Adsorption of polyallylamine to lignocellulosic fibres: effect of adsorption conditions on localisation of adsorbed polyelectrolyte and mechanical properties of resulting paper sheets

Cationic polyallylamine (PAH), was adsorbed onto lignocellulosic fibres, and a fluorescent label on the polyelectrolyte enabled its location to be shown by confocal fluorescence microscopy. The adsorption time and ionic strength were varied to study their effect on the localisation of the adsorbed PAH. The microscopy showed that a long adsorption time, 24 h, and a high ionic strength, 10⁻¹ M NaCl + 5 × 10⁻³ M NaHCO₃ or higher, resulted in the adsorption of polyallylamine throughout the fibre walls. Shorter adsorption times and/or lower ionic strength resulted in adsorption only to the fibre exterior. By preparing sheets from fibres with polyelectrolyte adsorbed either to the exterior parts or into the fibre cell wall and testing their mechanical behaviour, a link was established between the localisation of adsorbed polyelectrolyte and the mechanical properties. Adsorption to the fibre exterior led to an increase in tensile strength and strain at break. The creep deformation at 90%RH was also slightly reduced by the adsorption of low molecular weight PAH (15 kDa). When polyallylamine was adsorbed throughout the wall of the lignocellulosic fibres, the mechanical properties were not however improved and the creep deformation at 90%RH actually increased somewhat.     

Viscoelastic properties of durum wheat and common wheat dough of different strengths

Linear viscoelastic properties (LVP) were determined for five durum wheat doughs and five common wheat doughs (representing four different classes of Canadian common wheat) of different strength using creep testing. A creep time of 10,000 s was sufficient to reach a state of steady state flow for all of the doughs. Creep compliances were analyzed in terms of a Burgers model. For the durum doughs, the entire elastic compliance curve was shifted to higher values as the strength of the dough (as measured by extensigraph) decreased, while the steady state viscosity increased with strength. For common wheat doughs, the elastic compliance curves were steeper and the steady state viscosities were lower than for durum doughs of comparable extensigraph strength. The retardation strengths associated with a maximum in the retardation spectra were lower for the stronger durum doughs than for common wheat doughs of comparable strength. Differences in the LVP between durum and common wheat doughs of similar extensigraph strength were interpreted in the context of physical gels with crosslinks and entanglements, whose contributions to material properties are difficult to distinguish in short-time creep or dynamic measurements. The increased extensibility of common wheat doughs relative to durum doughs of comparable extensigraph strength was attributed to a higher molecular weight fraction in the polypeptide chains, similar in some respects to end-linked bimodal polymer networks. The idea of considering these doughs as physical gels was supported by their stress relaxation behavior. Received: 6 February 2000 Accepted: 22 August 2000     

Temperature-dependent ratcheting of PTFE gaskets under cyclic compressive loads with small stress amplitude

Uniaxial stress-controlled ratcheting experiments on PTFE gaskets under cyclic compressive loads with small stress amplitude were performed. The effect of temperature on the deformation behavior was considered. Results showed that the compressive modulus decreases rapidly when the temperature increases from 100 °C to 200 °C. Compressive ratcheting deformation with cycles increase significantly with the increases of temperature. The ratcheting deformations at 100 °C, 150 °C and 200 °C are nearly two, three and five times that at room temperature, respectively. Most of ratcheting deformation mainly occurs during the first 20 cycles because the subsequent ratcheting rate and strain range are small and much less than those in the previous cycles. The accumulated deformation under cyclic loads with small stress amplitude is relatively approach to the static compressive creep with the same peak stress. Therefore, the accumulated deformation with time of PTFE gaskets obtained by cyclic compression with small stress amplitude can be estimated by the corresponding static creep deformation with good accuracy under the approximate stress rate and the same temperature, especially at room temperature.     

Creep life evaluation of aluminum conductor composite core utilized in high voltage electric transmission

The creep life of aluminum conductor composite core (ACCC) utilized in high voltage electric transmission was investigated using an experimental method based on the equivalence relationship. First, the time-temperature-stress equivalence relationship was developed using the time-temperature and the time-stress equivalence relationships. Then, tensile creep experiments were conducted under different temperatures and different stress levels to obtain the strain-time curves of the ACCC. Finally, the creep strain master curve was obtained using the experimental data based on the time-temperature-stress equivalence relationship, allowing prediction of ACCC creep life. The results will play an important role in evaluation of the long-term characteristics of the ACCC for engineering applications.     

Analysis of nickel cylindrical bump insertion into aluminium thin film for flip chip applications

This paper investigates the mechanical deformation and the electrical contact resistance of an electroplated Ni micro-cylinder called micro-insert inserted in an Al thin film. A modified nanoindentation apparatus is used to perform the experiments with 6 μm, 8.5 μm and 12.5 μm diameters micro-inserts having the same 5 μm height. Mechanical deformation of Ni micro-insert and Al film is described at different maximum loads corresponding to an equivalent stress of 0.8 GPa, 1.6 GPa and 3.2 GPa. At equivalent stress less than 1.6 GPa, Ni micro-insert exhibits an elastic deformation while at 3.2 GPa it presents an elastic-plastic deformation with a large amount of compression and penetration into micro-insert foundation. Visco-plastic deformation of Al film is noticed during hold at all maximum loads. Beside, Al creep parameters are extracted using a combined Maxwell/Kelvin-Voigt phenomenological model. Mechanical results are coupled to electrical contact resistance measurement.     

Viscoplastic behaviour of a medium density polyethylene (MDPE): Constitutive equations based on double nonlinear deformation model

The viscoplastic behaviour of a medium density ethylene–butene copolymer (MDPE) is investigated by using samples cut out from thick-walled MDPE pipe. Extensive experimental work has been performed to characterise the nonlinear time-dependent response of such semi-crystalline thermoplastic material. Tests were carried out at 60 °C, on smooth tensile, full axisymmetrically notched creep tensile (FNCT) and double edge notched tensile (DENT) specimens.     

An intermediate model method for obtaining a discrete relaxation spectrum from creep data

A convenient method is described for obtaining a discrete stress relaxation spectrum from linear viscoelastic creep data by means of a three-stage process. In stage one, a discrete retardation spectrum is fitted to the creep data using a least squares procedure, subject to the constraint that the discrete spectrum must be a specified order of polynomial function of the retardation time. In stage two, the resulting generalised Voigt model is solved numerically for an imposed step in strain, to determine the stress relaxation modulus function of time. In stage three, a discrete relaxation spectrum is fitted to the calculated stress relaxation modulus function. Although three stages are involved instead of the usual two, the procedure has been found to have certain practical advantages. These advantages make it suitable for the generation of relaxation spectra needed in viscoelastic stress analyses of solids, for example by the finite element method. In order to illustrate the proposed procedure it is applied to both artificial data and experimental creep data for poly(methyl methacrylate) at 70°C and at the glass transition.     

Identification of viscoelastic properties by means of nanoindentation taking the real tip geometry into account

Motivated by recent progress in viscoelastic indentation analysis, the identification of viscoelastic properties from nanoindentation test data taking the real tip geometry into account is presented in this paper. Based on the elastic solution of the indentation problem, the corresponding viscoelastic solution is obtained by the application of the method of functional equations. This general solution, which accounts for the real geometric properties of the indenter tip, is specialized for the case of a trapezoidal load history, commonly employed in nanoindentation testing. Three deviatoric creep models, the single dash-pot, the Maxwell, and the three-parameter model are considered. The so-obtained expressions allow us to determine viscoelastic model parameters via back calculation from the measured load–penetration history. The presented approach is illustrated by the identification of short-term viscoelastic properties of bitumen. Hereby, the influence of loading rate, maximum load, and temperature on the model parameters is investigated.     

Creep crack growth on spent fuel zircaloy cladding in interim storage

The effect of creep failure mechanisms on the creep crack growth is examined on spent fuel Zircaloy cladding in interim storage. Based on the creep fracture mechanics parameter C^* and the strain energy density criteria, the relationship between the creep crack growth rate and the fracture mechanics parameter C^* is established theoretically. The effects of initial crack lengths and storage temperature profiles on cladding failure are discussed in detail. The results show that the initial crack length and the storage temperature profile play an important role in the interim dry storage. When the storage temperature remains at a constant temperature of 400 °C, it will be safe for the cladding which stores in the interim dry storage. The results presented in this study provide a reliable cladding integrity evaluation for spent fuel in the interim dry storage.