Preparation and Characterization of Nano-ZnFe2O4/TiO2 Films

The nano-ZnFe2O4/TiO2 films possess the functions of desulfurization and degradation for organic pollutants. The sols of ZnFe2O4/TiO2 were prepared by sol-gel method and coated on glass and porous ceramic by vertical coating and dipping-lift processes, respectively, and the samples were obtained after drying and sintering. The composition, appearance, absorption spectrum of the films, and the influence of the film on porous ceramic performances were analyzed using SEM, AFM, UV-Vis spectrometer, and mercury porosimeter, respectively, to determine the operation parameters of the multifunction porous ceramic elements for gas-purification.     

First‐principles study of metal/nitride polar interfaces: Ti/TiN

We have examined the optimal interface structure, ideal work of adhesion and bonding character of polar Ti(110)/TiN(111) interfaces by first‐principles density‐functional plane‐wave pseudopotential calculations. Both Ti‐ and N‐terminated interfaces, including six different interface structures, were calculated. The interface structure for each termination, continuing the TiN crystal structure across the interface, has the largest work of adhesion. Although both terminations yield substantial adhesion energies in the range 3–7 J m^?2, the N‐terminated interface is ～4 J m^?2 stronger than the Ti‐terminated interface. Analysis of the interfacial electronic structure shows that the Ti‐terminated interface is a mixed strong, metallic and weak covalent character, whereas the N‐terminated interface is a polar covalent bond similar to the Ti/TiC interface. Further study of the separation of the optimal interface shows that the cleavages will never fracture at the interface due to the strong bonding, which is consistent with the experimental results. Copyright © 2003 John Wiley & Sons, Ltd.     

Ultrahigh Energy Storage Capacitors Based on Freestanding Single-Crystalline Antiferroelectric Membrane/PVDF Composites

Inorganic/organic dielectric composites are very attractive for high energy density electrostatic capacitors. Usually, linear dielectric and ferroelectric materials are chosen as inorganic fillers to improve energy storage performance. Antiferroelectric (AFE) materials, especially single-crystalline AFE oxides, have relatively high efficiency and higher density than linear dielectrics or ferroelectrics. However, adding single-crystalline AFE oxides into polymers to construct composite with improved energy storage performance remains elusive. In this study, high-quality freestanding single-crystalline PbZrO₃ membranes are obtained by a water-soluble sacrificial layer method. They exhibit classic AFE behavior and then 2D–2D type PbZrO₃/PVDF composites with the different film thicknesses of PbZrO₃ (0.1-0.4 µm) is constructed. Their dielectric properties and polarization response improve significantly as compared to pure PVDF and are optimized in the PbZrO₃(0.3 µm)/PVDF composite. Consequently, a record-high energy density of 43.3 J cm⁻³ is achieved at a large breakdown strength of 750 MV m⁻¹. Phase-field simulation indicates that inserting PbZrO₃ membranes effectively reduces the breakdown path. Single-crystalline AFE oxide membranes will be useful fillers for composite-based high-power capacitors.     

CePO_4/Ce-ZrO_2可加工陶瓷性能与断裂机制研究

以Ce ZrO2为基体,通过复合不同加入量的第二相CePO4颗粒,研究了陶瓷材料力学性能的变化,并借助加载能谱仪(EDS)的扫描电子显微镜(SEM)对材料弯曲断口及压痕裂纹扩展方式进行分析。当CePO4加入量为25%时,虽然材料力学性能有一定下降,但已经能用WC刀具进行加工。材料的弯曲断口显示,CePO4在两相体系中的断裂呈层片状形式;加入CePO4后,由于两相之间弱结合界面的存在,压痕裂纹扩展形式发生明显变化,由连续扩展机制过渡为不连续扩展。由这两种机制形成的材料断裂过程是阶段性的,在实际中可以用作材料最终破坏前的预报。     

Microwave assisted low temperature synthesis of sodium zirconium phosphate (NaZr<Subscript>2</Subscript>P<Subscript>3</Subscript>O<Subscript>12</Subscript>)

Sodium zirconium phosphate [NaZr₂P₃O₁₂], a potential ceramic matrix for fixation of high level nuclear waste, was synthesized by heating the mixture of sodium carbonate [Na₂CO₃], zirconyl nitrate hydrate [ZrO(NO₃)₂·5H₂O] and ammonium dihydrogen phosphate [NH₄H₂PO₄] in air, in a resistance heated furnace and a microwave heating system respectively in the temperature range 450 to 650°C. The mixture heated for 1 h in a resistance furnace at 450°C yielded a poorly crystalline NaZr₂P₃O₁₂ [NZP]. Increasing the temperature to 650°C produced a highly crystalline product. The same mixture heated in a microwave oven at 450°C for 1 h however, yielded the most crystalline NZP.In an alternate method, the mixture of sodium dihydrogen phosphate (NaH₂PO₄), zirconium dioxide (ZrO₂) and diammonium hydrogen phosphate [(NH₄)₂HPO₄] heated in resistance furnace at 650°C for the same period did not react in air. It also did not yield the pure product at 450°C when heated in microwave assembly for 1 h.The authors thank the Board of Research in Nuclear Sciences (BRNS) of the Department of Atomic Energy (DAE) for the financial support for this work under the project No. 2000/37/19/BRNS/1959 dtd09-02-02.     

Preparation and Characterization of Nanotitanium Dioxide Coating Film Doped with Fe^3＋ Ions on Porous Ceramic

The nanotitanium dioxide （TiO2） photocatalytic and porous ceramic filtering technique is one of the advanced methods to effectively treat organic wastewater. The TiO2 sol doped with Fe^3＋ ions was prepared by sol-gel processing. The influences of the process conditions of coating nanophotocatalytic material- Fe^3＋-TiO2 film on the surface of porous ceramic filter by dipping-lift method on the performance of porous ceramic filter were studied. The porous ceramic filters have two functions at the same time, filtration and photocatalytic degradation. The results of this study showed that the pH and viscosity of the sol, amount of Fe^3＋ ions doped as well as the coating times greatly affect the quality of coating film, the performance parameters and the photocatalytic activity of the porous ceramic filter. When the pH of the sol is 3-4, the viscosity is about 6 mPa.S, the amount of doped Fe^3＋ ions is about 2.0 g/L, the porous ceramic filter has been shown to have the best filtering performance and photocatalytic activity. In this condition, the porosity of porous ceramic is about 42.5%, the pore diameter is 8-10μm. The degradation of methyl-orange is 74.76% under lighting for 120 rain.     

Mesoporous amorphous MnO<Subscript>2</Subscript> as electrode material for supercapacitor

A kind of novel mesoporous, electrochemical active material, amorphous MnO₂ has been synthesized by an improved reduction reaction and using supramolecular as template. The synthesized sample was characterized physically by thermogravimetric analysis, X-ray diffraction, transmission electron microscope (TEM), and Brunauer–Emmett–Teller (BET) surface area measurement, respectively. Electrochemical characterization was performed using cyclic voltammetry and chronopotentiometry in 2 mol/l KOH aqueous solution electrolyte. The results of BET and TEM analysis indicated that supramolecular template plays an important role in the process of big specific surface area mesoporous material forming. After sintering at 200 °C, the sample still remained an amorphous structure, and its specific capacitance reached 298.7 F/g and presented a very stable capacitance after 500 cycles. In addition, the electrochemical process, such as ion transfer and electrical condition, was also investigated with electrochemical impedance spectroscopy.     

Modification of carbon ceramic electrode prepared with sol-gel technique by a thin film of chlorogenic acid: application to amperometric detection of NADH

The carbon ceramic electrode prepared with sol-gel technique is modified by a thin film of chlorogenic acid (CGA). By immersing the carbon ceramic electrode in aqueous solution of chlorogenic acid at less than 2 s a thin film of chlorogenic acid adsorbed strongly and irreversibly on the surface of electrode. The cyclic voltammetry of the resulting modified CCE prepared at optimum conditions shows a well-defined stable reversible redox couple due to hydroquinone/quinone system in both acidic and basic solutions. The modified electrode showed excellent electrocatalytic activity toward NADH oxidation and it also showed a high analytical performance for amperometric detection of NADH. The catalytic rate constant of the modified carbon ceramic electrode for the oxidation of NADH is determined by cyclic voltammetry measurement. Under the optimised conditions the calibration curve is linear in the concentration range 1-120 μm. The detection limit (S/N = 3) and sensitivity are 0.2 μM and 25 nA μM⁻¹.The results of six successive measurement-regeneration cycles show relative standard deviations of 2.5% for electrolyte solution containing 1 mM NADH, indicating that the electrode renewal gives a good reproducible and antifouling surface. The advantages of this amperometric detector are: high sensitivity, excellent catalytic activity, short response time t < 2 s, remarkable long-term stability, simplicity of preparation at short time and good reproducibility.     

Electroanalytical Study of the Composition of the Raw Pigment Mixtures that Yield the Metallic Lustre on Ceramics. A Link Between Composition and Final Result

Voltammetry of immobilized microparticles was used to study the electrochemistry of the raw pigments that produce the metallic lustre on ceramics after a successful firing. To study this influence of the mixture components on the reduction properties to achieve the metallic lustre, 14 mixtures of illitic clay, Fe₂O₃, HgS, CuO and AgNO₃ were prepared and studied in different media. Iron oxide improves the yield of the reduction of the metals and cinnabar helps a closer reduction of silver to copper reduction and prevents the Ag? Cu alloying because of the formation of silver–mercury adducts. The presence of one of the metals influences the peak position of the other metal. The use of vinegar as diluting agent is not casual, because in this media the reduction of silver takes place at a potential closer to the copper. This electroanalytical technique allowed to distinguish between powders of different composition and offered some information about the role of the components in the reduction of copper and silver and the selection of vinegar to prepare the raw pigment suspensions.     

Topical Problems in Elemental Analysis of Advanced Ceramic Materials

Selected prominent problems in the analysis of advanced ceramic materials are surveyed. The importance of reliability of results is discussed in the field of elemental trace- and microanalysis in view of its interaction with economy, power of detection, local resolution and speciation selectivity. Particular problems in the analysis of major constituents, trace components and microlocal distributions are based on the striking propertics of ceramics; they are exemplified. Analytical assistance must start from the beginning of the production processing, in the preparation of the powdered base materials. Determination of the stoichiometry requires high accuracy and differentiation of chemical species in bulk and surface analysis of ceramic base powders. Element trace determination by direct instrumental methods requires standard reference materials for calibration; these are currently inavailable in a sufficient variety. For optimum reliability and power of detection, element traces must be prepared in isolated form in a small excitation volume for analysis. A review on the state-of-the-art of wet-chemical combined procedures is presented. Decomposition position procedures are emphasized, due to their risk of contributing severe systematic error. Combustion in elementary fluorine is presented for decomposition of refractory materials. The performance of some direct procedures is discussed. Very efficient methods are available for element trace determinations in ceramic materials, offering high detection power. Several approaches for high-resolution local microanalysis in non-conductive ceramic materials are identified as the most promising development in the analysis of sintered compact ceramic products and devices.