Improvement of corrosion properties of microarc oxidation coating on magnesium alloy by optimizing current density parameters

The microstructure, composition and corrosion performance of oxide coatings formed on AM60B alloy using microarc oxidation techniques at different waveforms of applied current densities were investigated within this study. It is found that the use of optimizing current density waveforms, i.e. decaying freely current density in the later stage and stepped decreasing current density, significantly improved the microstructure of oxide coatings compared with the constant current density mode, which are connected with changes in behaviors of spark discharges on the surface in oxidation process. The optimal waveform of current density is showed to be decaying freely current density in the later stage, which results in sealing the originally formed large micropores. The optimisation of the microstructure results in a significant improvement of the corrosion resistance of oxide coating.     

Characterization of Ti6Al4V implant surface treated by Nd:YAG laser and emery paper for orthopaedic applications

A more noble and biocompatible Ti alloy was achieved at fluence of 140 J cm⁻² where the implant indicated a higher degree of hardness (825HV), higher corrosion resistance (−0.21 V) and highest hydrophilicity (i.e. θ_c = 37°) compared with 70° of the control sample. These values corresponded to 58 and 39 mN m⁻¹ of surface tension respectively. The laser treated samples at 140 J cm⁻² showed higher wettability characteristics than mechanically roughened surface. Cell growth and their spreading condition in a specific area were analyzed by SEM and Image J Program software. Clearly, more cells were attached (1.2 × 10⁵) to and spread (488 μm²) over the surface at 140 J cm⁻² than in any other condition. Pathologically, the treated samples indicated no sign of infection.     

Quantum chemical and RRKM calculations of reactions in the H/S/O system

Quantum chemical calculations at the MRCI/aug-cc-pV5Z level are used to describe the conversions between HSO, HOS, H + SO, S + OH and O + SH on the doublet H/S/O potential energy surface. An RRKM analysis of this multiple-well system was carried out in the temperature range 300-2000 K between 0.1 and 10 atm. At these pressures, the stabilization reaction H + SO → HSO or HOS is at the low pressure limit, and stabilization from S + OH and O + SH was not detected. The reactions S + OH → H + SO and O + SH → H + SO were found to be barrierless and very fast at room temperature (4 × 10¹⁴ and 1.5 × 10¹⁴ cm³ mol⁻¹ s⁻¹, respectively). The reaction channel O + SH → S + OH is two orders of magnitude slower than the more exothermic O + SH → H + SO reaction, although a second pathway involving direct H-abstraction (O + SH → S + OH) on the quartet surface appears as a minor channel at high temperatures.     

ICP-AES快速测定土壤中硫含量

采用ICP-AES研究土壤中硫含量的测定.以王水消解土壤试样,优化全谱型ICP-AES分析条件测定土壤中S的含量,检出限为5.7ng/mL(180.7nm)和8.6ng/mL(182.0nm).测定土壤标准物质中的S含量,测定结果在标称值范围内,连续测定10个平行样其相对标准偏差均小于2%.方法快速、简单、准确.     

Understanding the adsorption of 4H-1,2,4-triazole derivatives on mild steel surface in molar hydrochloric acid

This study examines the use of some 4H-triazole derivatives, namely 3,5-diphenyl-4H-1,2,4-triazole (DHT), 3,5-bis(4-pyridyl)-4H-1,2,4-triazole (4-PHT) and 3,5-bis(4-methyltiophenyl)-4H-1,2,4-triazole (4-MTHT) for corrosion and dissolution protection of mild steel in normal hydrochloric acid solution. The inhibiting efficiency of the different additives is evaluated by means of weight loss and electrochemical techniques such as ac impedance measurements and polarisation curves. The experimental results obtained reveal that 4-MTHT is the best effective inhibitor and the inhibition efficiency is found to be in the following order: 4-MTHT > 4-PHT > DHT. The variation in inhibitive efficiency mainly depends on the type and nature of the substituents present in the inhibitor molecule. Polarisation curves show that theses triazoles are mixed-type inhibitors in 1 M HCl. The inhibition efficiency increases with 4H-triazole derivatives concentration and attains the maximum value of 99.6% in the case of 4-MTHT at 5 × 10⁻⁴ M. The results obtained from weight loss electrochemical studies were in reasonable agreement. The adsorption of 4H-triazole derivatives on the steel surface obeys to the Langmuir isotherm model. The thermodynamic data of adsorption and activation are determined and discussed. The fundamental thermodynamic functions were used to glean important information about the 4H-triazoles inhibitory behaviour. Molecular modeling was used to get better insight, about structural and electronic effects in relation to the inhibition efficiencies.     

Corrosive behavior of chromium carbide-based films formed on steel using a filtered cathodic vacuum arc system

The formation of chromium carbide-based hard-coatings on steels using a 90°-bend filtered cathodic vacuum arc (FCVA) has extensive industrial applications; such coatings are free of macroparticles and exhibit excellent characteristics. In this investigation, a working pressure of C₂H₂/Ar was adopted to synthesize amorphous chromium carbide film (a-C:Cr) and crystalline chromium carbide film (cryst-Cr₃C₂) from a Cr target (99.95%) at 500 °C under a substrate voltage of −50 V. The corrosion behavior of a-C:Cr coated on steel (a-C:Cr/steel) and cryst-Cr₃C₂ coated on steel (cryst-Cr₃C₂/steel) were compared in terms of open-circuit potentials (OCP) and polarization resistance (R_p) in an aerated 3.5 wt% NaCl aqueous solution, as determined by electrochemical impedance spectroscopy (EIS). The XRD results indicated that the transformation of a-C:Cr to cryst-Cr₃C₂ is distinct as the working pressure declines from 1.2 × 10⁻² to 2.9 × 10⁻³ Torr. The OCP of a-C:Cr/steel and cryst-Cr₃C₂/steel resemble each other and both assembly are nobler than uncoated steel. The R_p of the coatings exceeds that of the uncoated steel. The SEM observation and the EIS results demonstrate that the cryst-Cr₃C₂/steel more effectively isolates the defects than dose a-C:Cr/steel.     

Surface status and size influences of nickel nanoparticles on sulfur compound adsorption

Metallic nickel nanoparticles were incorporated on mesoporous silica to remove sulfur compounds in diesel selectively. In the first method, nickel nanoparticles were formed on mesoporous silica SBA-15 by impregnation and subsequent reduction of nickel nitrate. The sulfur adsorption capacity was strongly dependent on the nickel loading and the average nickel particle size. In the second method, nickel nanoparticles were synthesized in solution in the presence of a capping agent and then incorporated in mesoporous silica MCF by sonication. Although these particles maintain their sizes on the MCF surface after heat treatment, capping agent remaining on the Ni particle surface might interfere the adsorption of sulfur compounds.     

Characterization of microarc oxidation coatings formed on AM60B magnesium alloy in silicate and phosphate electrolytes

Microarc oxidation coatings on AM60B magnesium alloy were prepared in silicate and phosphate electrolytes. Structure, composition, mechanical property, tribological, and corrosion resistant characteristics of the coatings was studied by scanning electron microscope (SEM), X-ray diffraction (XRD) and microhardness analyses, and by ball-on-disc friction and potentiodynamic corrosion testing. It is found that the coating produced from the silicate electrolyte is compact and uniform and is mainly composed of MgO and forsterite Mg₂SiO₄ phases, while the one formed in phosphate electrolyte is relatively porous and is mainly composed of MgO phase. The thick coating produced from a silicate electrolyte possesses a high hardness and provides a low wear rate (3.55 × 10⁻⁵ mm³/Nm) but a high friction coefficient against Si₃N₄ ball. A relatively low hardness and friction coefficient while a high wear rate (8.65 × 10⁻⁵ mm³/Nm) is recorded during the testing of the thick coating produced from a phosphate electrolyte. Both of these types of coatings provide effective protection for the corrosion resistance compared with the uncoated magnesium alloy. The coating prepared from the silicate electrolyte demonstrates better corrosion behavior due to the compacter microstructure.     

选择性化学镍/金工艺的应用

本文主要通过对选择性化学镍／金的生产应用，就流程中的二次干膜、退膜、化学镍金、OSP的相关生产控制进行总结。     

Reaction of primary phosphines with elemental sulfur and alkali metal hydroxides (MOH, M = Na, K, Cs): a novel and facile three-component synthesis of trithiophosphonates

Primary phosphines readily react with elemental sulfur and alkali metal hydroxides (MOH, M = Na, K, Cs) in the molar ratio 1:3:2 under mild conditions (70 °C, 0.5 h, ethanol) to afford alkali metal trithiophosphonates in good to high yields (72-90%).