A Mössbauer spectroscopic study of an industrial catalyst for dehydrogenation of etylbenzene to styrene

Iron oxide catalyst with spinel structure used for dehydrogenation of ethylbenzene is one kind of important catalyst in petrochemical industry. In this work several series of industrial catalyst were prepared with different components and different manufacturing processes. Mössbauer Spectroscopy has been used to determine the optimal components and the better manufacturing process for spinel structure formation. The results may prove useful for producing the industrial dehydrogenation catalyst with better catalytic property.     

Nanocrystalline ceramic films for efficient conversion of light into electricity

Transparent nanocrystalline films of oxide semiconductors such as TiO₂ and Fe₂O₃ have been prepared on a conducting glass support employing a sol-gel procedure. The films are composed of nanometer-sized particles sintered together to allow for percolative charge carrier transport. The internal surface of these films is very high, roughness factors of the order of 1000 being readily obtained. Electric polarization was applied for forward and reverse biasing of the films and the resulting optical changes have been analyzed to derive their flat band potential. Band gap excitation of such nanocrystalline semiconductors produces electron-hole pairs which migrate through the film to be collected as electric current. Steady state photolysis and time resolved laser techniques have been applied to scrutinize the mechanism of light induced charge separation within the nanostructure. When derivatized with a suitable chromophore, TiO₂ films give extraordinary efficiencies for the conversion of incident photons into electric current, exceeding 90% for certain transition metal complexes within the wavelength range of their absorption band. The underlying physical principles of these astonishing findings will be discussed. Exploiting this discovery, we have developed a new type of photovoltaic device whose overall light to electric energy conversion yield is 10% under simulated AM 1.5 solar radiation.     

Metal–Nitrosyl complexes as a source of new vasodilators: Strategies derived from systematic chemistry and nitrosyl ligand reactivity

A series of nitrosyl complexes of empirical formula K_n[M(CN)₅NO], where M = V, Cr, Mn and Co and n = 3, or M = Mo and n = 4, have been prepared which are notional analogues of the widely used vasodilator sodium nitroprusside. Their reactivity towards common nucleophiles (OH^?, NH₂R, NHR₂, HS^? and RS^?), acid and photolysis has been investigated to elucidate the desired properties required of new metal nitrosyls which may have some potential as new non-cyanide-based vasodilators.     

Species differences in the metabolism of arsenic compounds

Humans are exposed via air, water and food to a number of different arsenic compounds, the physical, chemical, and toxicological properties of which may vary considerably. In people eating much fish and shellfish the intake of organic arsenic compounds, mainly arsenobetaine, may exceed 1000 μg As per day, while the average daily intake of inorganic arsenic is in the order of 10–20 μg in most countries. Arsenobetaine, and most other arsenic compounds in food of marine origin, e.g. arsenocholine, trimethylarsine oxide and methylarsenic acids, are rapidly excreted in the urine and there seem to be only minor differences in metabolism between animal species. Trivalent inorganic arsenic (AsIII) is the main form of arsenic interacting with tissue constituents, due to its strong affinity for sulfhydryl groups. However, a substantial part of the absorbed AsIII is methylated in the body to less reactive metabolities, methylarsonic acid (MMA) and dimethylarsinic acid (DMA), which are rapidly excreted in the urine. All the different steps in the arsenic biotransformation in mammals have not yet been elucidated, but it seems likely that the methylation takes place mainly in the liver by transfer of methyl groups from S-adenosylmethionine to arsenic in its trivalent oxidation state. A substantial part of absorbed arsenate (AsV) is reduced to AsIII before being methylated in the liver. There are marked species differences in the methylation of inorganic arsenic. In most animal species DMA is the main metabolite. Compared with human subjects, very little MMA is produced. The marmoset monkey is the only species which has been shown unable to methylate inorganic arsenic. In contrast to other species, the rat shows a marked binding of DMA to the hemoglobin, which results in a low rate of urinary excretion of arsenic.     

Band bending at the Si(1 1 1)–SiO2 interface induced by low-energy ion bombardment

Experiments employing photoreflectance spectroscopy have uncovered band bending due to electrically active defects at the Si(1 1 1)–SiO₂ interface after sub-keV Ar⁺ ion bombardment. The band bending of about 0.5 eV resembles that for Si(1 0 0)–SiO₂, and both interfaces exhibit two kinetic regimes for the evolution of band bending upon annealing due to defects healing. The healing takes place about an order of magnitude more quickly at the (1 1 1) interface, however, probably because of less fully saturated bonding and higher compressive stress.     

溶胶–凝胶法制备ATO-SiO_2抗静电复合薄膜的特性研究

采用两步溶胶–凝胶法制备出 ATO(掺锑氧化锡)-SiO_2复合抗静电薄膜。通过 DTA-TG、XRD、SEM 对 薄膜的结构和形貌进行了表征,结果表明:抗静电复合薄膜表面均匀致密。薄膜中 SiO_2为无定形结构,ATO 的衍射峰 与 SnO_2一致。研究了 SnO_2的含量对薄膜导电性能、结合强度和透过率的影响,发现随 SnO_2含量增加 ?(SnO_2/ SiO_2)从 5 至 12.5,薄膜的表面电阻降低(从 1010ù/□降低到 108ù/□),薄膜的结合强度下降,薄膜的透过率降低(从 89.0%降至 84.2%),结合三方面性能,得出最佳 SnO_2的配比为:?(SnO_2/ SiO_2)=10。     

A double-layer current conduction model for high-κ gate dielectric materials with interfacial oxide or silicate layer

The current-voltage (I-V) characteristics of metal-oxide-semiconductor (MOS) structures with hafnium oxide as the gate dielectric film were studied. Sharp shifts from a low-voltage ohmic regime to a tunneling conduction were observed in the high-voltage range. The paper demonstrates that this behavior can be described very well with a double-layer dielectric model. Excellent fittings of the experimental curves were obtained and the related key structural and physical parameters were obtained. The model fitting further suggests the optimal annealing conditions for preparing the hafnium oxide films.     

The Fundamental Experiments of Red Tide Chemical Forecast

Many food algae and red tide algae were cultivated in the f/2 medium, and the nitric oxide (NO) concentration of the medium and the cell density were determined. The experiments on algae were conducted when different concentrations of NO were added into the medium using two methods. The results show that low concentrations of NO were self-produced by marine algae during the exponential growth period and were about nmol/L level. But at the end of the period, i.e., 2 or 3 days before the cell density reaches the maximum, an NO peak appeared, with the NO concentration reaching 10 nmol/L. The NO threshold concentration exists according to the influence of exogenous NO on the marine phytoplankton growth. One type is the threshold concentration that can promote algae growth, and its value is between 10 and 1 nmol level, or even lower. The other type can inhibit the phytoplankton growth, which is about μmol level or higher. The results indicate that red tide algae are far more sensitive to NO than are food algae. The fundamental experimental outcome above may provide a new clue for red tide chemical forecast by inspecting the NO change.     

Reactivity of a Ti–45.9Al–8Nb alloy in air at 700–900°C

A Ti–45.9Al–8Nb (at%) alloy with a lamellar structure (γ+α₂) was oxidised in air at 700, 800, 850 and 900°C in isothermal and thermal cycling conditions. The reaction progress was followed by thermogravimetric measurements. In isothermal conditions the oxidation kinetics followed approximately a parabolic rate law and the rate constants ranged from about 10^–12 kg² m^–4 s^–1 at 700°C to 10^–10 kg² m^–4 s^–1 at 900°C. The oxide scales were built of Al₂O₃ and TiO₂, the former being the main component of the outermost layer. The oxidation behaviour of Ti–45.9Al–8Nb was referred to a commercial titanium alloy, WT4 (Ti–6Al–1Mn), and selected oxidation-resistant alloys.     

Synthesis, morphology and random laser action of ZnO nanostructures

Three-dimensional (3-D) ZnO random-wall nanostructures and one-dimensional (1-D) ZnO nanorods were prepared on silicon substrates by a simple solid-vapour phase thermal sublimation technique. Optical pumped random lasing has been observed in the ZnO random-wall arrays with a threshold intensity of 0.38 MW/cm² in the emission wavelength from 380 to 395 nm. The optical gain was attributed to the closed-loop scattering and light amplification of the ZnO random-wall. The experimental result suggests that the morphology of nanostructure is the key factor to effect random lasing.