Reactivity Ratios of Butyl Acrylates in Radical Copolymerization with Methacrylates

The reactivity ratios of four butyl acrylates versus methyl methacrylate and tert-butyl methacrylate were determined for their radical copolymerization in 2-butanone solution using the Jaacks method. The reactivity ratios values obtained were positively verified by substituting into the Alfrey-Goldfinger equation, yielding correct copolymer composition for a series of samples obtained from different initial mole fractions of the comonomers.     

Photopolymerization of enzymatically synthesized methacrylated poly(caprolactone) with poly(ethylene glycol) macromonomer

Polycaprolactone (PCL) based α,ω-methacrylated macromonomer (DMPCL) was synthesized via enzymatic ring-opening polymerization (eROP) by using Novozyme 435 as the enzyme immobilized catalyst. DMPCL was further photopolymerized with monofunctional poly(ethylene glycol) methyl ether methacrylate (PEGMA-950) macromonomer and trimethylolpropane triacrylate (TMPTA) as tri-functionalized crosslinking agent in glass vials when CHCl₃ was the solvent and Irgacure 819 was the photoinitiator. Ultraviolet (UV) Light Emitting Diode (LED) bulbs enabled photoinduced reactions at room temperature with low heat generation and high reaction efficiency. The obtained gels were characterized with Fourier Transform Infrared Spectroscopy (FT-IR) and Differential Scanning Calorimetry (DSC). DMPCL participated as an effective crosslinking agent in the photopolymerization of PEGMA-950. Combined usage of DMPCL and PEGMA-950 resulted in significantly more effective polymerization than the separate photopolymerizations of these macromonomers.     

Suppressing the environmental dependence of the open‐circuit voltage in inverted polymer solar cells through a radical polymer anodic modifier

Developing stable, readily‐synthesized, and solution‐processable transparent conducting polymers for interfacial modifying layers in organic photovoltaic (OPV) devices has become of great importance. Here, the radical polymer, poly(2,2,6,6‐tetramethylpiperidinyloxy methacrylate (PTMA), is shown to not affect the absorption of the well‐studied poly(3‐hexylthiophene) (P3HT) and [6,6]‐phenyl‐C₆₁‐butyric acid methyl ester (PCBM) active layer when incorporated into inverted OPV devices, as it is highly transparent in the visible spectrum due to the non‐conjugated nature of the PTMA backbone. The inclusion of this radical polymer as an anode‐modifying layer enhanced the open‐circuit voltage and short‐circuit current density values over devices that did not contain an anodic modifier. Importantly, devices fabricated with the PTMA interlayer had performance metrics that were time‐independent over the entire course of multiples days of testing after exposing the OPV devices to ambient conditions. Furthermore, these high performance values were independent of the metal used as the top electrode contact in the inverted OPV devices. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 311–316     

Tristable switching of the electrical conductivity through graphene quantum dots sandwiched in multi-stacked poly(methyl methacrylate) layers

Tristable switching nonvolatile memory (NVM) devices based on graphene quantum dots (GQDs) sandwiched between multi-stacked poly (methyl methacrylate) (PMMA) layers were fabricated on indium-tin-oxide (ITO)-coated glass substrates by using a solution-processed method. Current-voltage (I-V) curves at 300 K for the silver nanowire/PMMA/GQD/PMMA/GQD/PMMA/ITO/glass devices showed tristable switching currents with high-resistance, intermediate-resistance, and low-resistance states. The device's cycling endurance of the three resistance states remained stable with a distinguishable value for each resistance state over 1000 cycles, and the obtained retention results showed well-distinguished resistance states without degradation for up to 1 × 10⁴ s. Schottky emission, Poole-Frenkel emission, trapped-charge limited-current, and ohmic conduction were proposed as the dominant conduction mechanisms for the fabricated NVM devices based on the obtained I-V characteristics. The described energy-band diagrams confirm the proposed conduction band mechanisms.     

Synthesis and investigation of dual pH‐ and temperature‐responsive behaviour of poly[2‐(dimethylamino)ethyl methacrylate]‐grafted gold nanoparticles

Gold nanoparticles (AuNPs) were synthesized by reduction of chloroauric acid (HAuCl₄) aqueous solution with hydrazine monohydrate. The AuNPs were immediately treated with cysteamine to obtain amine‐functionalized nanoparticles (Au‐NH₂). The reaction of Au‐NH₂ with epichlorohydrin and subsequent treatment with sodium hydroxide gave epoxidized AuNPs (Au‐EP). Then, thiol‐capped AuNPs (Au‐SH) were synthesized by reaction of Au‐EP with cysteamine. A ‘grafting to’ approach was utilized to graft bromine‐terminated poly(N ,N ′‐dimethylaminoethyl methacrylate), synthesized via aqueous atom transfer radical polymerization, with various molecular weights (6280, 25 800, 64 200 and 87 600 g mol⁻¹) onto Au‐SH to obtain Au‐P1, Au‐P2, Au‐P3 and Au‐P4 samples, respectively. All samples were exposed to temperature and pH variations, and Z‐average diameter was monitored using dynamic light scattering. According to the results, polymer‐grafted nanoparticles collapsed at lower temperatures with increasing solution pH for all molecular weight ranges due to deprotonation of tertiary amine groups. However, higher molecular weight polymers were more sensitive to pH variation especially in alkaline media. Also, a high degree of agglomeration was observed for Au‐P4 nanoparticles in alkaline media on increasing the temperature to 55 and 65 °C.     

A degradable atom transfer radical polymerization inimer: Synthesis,polymerization, and cleavage of the resulting polymer products

A novel degradable inimer for atom transfer radical polymerization (ATRP), 2‐(6‐(2‐((2‐bromo‐2‐methylpropanoyl)oxy)ethyl)pyridin‐2‐yl)ethyl methacrylate (PyDEBrMΑ), was synthesized by the two‐step esterification of 2,6‐pyridinediethanol, first with α‐bromoisobutyryl bromide in order to introduce the initiator moiety, and then with methacryloyl chloride in order to introduce the monomer moiety. PyDEBrMA was subsequently used to initiate the self‐condensing ATRP of methyl methacrylate (MMA) to obtain a hyperbranched MMA homopolymer which could be cleaved at the PyDEBrMA residue either by treatment under mildly alkaline hydrolysis conditions (sodium deuteroxide in d₆‐DMSO at room temperature) or thermolysis at 150 °C. The lability of the PyDEBrMA residue arises from the presence in its structure of two 2‐(pyridin‐2‐yl)ethyl ester moieties. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55, 2831–2839     

Grafting onto Wool. XXVII. Graft Copolymerization of MixeD Vinyl Monomers by Use of Ceric Ammonium Nitrate as Redox Initiator

In order to ascertain the effect of a donor monomer, vinyl acetate (VAc), on the graft copolymerization of acceptor monomers, ethyl acrylate (EA) and butyl acrylate (BA), grafting of mixed vinyl monomers (EA + VAc) and (BA + VAc) was carried out on Himachali wool in aqueous medium using ceric ammonium nitrate (CAN) as a redox initiator. Graft copolymerization was carried out at different temperatures for various reaction periods. Percent grafting and percent efficiency were determined as functions of 1) concentration of mixed vinyl monomers, 2) concentration of CAN, 3) concentration of HNO₃ 4) temperature, and 5) reaction time. VAc, the donor monomer, was found to decrease percent grafting of EA and BA onto wool.     

Study of Polymer-Cement Composite Containing Portland Cement and Aqueous Poly (methyl methacrylate) Latex Polymer by Fourier-Transform Infrared (FT-IR) Spectroscopy

The polymer-cement composite is an immiscible band having modified morphology. Polymer phase improves the toughness of brittle cement and has a reinforcing effect, and interactions between cement components and polymers provide stability. In this study, polymer latex [poly(methyl methacrylate), PMMA] – cement paste was prepared with different weight proportions of polymer content. The main scientific objective of this report has been the analysis and the prediction of high strength with the aim of understanding the interactions of PMMA polymer with Portland cement after hydration reaction of cement pastes and curing the specimens for 28 days. The samples were studied by Fourier transform infrared (FT-IR) spectroscopy. The results are critically examined. It is shown that bands support the interaction of PMMA with cement in the composite.     

Microbial Screening of Copolymers of N‐Vinylimidazole with Phenacyl Methacrylate: Synthesis and Monomer Reactivity Ratios

N‐vinylimidazole (VIM), and phenacyl methacrylate (PAMA) copolymerized with different feed ratios using 1,4‐dioxane as a solvent and α,α'‐azobisisobutyronitrile (AIBN) as an initiator at 60°C. Structure and composition of copolymers for a wide range of monomer feed were determined by elemental analysis (content of N for VIM‐units) and by Fourier transform infrared spectroscopy through recorded analytical absorption bands for VIM (670 cm^?1 for C‐N of imidazole ring) and PAMA (1730 cm^?1 for C?O of ester group) units, respectively. Monomer reactivity ratios for VIM (M₁)‐PAMA (M₂) pair were determined by the application of conventional linearization methods such as Fineman‐Ross (F‐R) and Kelen‐Tüdös (KT) and a nonlinear error invariable model method using a computer program RREVM. The molecular weights (_w and _n) and polydispersity indices of the polymers were determined using gel permeation chromatography (GPC). Thermal behaviors of copolymers with various compositions were investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Also, the apparent thermal decomposition activation energies (ΔE_d) were calculated by Ozawa method using the SETARAM Labsys TGA thermobalance. The antibacterial and antifungal effects of polymers were also tested on various bacteria, fungi and yeast.