Ni-B和Ni-Ce-B超细非晶态合金的退火晶化及其催化性能

 采用XAFS,XRD和DTA方法研究了Ni－B和Ni－Ce－B超细非晶态合金在退火过程中的结构变化及其结构与催化性能的关系．活性结果表明,在退火温度为623K时,Ni－B和Ni－Ce－B样品的苯加氢催化反应转化率最高,分别为63％和81％,0．3％Ce的掺入提高了Ni－Ce－B的催化活性．DTA结果表明,Ni－B超细非晶态合金在598和653K有两个晶化峰,而Ni－Ce－B样品有548,603,696和801K四个晶化峰．XAFS和XRD结果进一步说明,在573K退火时,Ni－B样品晶化生成晶态Ni3B和纳米晶Ni,此时Ni－Ce－B仅有少量晶态Ni3B生成．在673K退火时,Ni－B样品中的Ni3B开始分解生成晶态Ni,同时纳米晶Ni聚集并形成大颗粒晶态Ni,而Ni－Ce－B样品晶化生成晶态Ni3B和纳米晶Ni．在773K和更高的温度退火处理后,Ni－B样品中Ni的局域环境结构与金属Ni箔基本一致,但Ni－Ce－B样品晶化生成的Ni晶格有较大畸变,同时Ni3B并未分解．说明0．3％的Ce对提高Ni－Ce－B样品的稳定性有显著作用．本文首次报道了Ni－B和Ni－Ce－B超细非晶态合金中苯加氢催化活性中心为纳米晶Ni和类似于金属Ni的Ni－B非晶态合金．     

Double Electric Layer on Liquid Sn-Ga Alloy in Acetonitrile Solutions of Electrolytes

The structure of the double electric layer (DEL) on a liquid dropping Sn-Ga electrode containing 8 at. % of Sn is studied in acetonitrile (AN) solutions of electrolytes. It is shown that the transition from aqueous to AN solutions of electrolytes makes it possible to expand the region of investigation of parameters of DEL on an Sn-Ga electrode from negative charges to a zero charge and to small positive charges. As follows from the obtained data, throughout the entire interval of charges studied, an excess, as compared with an Hg electrode, chemisorption interaction (Sn-Ga)-AN is absent. It is established that the distance of the closest approach of AN dipoles to an ionic core increases upon going from Hg to Sn-Ga to Ga. The Ga, Bi-Ga, and Sn-Ga electrodes, which possess close values of the “electrochemical work function,” are used as an example to show that the metal-solvent chemisorption interaction increases with decreasing distance of the closest approach of its dipoles to the ionic core of the metal. The effect of this factor becomes stronger as the donor number of the solvent increases.     

Structures and electrochemical characteristics of several kinds of alloys

The structures and the electrochemical characteristics of La_0.7−x Ce_xMg_0.3Ni_2.8Co_0.5 (x = 0.1–0.5) alloy, Ti_0.25−x Zr_xV_0.35Cr_0.1Ni_0.3 (x = 0.05–0.15) alloy and AB_3<x<5-type alloy, which are the representative examples of AB₃-type alloy, solid solution alloy and non-AB₅-type alloy, respectively, have been investigated, and the performances of MH-Ni battery in which AB_3<x<5 type alloy is used as the negative electrode material are examined at relatively low temperature.     

加速剂对化学镀镍层组成与结构的影响

加速剂对化学镀镍层组成与结构的影响方景礼，武勇，韩克平，张敏（南京大学应用化学研究所配位化学国家重点实验室南京２１００９３）关键词化学镀镍，Ｎｉ０Ｐ合金，加速剂，硫脲化学镀镍磷合金具有耐蚀性、可焊性、厚度均匀和硬度高等优点，已得到广泛应用。为提高生产...     

人工神经网络X射线荧光光谱法测定钢中酸溶铝

建立了一种人工神经网络-X射线荧光光谱法测定钢中酸溶铝的方法，用X射线荧光光谱法测定低合金钢中总铝值，应用所建立的ANN-BP网络模型，输入总铝含量直接预测出酸溶铝含量。同时使用改进的BP算法，避免了神经网络学习中可能产生的麻痹现象。该方法用于钢中酸溶铝的测定，结果满意。     

Determination of Labile Iron at Low nmol L−1 Levels in Estuarine and Coastal Waters by Anodic Stripping Voltammetry

A new method is presented for the determination of electrochemically labile iron in estuarine and coastal seawater. The method is based on differential pulse anodic stripping voltammetry (DPASV) at a rotating silver‐alloy disk electrode. The voltammetric parameters include a plating potential of ?1.5 V and an activation potential of ?5 V for 10s; the seawater is at the original sample pH. The main finding is the presence of a peak for low nmol L^?1 levels of iron at ?0.55 V ascribed to elemental iron deposited on the bare silver alloy electrode. The peak increased linearly with the iron concentration between <1 and 14 nmol L^?1 using a 900 s plating time. At higher concentrations an additional iron peak appeared at ?0.7 V which was also found to increase linearly with the iron concentration but at a higher concentration range from ca. 15 to 90 nmol L^?1 using a 300 s plating time. The second peak was ascribed to iron deposited on iron. Additions of chelating agents (EDTA and a siderophore) to seawater caused the iron peak to be masked indicating that this method is suitable for iron speciation as only the electrochemically labile fraction is determined. The detection limit was 0.3 nmol L^?1 using a 900 s plating time. The method was used to determine iron in the range of 5 to 50 nmol L^?1 in samples from the Mersey estuary near Liverpool and its potential use for in situ monitoring was demonstrated by using it to monitor labile iron (at 2–3 nmol L^?1) over a period of 4 days at 1 h intervals in coastal waters in the Trondheim fjord, Norway.     

氢化物发生石墨炉原子吸收光谱法直接测定高温镍基合金中的硒

在６ｍｏｌ／Ｌ盐酸介质和０．１％ＫＢＨ４条件下，不但能有效地发生硒的氢化物，而且５ｍｇ／ｍｌＮｉ和３ｍｇ／ｍｌＦｅ都不干扰硒的测定。利用涂钯石墨；管作为氢化物的原子化器，直接测定了高温镍基合金中的硒，特征质量为４０ｐｇ，相对标准偏差在６．１％以内，回收率在９７％－１１０％之间。     

纳米多孔双金属氧化物在镍钛合金纤维上的原位生长及其对多环芳烃的选择性固相微萃取

采用阳极氧化法在镍钛合金(NiTi)纤维上原位生长了双金属氧化物纳米孔(NiTiONPs)涂层,通过扫描电镜(SEM)和能谱(EDS)考察了电解质组成和电压对形貌的影响。将NiTiONPs涂层的NiTi纤维与高效液相色谱-紫外检测器联用,研究了4种典型芳香分析物的萃取性能。结果表明,富含TiO2的NiTiONPs涂层对多环芳烃(PAHs)具有良好的萃取效率,尤其对苯并[a]芘的萃取选择性优于市售聚二甲基硅氧烷纤维和聚丙烯酸酯纤维。在优化条件下,PAHs的线性范围为0.05~200μg/L,相关系数均大于0.999,检出限为0.012~0.134μg/L。对单支纤维日内和日间分析的相对标准偏差(RSDs)分别为4.0%~5.5%和6.0%~6.8%,使用分批组装的5支纤维分析的RSDs为6.4%~7.6%。实际水样分析的加标回收率为84.5%~111.5%。所制备NiTi纤维至少可重复使用250次以上,重现性好。     

压力、温度和晶粒尺寸对Fe-N合金的合成及结构的影响

在 1× 1 0 - 3 Pa～ 4 GPa的压力和 5 80～ 930 K温度范围内 ,利用高压技术并结合机械球磨 ,研究了压力、温度和晶粒尺寸对α-Fe与非晶 BN的固态反应的影响 .发现高压和晶粒细化可以极大地促进α-Fe和非晶 BN的固态反应过程 ,α-Fe与非晶 BN发生固态反应的临界晶粒尺寸约 8nm.压力和温度对反应产物及其晶体结构有明显影响 .2 GPa和 80 0 K时 ,反应产物为具有正交结构的 Fe-N新相 ;在 3～ 4 GPa和 690～80 0 K时 ,可形成单一ε-Fex N合金相 ;而在 4 GPa和 930 K以上 ,反应产物由 Fe-N合金相转变为 Fe3B相     

植入用Co—Cr—Mo合金与Ti—6Al—4V合金的电偶腐蚀研究

组件式设计常被用地人工髋关节，钴络钼合金（Ｃｏ－Ｃｒ－Ｍｏ）与钛合金（Ｔｉ－６Ａｌ－４Ｖ）的压配最常用，本文应用电化学方法研究了静态条件下两种合金的电偶腐蚀行为，浸泡实验表明，钴络钼合金为阳极，但电偶电流与其维钝电流相近，并无明显加速度腐蚀效应，钛合金为阴极，受到保护，失重及金相观察结果显示，在４５天的浸泡实验周期内，未发现腐蚀痕迹，混合电位理论和电位处于两种合金的钝化电位区，电偶电流为合金的维钝