Improvement in a-plane GaN crystalline quality using wet etching method

Nonpolar （1120） GaN films are grown on the etched a-plane GaN substrates via metalorganic vapor phase epitaxy. High-resolution X-ray diffraction analysis shows great decreases in the full width at half maximum of the samples grown on etched substrates compared with those of the sample without etching, both on-axis and off-axis, indicating the reduced dislocation densities and improved crystalline quality of these samples. The spatial mapping of the E2 （high） phonon mode demonstrates the smaller line width with a black background in the wing region, which testifies the reduced dislocation densities and enhanced crystalline quality of the epitaxial lateral overgrowth areas. Raman scattering spectra of the E2 （high） peaks exhibit in-plane compressive stress for all the overgrowth samples, and the E2 （high） peaks of samples grown on etched substrates shift toward the lower frequency range, indicating the relaxations of in-plane stress in these GaN films. Furthermore, room temperature photoluminescence measurement demonstrates a significant decrease in the yellow-band emission intensity of a-plane GaN grown on etched templates, which also illustrates the better optical properties of these samples.     

Solar-blind ultraviolet band-pass filter based on metal–dielectric multilayer structures

Solar-blind ultraviolet （UV） band-pass filter has significant value in many scientific, commercial, and military appli- cations, in which the detection of weak UV signal against a strong background of solar radiation is required. In this work, a solar-blind filter is designed based on the concept of ＂transparent metal＂. The filter consisting of Al/SiO2 multilayers could exhibit a high transmission in the solar-blind wavelength region and a wide stopband extending from near-ultraviolet to infrared wavelength range. The central wavelength, bandwidth, Q factor, and rejection ratio of the passband are numerically studied as a function of individual layer thickness and multilayer period.     

基于腔面非注入区的半导体激光器的热特性分析

利用Ansys有限元分析软件模拟了宽条形激光器腔面在不同生热率条件下对有源区温度的影响,并对带有腔面非注入区的激光器结构进行了热分析,比较了不同长度的非注入区结构的器件的温度特性。腔面的温升对器件可靠性影响极大,计算结果表明随着非注入区宽度的增加,芯片前腔面有源区的温度明显降低。结果为采用非注入区结构提高COD阈值功率提供了设计参考。     

Adjustable surface plasmon resonance with Au,Ag, and Ag@Au core-shell nanoparticles

We report an experimental study on the synthesis of metal nanoparticles （NPs） with adjustable optical density based on surface plasmon resonance （SPR）. Metal NPs prepared by laser ablation in liquid method and the effect of laser parameters on the size, distribution, wavelength of SPR of Ag, Au, and mixture of Ag-Au, and Ag core/Au shell NPs are investigated. Our results show that the adjustable SPR band can be achieved in each class of NPs which is suitable for adjustable optical window applications.     

新型半导体制冷肾脏灌注保存箱的实验研究

低温灌注保存箱可保证移植肾在摘离人体后的质量,而目前存在的保存箱内温度不均、设备运行时间短等不足会影响移植肾的保存质量。针对这些不足,通过加装一套小型半导体制冷系统,该保存箱可在两小时内将箱内仿离体肾脏降至4℃,并稳定运行时长达35小时。实验结果表明,新型保存箱提升了使用性能,离体肾脏保存温度得到保障,病人术后生存质量和存活率也得以提高。     

管式炉中半导体激光器巴条Au80Sn20焊料封装研究

为了提高半导体激光器的封装质量和效率,引入管式炉利用夹具进行批量封装。由于封装质量的好坏直接影响半导体激光器的输出特性和使用寿命,利用MOCVD生长808 nm芯片,重点分析了管式炉温度和封装时间对半导体激光器巴条双面金锡封装质量的影响。利用X射线检测、结电压、光电特性参数和smile效应测试手段,确定了管式炉封装半导体激光器巴条的最优封装条件,为以后的产业化提供了指导意义。     

石墨片作辅助热沉的高功率半导体激光器热传导特性

为使边发射高功率单管半导体激光器有源区温度降低,增加封装结构的散热性能,降低器件封装成本,提出一种采用高热导率的石墨片作为辅助热沉的高功率半导体激光器封装结构。利用有限元分析研究了采用石墨片作辅助热沉后,封装器件的工作热阻更低,散热效果更好。研究分析过渡热沉铜钨合金与辅助热沉石墨的宽度尺寸变化对半导体激光器有源区温度的影响。新型封装结构与使用铜钨合金作为过渡热沉的传统结构相比,有源区结温降低4.5 K,热阻降低0.45 K/W。通过计算可知,激光器的最大输出功率为20.6 W。在研究结果的指导下,确定铜钨合金与石墨的结构尺寸,以达到最好的散热效果。     

FeCl3催化2-(1-丙炔基)-2’-乙酰基联苯环化反应的机理研究

采用密度泛函理论的B3LYP方法研究了2-(1-丙炔基)-2’-乙酰基联苯分子内环化生成菲衍生物的反应机理。结果表明,该反应在无催化剂和FeCl3催化下均能通过四元环和八元环路径生成产物,其相应的决速步骤分别为四元环和八元环的生成过程。在无催化剂时,四元环路径和八元环路径的决速步骤的能垒相差仅6.8kJ·mol-1,两条路径为竞争反应。在FeCl3催化下,四元环路径决速步骤的能垒为137.52 kJ·mol-1,比八元环路径的低57.4 kJ·mol-1,为优势反应路径。该能垒比没有催化剂时低114.23 kJ·mol-1,表明FeCl3对于该反应具有强的催化作用,能够有效地提高反应速率,使反应在温和的条件下进行。     

机械抛光铜金属表面对罗丹明的荧光增强效应

应用激光光谱学方法,研究了铜表面Rh6G分子的荧光增强效应对于金属衬底表面所形成的氧化层的依赖关系,探索了由于空气氧化而形成的氧化层在表面荧光增强效应中的重要意义和作用机理.实验采用罗丹明6G荧光探针分子,在532 nm连续光激发下,研究机械抛光铜金属衬底在经历不同氧化时间,对吸附其表面的Rh6G分子的荧光增强效果.研究结果表明,适当控制金属样品表面的氧化时间,金属铜表面对若丹明分子的荧光发射表现出猝灭和增强效应.金属氧化层起到了隔离荧光分子与金属表面的作用,减弱了由于激发态荧光分子向金属转移非辐射能量和在金属表面诱导反向偶极子而产生的荧光猝灭效应,从而提高了纯金属铜表面荧光增强辐射行为.因此在微纳金属衬底的荧光增强效应研究中,采用适当的实验手段,精确控制隔离层间距,是表面增强光谱获取的重要途径之一.     

2μm波段全光纤保偏被动锁模掺铥光纤激光器

报道了2μm波段的全光纤保偏锁模掺铥光纤激光器,通过在法布里-珀罗(F-P)腔内加入半导体可饱和吸收镜做为被动锁模器件,采用主振-放大构型,获得了最高输出平均功率为1.08W,重复频率为10.24MHz,脉冲宽度为15.24ps,中心波长为2054.68nm,光谱宽度约为0.3nm的2μm线偏振激光脉冲输出,激光脉冲的消光比为24.17dB。