锂离子电池负极合金CoSn和Cu-Sn的制备与表征

CoSn alloy and Cu-Sn samples were synthesized by H₂-reduction following solid-state reaction between Co(Ⅱ)， Cu(Ⅱ)， Sn(Ⅳ) and NaOH at ambient temperature. The samples were characterized by XRD， SEM. The results showed that CoSn alloy (80～200nm) is globe-shaped， ultrafine hexagonal material， and Cu-Sn alloy powder consists of two phases， i.e. Cu₆Sn₅ and Cu₃Sn. Cu-Sn powder has spherical morphology and the particle size is estimated to be 60～70nm. The electrochemical performances of CoSn alloy and Cu-Sn powder were studied using lithium-ions model cell Li/LiPF₆ (EC+DMC)/CoSn (or Cu-Sn). It was demonstrated the reversible discharge capacities for 10 cycles keep above 280mAh·g^-1 for nanophase Cu-Sn， and 60mAh·g^-1 for CoSn alloy. Differ-ential capacity plots showed that the reaction mechanisms of Cu-Sn with lithium were reversible.     

一种新型锂离子电池用聚合物电解质复合膜的制备和性能表征

阐述了一种新型锂离子电池用PVDF-HFP(聚偏氟乙烯-六氟丙烯聚合物树脂)基聚合物电解质复合膜的制备过程. 对复合膜中使用的无机TiO2纳米颗粒进行固体超强酸化处理, 并进行颗粒表面酸强度H0测试、XRD晶体结构分析以及复合膜的电解液吸附率测试和电化学阻抗谱测试. 采用PE无纺布支撑体作为增强材料, 以浸涂方法制备复合膜,并进一步组装为锂离子电池, 性能测试表明该电池具有良好的电化学性能.     

纳米级锰酸锂阴极材料的制备及其电化学性能研究

1．引言 锰酸锂阴极材料具有制备工艺简单、价格低廉、环保、安全性能较好等优点，已被国内大多数锂离子电池制造企业作为手机电池的阴极材料。但锰酸锂在高倍率电池中的研究和应用还较少，其原因之一是因为常用的高温固相法合成的锰酸锂产品粒径较大，在几个微米左右，锂离子在其颗粒内部嵌入脱嵌时迁移路径较长，导致其大倍率充，放电性能不佳。     

锂离子筛的制备及其交换性能研究

用浓度为0.5mol/L的盐酸对高温固相合成的前体LiMn2O4进行酸洗脱锂,制得锂离子筛HMn2O4,并在不同pH值和温度下进行了Li 交换性能的研究,同时运用XRD和TEM进行了相应表征。结果表明,锂离子筛吸附交换前后晶体结构只发生了细微变化,但都仍为尖晶石型结构;交换反应在前10min速率最快,约20min就趋于平衡;Li 交换总量随pH值增大而升高,其中pH=7时交换容量为18.5526mg/g;Li 交换量和交换选择性随温度的升高而显著增强。     

锂离子电池用多孔硅/石墨/碳复合负极材料的研究

在两步高能球磨和酸蚀条件下制得了多孔硅/石墨复合材料，并对其进行碳包覆制成多孔硅/石墨/碳复合材料。通过TEM，SEM等测试手段研究了多孔硅材料的结构。作为锂离子电池负极材料，电化学测试结果表明多孔硅/石墨/碳复合材料相比纳米硅/石墨/碳复合材料有更好的循环稳定性。同时，改变复合体配比、热解碳前驱物、粘结剂种类和用量也会对材料的电化学性能产生较大的影响。其中使用质量分数为10％的LA132粘结剂的电极200次循环以后充电容量保持在649.9 mAh·g^-1，几乎没有衰减。良好的电化学性能主要归因于主活性体-多孔硅颗粒中的纳米孔隙很好地抑制了嵌锂过程中自身的体积膨胀，而且亚微米石墨颗粒和碳的复合也减轻了电极材料的体积效应并改善了其导电性。     

Nb 掺杂LiFePO4/C 的一步固相合成及电化学性能

用固相法一步合成了Nb掺杂的LiFePO4/C复合材料, 研究了Nb掺杂量对材料电化学性能的影响. 结果表明, Nb掺杂后LiFePO4/C复合材料的电化学性能明显提高. 在0.5C、1C和2C充放电倍率下, 名义成分为Li0.96Nb0.008FePO4/C正极材料的比容量分别为161、148和132 mAh•g−1, 已达到实用化水平. 阻抗谱和循环伏安特性测试显示, Nb掺杂有效地降低了复合材料电极的阻抗和极化, 说明Nb掺杂的主要作用是提高了LiFePO4的电子电导率.     

添加剂对SiO电性能的影响及其机理分析

SiO_x/CoO and SiO/Li₂CO₃ composite materials were prepared by mechanical ball-milling. The structures of the obtained materials were characterized by X-ray diffraction (XRD). And scanning electron microscopes (SEM) of three samples after 20 cycles were also given. In addition， the electrochemical performances of three materials with galvanostatic charge-discharge cycling were investigated. The results show that the composite samples have larger initial reversible capacities and better cycle performance than pure SiO. Also，a schematic diagram showing the buffer effects of Li₂CO₃ addition and the mechanism of improving electrochemical performance by adding Li₂CO₃ are suggested.     

一维棒状ZnO的制备及电化学嵌锂性能研究

目前,商业化锂离子电池一般采用石墨作为负极材料,因其电位与金属锂电极的电位很接近,所以当电池反复循环和过充时,石墨表面易析出金属锂,会因形成枝晶而短路。在温度过高时还容易引起热失控。同时,锂离子电池的容量在很大程度上取决于负极的锂嵌入量,而且石墨材料容量相对较低     

锂离子电池高比容量FeSn2-C复合负极材料的合成与性能

Sn基合金负极材料具有高达990 mAh·g^-1的理论比容量,但其也存在因脱嵌锂过程发生巨大的体积变化而导致循环性能较差的问题. 本文以Sn、Fe、石墨为原料利用简易的高能球磨法成功制备了具有核壳结构的FeSn₂-C复合物,系统研究了球磨时间、FeSn₂相含量对材料物相结构及电化学性能的影响,并分析了电极的失效机理. 研究表明,球磨时间的增加有利于FeSn₂金属间化合物相的形成及材料颗粒的细化,进而有利于材料比容量的增加及循环性能的提升;FeSn₂相含量的增加能够提高FeSn₂-C材料的比容量,但会降低FeSn₂-C电极的循环稳定性. 经工艺优化及组分调节,球磨24 h合成的Sn₂₀Fe₁₀C₇₀材料具有最优的电化学性能,材料的比容量在540 mAh·g^-1左右,并能稳定循环100次,是一种非常有发展前途的锂离子电池高比容量负极材料.     

铜掺杂五氧化二钒的制备及电化学性质

采用沉淀法于300 和600 ℃制备了结晶状的Cu0.04V2O5材料. 扫描电镜显示, 300 ℃时制备的样品具有多孔特征, 而600 ℃时制备的样品具有很高的结晶度. X射线研究表明, 少量铜掺杂不会改变V2O5的正交晶体结构. 红外光谱研究表明, 300 ℃时制备的Cu0.04V2O5样品含有少量水. 热失重分析确定了样品中所含水分是以吸附水的形式存在, 1 mol材料分子吸附水的摩尔数约为0.18 mol. 铜掺杂显著改善了V2O5的结构稳定性, 进而提高了材料的充放电循环性能. 于600 ℃制备的样品在C/5.6倍率下具有160 mAh·g-1的可逆比容量, 但提高放电倍率明显降低了材料的循环性能. 于300 ℃制备的样品在C/5.6倍率时的循环性能不如600 ℃样品, 但该材料在C/1.9倍率时仍具有100 mAh·g-1左右的可逆比容量. 两种材料在电化学性能上的差异与材料的微结构有关. 低温样品在较高放电倍率时良好的循环性能得益于其多孔的微结构, 而高温样品由于其较高的结晶度而表现出优异的低倍率充放电性能.