Boride-based nano-laminates with MAX-phase-like behaviour

MAX-phases being usually composed of transition metals, group A elements and carbon/nitrogen are considered interesting materials for many applications because of their tremendous bulk modulus, “reversible” plasticity, and machinability. This is mainly due to their unique kind of bonding comprising covalent, ionic as well as metallic bonds providing “easy” planes of rupture and deformability due to the layered crystal structures.In transition metal boride systems, similar types of bonding are available. In particular the W₂B₅-structure type and its stacking variations allow the synthesis of strongly layered crystal structures exhibiting unique delamination phenomena.The paper presents ab initio calculations showing the similarities of bonding between the ternary carbides and the corresponding ternary or quaternary borides. Formation of boride-based nano-laminates from auxiliary liquid phases, from the melt as well as during sintering and precipitation from supersaturated solid solutions will be discussed by means of SEM and TEM studies. The role of impurities weakening the interlayer bonding will be addressed in particular. The pronounced cleavage parallel to the basal plane gives rise for crack deflection and pull-out mechanisms if the laminates are dispersed in brittle matrices such as boron carbide, silicon carbide or other transition metal borides.     

A novel microwave dielectric ceramic Ca2Zn4Ti16O38: Preparation and dielectric properties

A novel microwave dielectric powder with composition of Ca₂Zn₄Ti₁₆O₃₈ was synthesized through a citrate sol-gel process. The development of crystalline phases with heat-treating temperature for the gel derived powders was evaluated by using thermo-gravimetric analysis and X-ray powder diffraction analysis techniques. The pure phase of Ca₂Zn₄Ti₁₆O₃₈ with crichtonite crystal structure was obtained at relatively low temperature of 1000 °C. The synthesized powder has high reactivity and the dense ceramics with single crystalline phase were obtained at low sintering temperature of 1100 °C. Impedance spectroscopy and microwave dielectric measurements on sintered samples showed the present compound to be a modest dielectric insulator with excellent dielectric properties of ε_r∼47-49, Qf value ∼27,800-31,600 GHz and τ_f∼+45 to +50 ppm/°C. It shows comparable microwave dielectric properties to other moderate-permittivity microwave dielectrics, but much lower sintering temperature of 1100 °C.     

Optimization of firing parameters for ceramic wares by thermal analysis

Aesthetic and utilitarian properties of traditional ceramic wares as well as engineering properties of modern advanced ceramics are attained by maintaining an optimum temperature-time-atmosphere relationship, called firing schedule, in the kiln. The contribution of modern thermal analysis (TA) techniques such as TG/DTG, TG/EGA, TG/MS, DTA, DSC, TDA, etc. in 1) optimizing production steps by raw material quality control, by studying binder burn out, product densification, 2) in simulating appropriate preheating, firing and cooling schedules as well as 3) in developing shorter firing cycles has been extensively reported in recent literature. The paper will first discuss theoretical curves and energy required for ceramic firing and present from the literature selected examples of applications of thermal analysis in ceramic technology.     

Effect of Niobium Modifications to PZT (53/47) Thin Films Made by a Sol-Gel Route

Niobium-modified lead zirconate titanate thin films (PNZT) with nominal compositions, Pb_(1–0.5x) (Zr_0.53 Ti_0.47)_1–x Nb _x O₃:x = 0.02–0.07, have been prepared using a diol based sol-gel route. Single-layer (0.5 m) films were fabricated on platinised silicon substrates by spin-coating. The effect of niobium additions with regard to phase development, microstructure, and ferroelectric and dielectric properties were investigated for different annealing temperatures. For comparison, unmodified PZT films were also prepared. Niobium substitution increased the crystallisation temperatures for perovskite PNZT phase formation. The values of remanent polarisation P _r and dielectric constant _r were found to decrease with the introduction of Nb. For example, in films heated at 700°C for 15 min, the P _r value of an unmodified PZT film was 31 C cm^–2, compared to 17 C cm^–2 for an x = 0.05 PNZT film, whilst respective relative permittivity values fell from 1190 to 600. The highest Nb concentration film, x = 0.07, did not display any switchable polarisation characteristics, which is consistent with high levels of intermediate pyrochlore phase.     

Alkoxide Derived SrBi2Ta2O9 Phase Pure Powder and Thin Films

Phase pure powder and thin films of the novel ferroelectric materials SrBi₂Ta₂O₉ (SBT) have been prepared using the organic precursors. The xero-gel formed was dried and characterized using TGA and DTA to determine the organic burn out and crystallization temperature of SBT. Powder X-ray diffraction was used systematically to check the crystallinity of SBT. Phase pure SBT powder was formed as low as 650°C and thin films at 600°C in comparison to other earlier reported work. SEM micrographs show a grain size of ≈0.1 μm and show crack free films with a film thickness of 2 μm.     

CdSe quantum dot-dispersed DOBAMBC: an electro-optical study

Cadmium selenide quantum dot (CdSe QD) has been used as a dopant in ferroelectric liquid crystal (FLC) 2-methylbutyl 4-(4-decyloxybenzylideneamino) cinnamate (DOBAMBC). Effect of CdSe QD in DOBAMBC on its different electro-optical (E-O) properties has been studied in the SmC* phase. The optical micrographs recorded for the pure and composite material are showing good dispersion of QDs in the FLC matrix. Micrographs of unaligned sample cell revealed that CdSe QDs induce homeotropic alignment of FLC molecules. An appreciable change in the value of E-O parameters like tilt angle, spontaneous polarisation and response time with shifting of SmA–SmC* phase transition temperature has been observed for CdSe QD–DOBAMBC composite. The observed properties of composite system have been discussed on the basis of surface properties of QDs in FLC system.     

Ferroelectric liquid crystals with axially chiral 2,2′-spirobiindan-1,1′-dione cores

The axially chiral mesogens 5-alkoxy-5′-[(4-alkoxybenzoyl)oxy]-2,2′-spirobiindan-1,1′-dione (QL7-n) were synthesised as racemic mixtures and resolved as single enantiomers by preparative chiral phase HPLC. The shorter homologues (R)-QL7-8 and QL7-9 form enantiotropic N* and SmC* phases, whereas the longer homologues (R)-QL7-10 and QL7-12 form an enantiotropic SmC* phase only. Texture analysis showed that the helical pitch of the N* phase is below the wavelength range of visible light; a helical pitch of 187 nm was measured at T – T_NI = –5 K by selective reflection using enantiomerically enriched mixtures of (R)- and (S)-QL7-8 (0.35 ≤ ee ≤ 0.80). Spontaneous polarisations were measured as a function of temperature in the SmC* phase by the triangular wave method. P_S values at saturation range from 102 nC cm^–2 for (R)-QL7-8 to 120 nC cm^?2 for (R)-QL7-9, which are up to three times greater than the highest polarisation previously reported for an axially chiral SmC* mesogen. Optical tilt angles θ were measured as a function of temperature and showed a sharp rise consistent with first-order N*–SmC* or I–SmC* transitions, with values at saturation ranging from 42 to 44°.