铌酸锰-还原氧化石墨烯复合光催化剂的构建以及可见光下降解亚甲基蓝

通过水热法和光还原方法成功地制备了铌酸锰-还原氧化石墨烯复合光催化剂。这种复合光催化剂可以明显地提高光催化降解亚甲基蓝的光催化活性,降解效率在60 min内达到了78.2%,是单体铌酸锰降解效率的2倍。通过活性物质捕获实验的研究,增强的光催化性能可以归因于还原氧化石墨烯加速了光生电子-空穴的分离效率,进而解决了低光催化活性的问题。     

Ag_3PO_4/Palygorskite的静电调控合成及可见光催化降解罗丹明B和气相异丙醇

以大比表面的廉价易得的凹凸棒(palygorskite)为载体,借助带电荷界面的静电调控作用,采用吸附-沉积沉淀方法制备磷酸银/凹凸棒(Ag3PO4/palygorskite)复合催化剂.利用X-射线衍射仪(XRD)、场发射扫描电子显微镜(FE-SEM)、原子吸收光谱(AAS)、紫外可见漫反射光谱(UV-Vis DRS)等技术系统地表征催化剂.之所以能够制备高分散性的凹凸棒负载的磷酸银催化剂,主要是因为凹凸棒具有较大的比表面积、带负电荷界面以及适宜的磷酸根前驱体.以可见光催化脱色降解罗丹明B和氧化降解异丙醇为探针反应,考察复合材料的催化性能.研究表明,与纯磷酸银相比,磷酸银/凹凸棒催化脱色降解罗丹明B和氧化降解异丙醇速率分别提高了2和2.5倍.     

光散射法研究丙烯酸十八酯和苯乙烯微乳液 共聚机理

在十六烷基溴化吡啶/叔丁醇/15%丙烯酸十八酯和苯乙烯/水体系的O/W微乳液中,使用动态光散射法,研究其中两种单体共聚反应的成核机理。结果表明,聚合过程中乳胶粒成核位置主要在增溶胶囊的单体微珠中,乳胶粒主要依靠单体微珠不断提供单体而长大。     

Fe掺杂g-C3N4的制备及其可见光催化性能

以硝酸铁和三聚氰胺为原料制备不同含铁量的Fe 掺杂石墨氮化碳（g-C₃N₄）. 采用X 射线衍射光谱（XRD）、紫外-可见（UV-Vis）光谱、傅里叶变换红外（FT-IR）光谱、电感耦合等离子体-原子发射光谱（ICP-AES）、荧光（PL）光谱、X光电子能谱（XPS）等分析手段对制备的催化剂进行了表征. 结果表明,铁以离子形式镶嵌在g-C₃N₄的结构单元中,影响了g-C₃N₄的能带结构,增加了g-C₃N₄对可见光的吸收,降低了光生电子-空穴对的复合几率. 以染料罗丹明B的降解为探针反应系统研究了不同含铁量对g-C₃N₄在可见光下催化性能的影响. 结果表明,m（Fe）/m（g-C₃N₄）=0.14%时,制备的Fe 掺杂g-C₃N₄表现出最佳的光催化性能,120 min 内罗丹明B的降解率高达99.7%,速率常数达到0.026 min^-1,是纯g-C₃N₄的3.2 倍. 以叔丁醇、对苯醌、乙二胺四乙酸二钠为自由基（·OH）、自由基（O₂^-·）和空穴（h_VB⁺）的捕获剂,研究了光催化反应机理.     

单斜与锐钛矿双晶相TiO2/MWNTs复合材料的制备及其可见光光催化活性

以超强耐酸碱的表面活性剂-丁基封端脂肪醇聚氧乙烯醚作为晶型调节剂,利用钛酸丁酯和氢氧化钠的水热反应制备了单斜相与锐钛矿相双晶相TiO₂/多壁碳纳米管(简称MWNTs)复合材料,并考察了复合材料的可见光光催化活性。结果显示:MWNTs的加入可调控TiO₂的晶相组成,增强TiO₂的光催化活性,其中含5%MWNTs的样品具有较高的催化降解效率;随煅烧温度的升高,样品的光催化活性大幅提升。其机理归因于(1)促进单斜相和锐钛矿相双晶相结构的形成;(2)碳纳米管优良的导电作用及碳纳米管/TiO₂间的异质结效应;(3)高温下碳纳米管分解产生的碳元素掺杂作用。     

白色荧光粉NaGd（MoO4）2:Dy3+,Eu3+的水热合成及发光性能

采用谷氨酸辅助水热法合成了八面体形NaGd(MoO4)2:Dy3+,Eu3+白色荧光粉.X射线衍射结果表明,合成的样品为四方晶系的NaGd(MoO4)2纯相.扫描电子显微镜照片显示所制备的粒子为八面体形,各边长约为2μm.荧光光谱结果表明,在NaGd(MoO4)2:4%Dy3+,yEu3+(y=0,0.5%,0.6%,0.7%,0.8%,0.9%,1.0%)样品中,随着Eu3+掺入量的增加,Dy3+的发射峰逐渐减弱,而Eu3+的发射峰逐渐增强,说明Dy3+-Eu3+之间存在能量传递.通过色坐标图可知,当Eu3+掺杂量y=0.9%时,荧光粉的色坐标(0.338,0.281)与标准的白光色坐标(0.33,0.33)接近,表明NaGd(MoO4)2:4%Dy3+,0.9%Eu3+是很好的近紫外光激发下的白色荧光粉.     

Visible Light Photocatalytic Activity of Porphyrin Tin(IV) Sensitized TiO2 Nanoparticles for the Degradation of 4-Nitrophenol and Methyl Orange

A stable metalloporphyrin sensitized TiO₂ (Degussa P25) photocatalyst was prepared by using trans-dihydroxo[5,10,15,20-tetraphenylporphyrin]tin(IV) (SnP) as a sensitizer in a simple impregnation process. The solid diffuse reflectance ultraviolet-visible (UV-vis) spectrum of the SnP sensitized TiO₂ photocatalyst (SnP-TiO₂) indicated that there existed interaction between SnP and TiO₂. It was found that SnP-TiO₂ exhibited an enhanced visible light photocatalytic activity as compared with that over P25 for the degradation of 4-nitrophenol (4-NP) and methyl orange (MO) in aqueous solutions. The mechanism exploration showed that the degradation of MO and 4-NP experienced two different ways, that is, MO was photodegraded by reactive oxygen species and 4-NP was directly photodegraded by the excited state of SnP. Furthermore, it was found that the loading content of SnP had an important influence on the photocatalytic activity of TiO₂. The maximum photocatalytic efficiency was achieved when the contents of SnP were 25 mg and 30 mg per gram TiO₂ for MO and 4-NP, respectively. Importantly, SnP-TiO₂ was particularly stable and the photocatalytic activity was hardly decreased after being recycled seven times in the presence of oxygen, which could be attributed to the easy reductive regeneration of SnP.     

Color Point Tuning in Lu3−x−yMnxAl5−xSixO12:yCe3+ for White LEDs

A series of the solid‐solution phosphors Lu_3?x?yMn_xAl_5?xSi_xO₁₂:yCe³⁺ is synthesized by solid‐state reaction. The obtained phosphors possess the garnet structure and exhibit similar excitation properties as the phosphor Lu₃Al₅O₁₂:Ce³⁺, but with an effectively improved red component in the emission spectrum. This can be attributed to the energy transfer from Ce³⁺ to Mn²⁺. Our investigation reveals that electric dipole–quadrupole interactions dominate the energy‐transfer mechanism and that the critical distance determined by the spectral overlap method is about 9.21 Å. The color‐tunable emissions of the Lu_3?x?yMn_xAl_5?xSi_xO₁₂:yCe³⁺ phosphor as a function of Mn₃Al₂Si₃O₁₂ content are realized by continuously shifting the chromaticity coordinates from (0.354, 0.570) to (0.462, 0.494). They indicate that the obtained material may have potential application as a blue radiation‐converting phosphor for white LEDs with high‐quality white light.