明胶改性聚醚醚酮微载体的制备、表征及性能

微载体因其具有较高的表面积/体积比等优点可以大大提高哺乳动物细胞培养效率,被广泛应用于生物制药和组织工程等领域。 但微载体多为一次性使用,不耐高温,且主要依赖进口,价格昂贵,因而限制了其国内的应用和推广。 聚醚醚酮(PEEK)材料具有良好的生物相容性、化学稳定性及耐高温等特性,是一种优异的微载体材料,但存在熔点高,加工方法单一和生物惰性等缺陷。 本文以浓硫酸为溶剂,乙醇溶液为萃取剂,采用气流辅助滴注/相分离法,将PEEK制备成448 μm左右,尺寸均匀的微球;经氨丙基三乙氧基硅烷(APTES)处理,获得表面氨基化修饰的PEEK微球(PEEK-N);进一步,以N,N'-羰基二咪唑(CDI)为活性中间体,将明胶分子接枝到PEEK-N微球表面,获得表面明胶修饰的PEEK微载体(PEEK-G)。 对材料的物理化学性质、表面接枝量进行表征;并通过体外细胞实验评估其细胞毒性、细胞粘附效率和细胞增殖能力。 结果显示,通过该方法制备成功了3种不同明胶接枝含量的PEEK细胞微载体(PEEK-G1,PEEK-G2,PEEK-G3),其中明胶含量较高的PEEK-G3毒性最低,细胞粘附和增殖效果最理想。     

Effect of Al2O3 nanoparticles on the steel-glass/epoxy composite joint bonded by a two-component structural acrylic adhesive

This paper reports a study on the effect of Al₂O₃ nanoparticles on the adhesion strength of steel-glass/epoxy composite joints bonded by a two-component structural acrylic adhesive. The addition of Al₂O₃ nanoparticles to the two-component acrylic adhesive led to a remarkable enhancement in the shear and tensile strength of the composite joints. The shear and tensile strength of the adhesive joints increased by addition of Al₂O₃ up to 1.5 wt%, which decreased by further addition of the nanofiller. Introduction of the nanoparticles caused a reduction in the peel strength of the joints. DSC analysis revealed that the glass transition temperature (Tg) of the adhesives rose by increasing the nanofiller content. The advancing water contact angle was decreased for adhesives containing nanoparticles. SEM micrographs indicated good dispersions of the Al₂O₃ nanoparticles within the acrylic matrix in the specimens with up to 1.5 wt% Al₂O₃ and revealed that addition of nanoparticles altered the fracture morphology from smooth to rough fracture surfaces.     

Complex new materials from simple chemistry: Combining an amino‐substituted polysiloxane and carboxylic acids

Changes in rheological, adhesive, and swelling properties of quaternary salts, made by adding one of eight mono‐ or six α,ω‐alkanedioic acids (the latter with two to six or nine carbon atoms) to 6‐7PSil (a polysiloxane with 6%–7% of the monomer units contain a 3‐aminopropyl group) have been correlated with the salt structures. The simple acid‐base chemistry initiates drastic changes in the bulk properties of the materials that depend on the amount and type of the added acid. Thus, the quaternized forms of the 6‐7PSil have significantly enhanced viscoelastic and adhesive properties compared to those of the initial polysiloxane, and they can swell selectively liquids based on their polarity. Also, interpenetrating networks have been made in situ by photopolymerization of salts with vinylic carboxylic acids. DFT calculations on model systems consisting of dimethylammonium α,ω‐alkanedioate salts with two to six carbon atoms provide insights into the interactions responsible for the unexpected dependence of the properties of the 6‐7PSil salts on the chain lengths of the diacids. The potential for applying the methodologies described here to systems with other amino‐substituted polymers and other acid types is noted. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55, 3851–3861     

Adhesive fracture of heterogeneous interfaces

We have studied the effect of interface heterogeneity on fracture, at both local and global scales. The single cantilever beam adhesion test was used to investigate interfacial fracture between polycarbonate plates and an elastic/fragile epoxy adhesive. Two surface treatments were applied to a (given) polycarbonate plate giving zones of strong and weak adhesion parallel to the crack direction. Calculated fracture energies differed from those expected from a simple rule-of-mixtures. A perturbation method, proposed by Rice, was used and results compared with crack fronts observed in situ. The technique was applied successfully but the difference in values of stress intensity factor between the zones was found substantially different from the experimental value. In an attempt to explain discrepancies, specimens with discontinuous crack fronts (adhesive and/or plates severed along the strong/weak adhesion frontier) were tested. Good agreement was found with the rule-of-mixtures predictions raising questions about the role of crack front continuity in load transfer.     

Synthesis and Characterization of Poly(ether ether ketone)s with (2,5‐dihydroxy)phenyl Side Group

A new monomer, (2,5‐dimethoxy)phenylhydroquinone (DMPH), was prepared in a two‐step synthetic procedure. One aromatic poly(ether ether ketone)s with 2,5‐dimethoxy phenyl side group (DMP‐PEEK) was synthesized via an aromatic nucleophilic substitution reaction with 4,4′‐difluorobenzophenone (DFB). Poly(ether ether ketone)s with 2,5‐dihydroxy phenyl side group (DHP‐PEEK) was obtained via hydrolysis of methoxy group on the DMP‐PEEK. Both of the high molecular weight polymers could be obtained despite the steric effect of the bulky pendant groups. The two polymers have good solubility at room temperature.     

Regulation of shear stress on rolling behaviors of HL-60 cells on P-selectin

Circulating leukocytes in trafficking to the inflammatory sites, will be first tether to, and then roll on the vascular surface. This event is mediated through specific interaction of P-selectin and P-selectin glycoprotein ligand-1(PSGL-1), and regulated by hemodynamics. Poor data were reported in understanding P-selectin-mediated rolling. With the flow chamber technique, we herein observed HL-60 cell rolling on P-selectin with or without 3% Ficoll at various wall shear stresses from 0.05 to 0.4 dyn/cm2. The results demonstrated that force rather than transport regulated the rolling, similar to rolling on L- and E-selectin. The rolling was accelerated quickly by an increasing force below the optimal shear threshold of 0.15 dyn/cm2 first and then followed by a slowly decelerating phase starting at the optimum, showing a catch-slip transition and serving as a mechanism for the rolling. The catch-slip transition was completely reflected to the tether lifetime and other rolling parameters, such as the mean and fractional stop time. The narrow catch bond regime stabilized the rolling quickly, through steeply increasing fractional stop time to a plateau of about 0.85. Data presented here suggest that the low shear stress threshold serves as a mechanism for most cell rolling events through P-selectin.     

First mushroom-shaped adhesive microstructure: A review

This letter reviews the adhesive and frictional properties of the first mushroom-shaped adhesive microstructure (MSAMS), which has come a long way from inspiration by the attachment devices evolved in beetles to a large-scale industrial production. It was shown to have an that about twice higher pull-off force compared to a smooth control made from the same material measured on smooth substrates. Pull-off forces measured underwater are even higher than those in air. Moreover, it retained adhesive performance over thousands of attachment cycles and initial adhesive capability could be recovered by washing after being contaminated. In shearing, MSAMS exhibits reduced and stabilized friction in comparison with a smooth control, which demonstrated pronounced stick-slip motion, and shows zero pull-off force in a sheared state, allowing the adhesion to be switched on and off. The presence of a fluid in the contact zone showed adhesion enhancement on both smooth and rough substrates. All these features lead us to conclude that MSAMS may have practical potential in a variety of applications.