Beiträge zu den Eigenschaften von Titanaten mit Ilmenitstruktur. II. Zur Thermodynamik und elektrischen Leitfähigkeit von NiTiO3 und anderen oxidischen Phasen mit Ilmenitstruktur

Contributions to the Properties of Titanates with Ilmenite Structure. II. Study on the Thermodynamics and the Electrical Conductivity of NiTiO₃ and Other Phases with Ilmenite Structure NiTiO₃ shows a phase transition at high temperatures (T_c = 1290°C). The standard enthalpy and entrop of the reaction NiO + TiO₂ = NiTiO₃ was estimated for temperatures above and below the transition temperature using emf-measurements based on the following solid state galvanic cell: Ni,TiO₂, NiTiO₃|ZrO₂(+CaO)|Ni,NiO. The transition enthalpy was found to be 18 ± 2 kJmol^?1, The transition entropy is 12 ± 1 JK^?1mol^?1. This is in good agreement with the calculated entropy change for an order-disorder transition (11.5 JK^?1mol^?1). The influence of other cations like Mg²⁺ and Co²⁺ on the transition temperature was investigated by measurements of the electrical conductivity as a function of composition. Ni_1?xMg_xTiO₃ shows a strong shift of the transition to higher temperatures if a small part of the Ni²⁺ was replaced by Mg²⁺. A linear correlation between the temperature shift and the amount of Co²⁺ was found for Ni_1?xCo_xTiO₃. Thermoanalytical investigations reveal an endothermic peak during the heating period some degrees below the melting point of CoTiO₃. The substitution of Ge⁴⁺ for Ti⁴⁺ is without any influence on the transition temperature. By doping the NiTiO₃ with Ga₂O₃, the anomalous increase of the electrical conductivity with temperature is shifted to lower temperatures.     

一种新型低温共烧堇青石基微晶玻璃

采用传统的玻璃熔融工艺制备MgO-A12O3-SiO2-Bi2O3（MASB）玻璃粉末，研究了其烧结特性和析晶过程。结果表明，该玻璃粉末可在低于900℃烧结。在烧结中玻璃首先析出μ-堇青石，然后转变为α-堇青石，氧化铋没有参与晶相的形成。该微晶玻璃具有低介电常数（5．23），低介电损耗（约0．2％）和低温烧结特性，可用于超高频片式电感领域。     

微波烧结法制备Ba0.65Sr0.35TiO3热释电陶瓷

采用溶胶－凝胶工艺制备了（Ba,Sr)TiO3凝胶，并利用微波烧结技术对粉体进行了合成和烧结，获得了晶粒尺寸在1μm以内的Ba0.65Sr0.35TiO3热释电陶瓷。对样品的介电特性和热释电特性进行了测试，分析了微波烧结工艺对材料电性能的影响。实验结果表明：该工艺可将钙钛矿相的合成温度由1100℃降低至900℃，并在1310℃烧结25min获得细晶粒的Ba0.65Sr0.35TiO3，其热释电系数和介电常数与传统陶瓷相差不大，从而材料的热释电响应优值因子要比传统方法获得的样品提高了近1倍。     

A sonochemical synthesis of SrTiO3 supported N-doped graphene oxide as a highly efficient electrocatalyst for electrochemical reduction of a chemotherapeutic drug

A sonochemical based green synthesis method playa powerful role in nanomaterials and composite development. In this work, we developed a perovskite type of strontium titanate via sonochemical process. SrTiO₃ particles were incorporated with nitrogen doped graphene oxide through simple ultrasonic irradiation method. The SrTiO₃/NGO was characterized by various analytical methods. The nanocomposite of SrTiO₃/NGO was modified with laser-induced graphene electrode (LIGE). The SrTiO₃/NGO/LIGE was applied for electrochemical sensor towards chemotherapeutic drug detection (nilutamide). Cyclic voltammetry (CV) and differential pulse voltammetry (DPV) techniques have been used to examine the electrochemical performance of nilutamide (anti-cancer drug). DPV was found to be more sensitive and found to exhibit a sensitivity 8.627 µA µM⁻¹ cm⁻² for SrTiO₃/NGO/LIGE with a wide linear range (0.02–892 µM) and low Limit of detection (LOD: 1.16 µM). SrTiO₃/NGO/LIGE has been examined for the detection of nilutamide in blood serum and urine samples and obtained a good recovery in the range of 97.2–99.72 %. The enhanced stability and selectivity and practical application results indicates the suitability of SrTiO₃/NGO/LIGE towards the detection of nilutamide drug in pharmaceutical industries.     

NZFO-PZT磁电复合纳米纤维的制备及其吸波性能

采用静电纺丝法制备(1-x)Ni_0.5Zn_0.5Fe₂O₄-(x)Pb(Zr_0.52Ti_0.48)O₃(简称为(1-x)NZFO-(x)PZT, x=0.1、0.2、0.3、0.4、0.5)磁电复合纳米纤维, 研究了PZT含量对复合纳米纤维结构、电磁特性及微波吸收性能的影响。所有样品均由尖晶石结构NZFO和钙钛矿结构PZT两相所组成。由于NZFO磁损耗与PZT介电损耗的协同效应及界面效应的加强, 适量PZT相的引入可改善复合纳米纤维吸波涂层的电磁阻抗匹配和衰减特性, 提高微波吸收性能。x=0.3和0.4的复合纳米纤维分别在低频和高频范围表现出最强的微波吸收能力。当涂层厚度为2.5~5.0 mm时, x=0.3样品的最小反射损耗在6.1 GHz处达-77.2 dB, 反射损耗小于-10 dB的有效吸收带宽为11.2 GHz(2.8~12.9和16.9~18 GHz);x=0.4样品的最小反射损耗位于18 GHz处为-37.6 dB, 有效吸收带宽达到12.5 GHz(3.3~12.5和14.7~18 GHz)。     

Effect of carbon nanotubes addition on electrochemical performance and thermal stability of Li4Ti5O12 anode in commercial LiMn2O4/Li4Ti5O12 full-cell

Li₄Ti₅O₁₂ (LTO)/carbon nanotubes (CNTs) composite material is synthesized based on a solid-state method by sand-milling, spray-drying and calcining at 850 ℃ under N₂ flow. The LTO/CNTs samples with 1 wt% and 3 wt% weight ratio of CNTs addition and the pristine LTO sample are prepared. The rate performance and the thermal stability of these samples are investigated based on LiMn₂O₄ (LMO)/LTO full-cell. The results show that theweight ratio of CNTs addition has distinct effect on LTO performances. The composite materials of LTO composited CNTs have better performance at high-rate due to the intercalation enhancement by conductive network of CNTs. At second, the overcharging temperature response of the cell's surface with 1 wt% CNTs addition is the lowest. The particle size distribution is measured and the most uniform particles are obtained with 1 wt% CNTs addition. This trend could explain that the mediumquantity of CNTs is optimal to improve the heat and mass transfer and prevent the problems of crystallite growing interference and aggregation during the calcination process.     

pH值对Bi_2MoO_6晶体形貌和可见光催化性能的影响

以(NH4)6Mo7O24·4H2O和Bi(NO3)3·5H2O为原料,采用普通水热法制备Bi2Mo O6光催化剂,研究p H值对制备该光催化剂的影响。对所制备的系列样品,采用X-射线衍射仪(XRD)、扫描电子显微镜(SEM)、比表面积分析仪、X射线光电子能谱仪(XPS)和紫外-可见漫反射(UV-Vis DRS)进行表征。结果表明:p H值对Bi2Mo O6晶体的物相组成、形貌和光催化性能均有显著影响。p H值为1~7时,所制备的样品为纯相Bi2Mo O6,p H值为9或11时,出现第二相Bi3.64Mo0.36O6.55;随着p H值的升高,形貌依次为纳米棒、纳米片和无规则纳米颗粒。在可见光(λ≥420 nm)照射下,通过光催化降解罗丹明B(Rhodamine B,Rh B),探讨了制备Bi2Mo O6的p H值对其可见光催化活性的影响。当p H=7时,制备的样品光催化效果最好,光照50 min后对初始浓度为5 mg·L-1的罗丹明B溶液的降解率为85%。     

Lead‐Free,Air‐Stable All‐Inorganic Cesium Bismuth Halide Perovskite Nanocrystals

Lead‐based perovskite nanocrystals (NCs) have outstanding optical properties and cheap synthesis conferring them a tremendous potential in the field of optoelectronic devices. However, two critical problems are still unresolved and hindering their commercial applications: one is the fact of being lead‐based and the other is the poor stability. Lead‐free all‐inorganic perovskite Cs₃Bi₂X₉ (X=Cl, Br, I) NCs are synthesized with emission wavelength ranging from 400 to 560 nm synthesized by a facile room temperature reaction. The ligand‐free Cs₃Bi₂Br₉ NCs exhibit blue emission with photoluminescence quantum efficiency (PLQE) about 0.2 %. The PLQE can be increased to 4.5 % when extra surfactant (oleic acid) is added during the synthesis processes. This improvement stems from passivation of the fast trapping process (2–20 ps). Notably, the trap states can also be passivated under humid conditions, and the NCs exhibited high stability towards air exposure exceeding 30 days.     

Ba0.6Sr0.4TiO3/聚偏氟乙烯-聚甲基丙烯酸甲酯复合材料的制备及其介电性能

采用流延热压工艺制备Ba_0.6Sr_0.4TiO₃(BST)/聚偏氟乙烯(PVDF)?聚甲基丙烯酸甲酯(PMMA)复合薄膜,研究了PMMA含量对复合材料微观组织结构和介电性能的影响规律。结果表明,BST相能够均匀分散在聚合物基体中,归因于PMMA与PVDF良好的相容性,2种聚合物之间的界面不分明;随着PMMA含量的增加,复合材料的介电常数先降低后升高,耐击穿强度和介电可调性先增加后减少。PMMA含量(体积分数)为15%的BST/PVDF?PMMA₁₅复合材料的综合性能最佳:介电常数为23.2,介电损耗为0.07,耐击穿强度为1412 kV·cm^-1,在550 kV·cm^-1偏压场下,介电可调性为26.2%。     

粒径可控的纳米铁酸铋的制备及其光催化性能

采用改进的聚丙烯酰胺凝胶法制备了BiFeO3纳米颗粒,利用热重-差热、红外光谱及X射线衍射等手段研究了干凝胶的热分解及BiFeO3的成相过程.结果表明,在600℃煅烧可制备出高纯的BiFeO3纳米颗粒.同时发现,随着双丙烯酰胺含量的增加,所得样品晶粒尺寸逐渐减小,从而制备出平均粒径约52～110nm的系列BiFeO3颗...