本文采用传统固相反应法,成功制备了新型无铅弛豫铁电陶瓷(1-x)[0.9BaTiO₃-0.1Bi(Mg_0.25Ta_0.5)O₃]-xBi_0.5Na_0.5TiO₃。结果表明,较高居里温度的Bi_0.5Na_0.5TiO₃的引入,使得材料体系中建立了更多的以Bi—O耦合为主的极性纳米区域,弥补了因Bi(Mg_0.25Ta_0.5)O₃的加入导致的宏观极化强度的减少,提高了材料的饱和极化强度,实现了较高储能密度的同时具有更好的温度稳定性。在245 kV/cm电场强度下,x=0.2样品的储能密度约为4.01 J/cm³,储能效率约为84.86%,同时该组分在20~170 ℃储能密度的变化率小于5%,储能效率的变化率小于6%,表现出优异的温度稳定性。     

Effect of mechanical force on domain switching in BiFeO_3 ultrathin films

Ferroelectric polarization can be switched by an external applied electric field and may also be reversed by a mechanical force via flexoelectricity from the strain gradient.In this study,we report the mechanical writing of an epitaxial BiFeO3(BFO)thin film and the combined action of an applied mechanical force and electric field on domain switching,where the mechanical force and electric field are applied using the tip of atomic force microscopy.When the applied force exceeds the threshold value,the upward polarization of the BFO thin film can be reversed by pure mechanical force via flexoelectricity;when an electric field is simultaneously applied,the mechanical force can reduce the coercive electric field because both the piezoelectricity from the homogeneous strain and the flexoelectricity from strain gradient contribute to the internal electric field in the film.The mechanically switched domains exhibit a slightly lower surface potential when compared with that exhibited by the electrically switched domains due to no charge injection in the mechanical method.Furthermore,both the mechanically and electrically switched domains exhibit a tunneling electroresistance in the BFO ferroelectric tunnel junction.     

BaPbO_3－Nd_2O_3系陶瓷导电性研究

研究了ＢａＰｂＯ３－Ｎｄ２Ｏ３系陶瓷的导电性，研究表明，此系统陶瓷的导电载流子是氧缺位中存在的施主电子；添加适量的Ｎｄ２Ｏ３，可以改善ＢａＰｂＯ３陶瓷的导电性和ＰＴＣ特性     

ZnVSb基压敏陶瓷中尖晶石相形成机理的研究

ZnO压敏电阻陶瓷是一种典型的“晶界特性”功能陶瓷材料，材料的宏观电学特性与陶瓷的显微组织结构有密切联系。由于ZnSb尖晶石相在使ZnO基压敏电阻陶瓷显微形貌细化和均匀化方面有明显促进作用，自ZnO基压敏电阻发明以来．ZnSb尖晶石在其中的形成机理就成为该陶瓷研究领域的热点。     

单相Ba2Ti9O20柠檬酸凝胶法制备、表征及介电性能

采用柠檬酸凝胶法两步热处理工艺制备了单相Ba₂Ti₉O₂₀。干凝胶在750 ℃热处理得到了物相为BaTi₅O₁₁和Ba₄Ti₁₃O₃₀、尺寸为30～50 nm的前驱体粉体。纳米前驱体具有高表面活性，促使单相Ba₂Ti₉O₂₀在1 200 ℃热处理温度下形成。两步热处理所得的粉体比一步热处理所得的粉体具有更好的烧结和介电特性，两步热处理所得的粉体，在1 250 ℃烧结4 h，可获得理论密度为97%的Ba₂Ti₉O₂₀微波介质陶瓷，其介电性能：ε_r=38.5，Qf=19 320 GHz，τ_f=8.7×10^-6 ℃^-1。     

Preparation and Characterization of Polyborosiloxanesand Their Blends with Phenolic Resin as ShapeableCeramic Precursors简

Two polyborosiloxanes(PBSis) with char yield up to 74.13% at 800 °C were synthesized by the direct polycondensation of boric acid with phenyltrimethoxysilane in diglyme. The PBSis were characterized by gel permeation chromatography, IR spectroscopy as well as1H-,29Si- and11B-NMR. PBSi modified phenol-formaldehyde resins(PBSi/PFs) were prepared at different PBSi/PF mass ratios and were cured at 150 °C. The PBSi/PFs were characterized by IR spectroscopy, scanning electron microscopy, thermogravimetric analysis and tensile test. The results revealed that the cured PBSi/PFs had sea-island morphology and higher char yield than the common PF. PBSi/PF blend with PBSi/PF mass ratio of 0.4:1 had char yield up to 70.83% at 800 °C. The PBSi/PFs had tensile strength similar to PF. The ceramization of PBSi/PFs was also studied. The silicon boron oxycarbide(SiBOC) ceramics formed were characterized by IR spectroscopy and elemental analysis. This method provided a valuable way to prepare easily shapeable polymer blends as ceramic precursors.     

Er~(3+)-Yb~(3+)掺杂SiO_2-SrO-NaF玻璃陶瓷的制备及表征

采用熔融晶化法制备了主晶相为SrF_2的Er~(3+)-Yb~(3+)共掺透明氟氧化物玻璃陶瓷,利用DSC、XRD、SEM、UV-Vis-NIR和荧光光谱对样品的结构、形貌、发光性能进行了测试与表征。研究表明:该体系玻璃最佳热处理温度为620℃,最佳热处理时间为2h,并讨论了Yb~(3+)不同掺杂浓度对Er~(3+)-Yb~(3+)共掺玻璃陶瓷样品上转换发光性能的影响,确定Er~(3+)-Yb~(3+)最佳掺杂浓度比为1∶7,同时观察到了明亮的绿光(522,540 nm)和较弱的红光(656 nm),对Er~(3+)和Yb~(3+)之间的能量传递过程进行了讨论。     

Critical behaviour of the order parameters at the SmC* to SmA phase transition in a ferroelectric liquid crystal mixture

Critical behaviour of the order parameters has been investigated in the ferroelectric liquid crystal mixture ZLI‐3654 in a 7.5 µm thick planar cell. The temperature dependence of the primary (tilt angle) and secondary (spontaneous polarisation) order parameters is considered. The critical exponent (β) has been evaluated from the fitting of the temperature dependence of the experimental data for both tilt angle and spontaneous polarisation. Experimental results are compared with the predictions of the de Gennes and Landau models.     

二氧化钛含量对铈稳定立方氧化锆陶瓷的性能影响

本文用无压烧结法成功制备了高硬度的立方氧化锆陶瓷,研究了氧化锆陶瓷的物相,Vickers硬度,显微结构,相对密度等性能,主要分析了TiO2添加量对Zr0.8Ce0.2O2陶瓷硬度和相对密度的影响。结果表明:烧结助剂TiO2可以有效抑制陶瓷晶粒异常生长,加快气孔排除,促进氧化锆陶瓷烧结致密化,提高陶瓷硬度。最高维氏硬度为20.2 GPa,最高相对密度达到了99.8%。     

金属β－二酮化合物用于MOCVD法生长铁电氧化物薄膜

对用于MOCVD法生长铁电氧化物薄膜的金属β－二酮化合物的制备、结构及性质进行了评述，对它们在生长铁电薄膜中的应用现状进行了介绍，并对它们的应用前景作了展望。