Improved coating method for uniform polymer layer in infrared hollow fiber

An improved coating method was proposed in order to form a uniform polymer layer in the fabrication of cyclic olefin polymer-coated silver (COP/Ag) hollow fiber. A COP solution was flowed in a closed loop, in which the silver-coated tube was used as a part of the loop. Owing to the constant flowing speed of the COP solution and the airtight flowing environment, a COP layer was uniformly formed. The hollow fibers attain high performance and deliver multi-wavelength laser light from the infrared to the visible simultaneously. The method was successfully applied to the fabrication of practical hollow fibers with 2 m length for the near and mid-infrared lasers.     

Growth of oxide thin films for optical gas sensor applications

Tungsten trioxide and titanium dioxide thin films were synthesised by pulsed laser deposition. We used for irradiations of oxide targets an UV KrF* (λ = 248 nm, τ_FWHM ≅ 20 ns, ν = 2 Hz) excimer laser source, at 2 J/cm² incident fluence value. The experiments were performed in low oxygen pressure. The (0 0 1) SiO₂ substrates were heated during the thin film deposition process at temperature values within the 300-500 °C range. The structure and crystalline status of the obtained oxide thin films were investigated by high resolution transmission electron microscopy. Our analyses show that the films are composed by nanoparticles with average diameters from a few to a few tens of nm. Moreover, the films deposited at substrate temperatures higher than 300 °C are crystalline. The tungsten trioxide films consist of a mixture of triclinic and monoclinic phases, while the titanium dioxide films structure corresponds to the tetragonal anatase phase. The oxide films average transmittance in the visible-infrared spectral range is higher than 80%, which makes them suitable for sensor applications.     

Structural and electrical characterization of SxSe100−x thin films

Thin films of samples of the glassy S_xSe_100−x system with 0 ≤ x ≤ 7.28 have been prepared by thermal evaporation technique at room temperature (300 K). X-ray investigations show that the structure of pure selenium (Se) does change seriously by the addition of small amount of sulphur S ≤7.28%. The lattice parameters were determined as a function of sulphur content. Results of differential thermal analysis (DTA) of the glassy compositions of the system S_xSe_100−x were discussed. The characteristic temperatures (T_g, T_c and T_m) were evaluated. Dark electrical resistivities, ρ, of S_xSe_100−x thin films with different thicknesses from 100 to 500 nm, were measured in the temperature range from 300 to 423 K. Two distinct linear parts with different activation energies were observed. The variation of electrical resistivity of examined compositions has been discussed as a function of the film thickness, temperature and the sulphur content. The application of Mott model for the phonon assisted hopping of small polarons gave the same two activation energies obtained from the resistivity temperature calculations.     

Matrix assisted pulsed laser evaporation processing of triacetate-pullulan polysaccharide thin films for drug delivery systems

We report the first successful deposition of triacetate-pullulan polysaccharide thin films by matrix assisted pulsed laser evaporation. We used a KrF* excimer laser source (λ = 248 nm, τ ≈ 20 ns) operated at a repetition rate of 10 Hz. We demonstrated by FTIR that our thin films are composed of triacetate-pullulan maintaining its chemical structure and functionality. The dependence on incident laser fluence of the induced surface morphology is analysed.     

Dependence of surface morphology of CVD diamond films on deposition conditions

ＤｅｐｅｎｄｅｎｃｅｏｆｓｕｒｆａｃｅｍｏｒｐｈｏｌｏｇｙｏｆＣＶＤｄｉａｍｏｎｄｆｉｌｍｓｏｎｄｅｐｏｓｉｔｉｏｎｃｏｎｄｉｔｉｏｎｓＹＡＮＧＧｕｏｗｅｉ（Ｄｅｐｔ．ｏｆＰｈｙｓ．，ＸｉａｎｇｔａｎＵｕｉｖｅｒｓｉｔｙ，Ｘｉａｎｇｔａｎ４１１１０５...     

SiH_4－O_2体系LPCVD SiO_2薄膜的工艺及其应用

本文研究了ＳｉＨ４—Ｏ２体系ＬＰＣＶＤＳｉＯ２的工艺及设备。为了得到厚度均匀性好的薄膜，改进了反应气体的进气方式和装片舟的结构，获得了每炉１００片、直径为１００ｍｍ的硅片的膜厚不均匀性≤士５％的结果。     

单层光学薄膜中薄膜－衬底体系的双重干涉效应及其应用

提出了单层光学薄膜中薄膜与衬底反射光之间的双重干涉效应的理论，实验结果证实了理论分析的正确性。双重干涉效应使薄膜－衬底体系的热致反射调制度高达８０％，这一效应可望有极广泛的应用     

钢铁表面锌系磷化膜的研究

本文采用ＳＥＭ和ＴＥＭ等测试手段，研究了四功能处理液不同条件下在钢铁表面上形成锌系磷化膜的形貌，晶体结构；采用ＥＤＳ研究了磷化膜的化学成发，通过实验确定了Ｚｎ／Ｐ值在２．１２～３．２０时，磷化膜具有良好的耐蚀性。     

热丝CVD生长金刚石薄膜喇曼散射研究

本文报道热丝化学气相沉积法（ＨＦＣＶＤ）生长金钢石薄膜的喇曼散射结果。选取多种峰型，对金钢石薄膜喇曼谱（１１０－１８００ｃｍ－１）采用最小二乘法进行非线性拟合，得到最佳拟合模型，其计算得到的拟合曲线怀实验谱图符合得较好。该模型揭示，石墨Ｄ峰（１３５５ｃｍ－１）是金刚石薄膜喇曼谱中不可缺少的一个组份，并且结合石墨Ｄ峰和金刚石喇曼的空间相关线型，可以解释金刚石喇曼区特殊峰形的物理机制，拟合参量的进一步     

电流控制LPE生长In_（1－x）Ga_xAs_yP_（1－Y）

用电流控制液相外延（ＣＣＬＰＥ）方法首次在（１００）ＩｎＰ衬底上成功地生长出Ｉｎ１－ｘＧａｘＡｓｙＰ１－ｙ（０．３０＜ｘ＜０．４７，０．７０＜ｙ＜０．９６）外延层，并对外延层特性进行了详细研究，提出在ＩｎＰ衬底上生长电外延层的机理，推导出生长动力学的理论模型，该模型与上述实验结果十分吻合。