in three-dimensional space was possible with the help of transformation of coordinates. It was possible, too, by utilization of the conception of the quasi two-component representation of the mole fractions with and without miscibility gap. Several influencing factors on ternary adsorption isotherms were discussed for the system ethanol/n-octane/n-hexadecane/TA 95.