用化学气相沉积法制备了液晶光阀中光电导层———非晶硅薄膜,从实验中得出最佳制备工艺的参数取值。给出了用包络线法测量非晶硅薄膜光吸收系数的原理,测量了样品的光吸收系数随波长的变化规律。得到样品在最佳工艺条件下的光吸收系数高于1×103cm-1。     

Photoluminescence and X-ray Diffraction of Distributed Bragg Reflector

Spectral and structural characteristics of distributed Bragg reflector (DBR) in vertical-cavity surface-emitting lasers were studied with photoluminescence and double- crystal X- ray diffraction measurement. The expected high quality epitaxial DBR structure was verified. In the X- ray double- crystal rocking curves of DBR the zeroth- order peak, the first and second order satellite peaks were measured. Splitting of diffraction peak appeared in the rocking curves was analyzed. The effects of introduced deep energy levels on the structural perfection and optical properties were discussed.     

γ-辐照对纯Y_2SiO_5和Eu~(3+)∶Y_2SiO_5晶体光谱性能的影响

研究了γ-辐照前后纯Y2SiO5和Eu3+掺杂的Y2SiO5晶体吸收光谱的变化,辐照后,未退火和氢气退火的纯Y2SiO5晶体在260~270 nm和320 nm波段产生了附加吸收峰,分别是由F心和O-心的吸收引起的;经过空气退火的纯YSO晶体中,由于消除了氧空位,因此辐照后没有出现色心吸收峰。在Eu3+∶Y2SiO5晶体中,不但有相同的F心和O-心吸收峰,而且还有Eu2+离子在300 nm和390 nm的吸收峰。随着辐照剂量的增加,色心附加吸收峰增强。空气退火能减少Eu3+∶Y2SiO5晶体中的色心,而氢气退火能增加色心。     

Eu- and Yb-induced reconstructions on a vicinal Si(1 0 0) surface

Early stages of rare-earth metal (Yb and Eu) growth on a vicinal, single-domain Si(1 0 0)2 × 1 surface have been studied in the coverage range of 0.1-0.3 monolayer (ML) by low energy electron diffraction, scanning tunneling microscopy, and synchrotron radiation photoemission spectroscopy. We show that Yb induces the 2 × 3 periodicity in the whole range of coverage studied. The 2 × 3 reconstruction coexists with the local 3 × 2/4 × 2 structure at about 0.2 ML of Yb. In contrast, Eu forms the 3 × 2 periodicity at 0.1-0.2 ML, whereas this structure is converted into the 2 × 3 phase at about 0.3 ML. The atomic arrangement and electronic properties of these reconstructions and the adsorbate-mediated modification of surface morphology are investigated.     

Closed-form solutions for a rectangular layer with central crack under anti-plane shear stress

We consider the problem of determining the stress distributionin a finite rectangular elastic layer containing a Griffithcrack which is opened by internal shear stress acting alongthe length of the crack. The mode III crack is assumed to belocated in the middle plane of the rectangular layer. The followingtwo problems are considered: (A) the central crack is perpendicularto the two fixed lateral surfaces and parallel to the othertwo stress-free surfaces; (B) all the lateral surfaces of therectangular layer are clamped and the central crack is parallelto the two lateral surfaces. By using Fourier transformations,we reduce the solution of each problem to the solution of dualintegral equations with sine kernels and a weight function whichare solved exactly. Finally, we derive closed-form expressionsfor the stress intensity factor at the tip of the crack andthe numerical values for the stress intensity factor at theedges of the cracks are presented in the form of tables.     

The spectrum of Nd in rare earth orthoaluminates. The trigonal to orthorhombic transition study of the level

Some structural and spectroscopic features of rare earth orthoaluminates are examined.The trigonal→ orthorhombic transition is studied in a series of Nd_xSm_1−xAlO₃ compounds. The evolution of the crystal structure is followed by X-ray analysis and optical absorption. The free ion and crystal field parameters of Nd³⁺ (4f³ configuration) are determined in LuAlO₃:Nd³⁺.The anomaly of the calculated splitting of the levels is slight, but well characterized in NdAlO₃. The spin correlated crystal field and orbitally correlated crystal field models are tested as well as an empirical correction which was proposed earlier.     

Crystallographic report: Bis(isonicotinonitrile)cadmium diselencyanate, [Cd(SeCN)2(pyCN)2] (pyCN = isonicotinonitrile)

The title compound, [Cd(SeCN)₂(pyCN)₂]_∞, adopts an extended one‐dimensional chain structure in which the neighboring cadmium atoms are bridged by two selenocyanate ions. The central cadmium atom has a distorted octahedral geometry defined by two isonicotinonitrile and four selenocyanate ions in a 4N2Se fashion. Copyright © 2003 John Wiley & Sons, Ltd.     

Crystallographic report: Diiodo[tris(2‐pyridyl)amine]mercury(II), [(C5H4N)3N]HgI2

In mononuclear HgI₂[(C₅H₄N)₃N], mercury is tetrahedrally coordinated by two nitrogen atoms of a tris(2‐pyridyl)amine ligand and two iodides. The coordination moieties are connected by weak intermolecular Hg(II)···I interactions to give a one‐dimensional structure. Copyright © 2003 John Wiley & Sons, Ltd.     

In-Situ Intrinsic Interface Strength Measurement at Elevated Temperatures and its Relationship to Interfacial Structure

A previously developed laser spallation technique has been modified to measure the tensile strength of thin film interfaces in-situ at temperatures up to 1100°C. Tensile strengths of Nb/A-plane sapphire, FeCrAl/A-plane sapphire and FeCrAlY/A-plane sapphire were measured up to 950°C. The measured strengths at high temperatures were substantially lower compared with their corresponding strengths at ambient temperature. For example, at 850°C, the interface tensile strength for the Nb/sapphire (151 ± 17 MPa), FeCrAl/sapphire (62 ± 8 MPa) and FeCrAlY/sapphire (82 ± 11 MPa) interface systems were lower by factors of approximately, 3, 5, and 8, respectively, over their corresponding ambient values. These results underscore the importance of using such in-situ measured values under operating conditions as the failure criterion in any life prediction or reliability models of such coated systems where local interface temperature excursions are expected. The results on alloy film interfaces also demonstrate that the presence of Y increases the strength of FeCrAl/Al₂O₃ interfaces.     

Light Diffraction of Aligned Polymer Fibers Periodically Dispersed by Phase Separation of Liquid Crystal and Polymer

We have confirmed light diffraction of aligned polymer fibers obtained by a phase separation of an anisotropic-phase solution of liquid crystal and polymer. He—Ne laser light passing through the polymer fibers was scattered in the axis vertical to the fibers, and had two peaks of light intensity symmetrical to the center of the transmitting laser spot. The two peaks were found to be caused by light diffraction due to the periodic polymer-fiber dispersion because the peaks corresponded to values calculated by intervals between the fibers. The periodical fiber networks are considered to be formed by anisotropic spinodal decomposition. This effect can be used to measure the dispersion order of the polymer fibers. © 2004 The Optical Society of Japan