针对纳米复相永磁材料发展中存在的问题, 阐述了交换耦合作用及其对微观结构的要求.在微观结构的优化方面提出了一些思路, 并介绍了成分优化和制备工艺优化(熔炼、快淬及晶化)等实现途径, 以更好地发挥该材料潜在的高性能.     

Chemical Liquid Phase Deposition of Thin Aluminum Oxide Films

Introduction Inorganic oxide films have attracted a lot of interest in the last several decades. Among them, silicon dioxide films are widely used in modern microelectronics, optics and mechanics. This material has been grown by various methods including thermal oxidation, chemical vapor phase deposition, plasma-enhanced chemical vapor phase deposition, and so on.1,2 Recently, Nagayama et al.3 have reported that SiO2 thin films could be produced by a new chemical method of liquid phase depos…     

用X-射线衍射法测定聚对苯二甲酸乙二醇酯/聚对苯二甲酸丁二醇酯共混体系的结晶度

Based on Hermans and Weidinger postulate that the crystalline fraction is proportional to crystalline intensity Ic and that the amorphous fraction is proportional to amorphous intensity Ia, it is. Suggseteet that for PBT/PET blends we assume that the intensity at 18. 2° is completely originated from amorphous scattering. The separation between the peaks at 17. 2° and 20. 8° is 3. 6°m, which is regarded as large enough to justify this assumption. Thus , it is possible to draw an acceptable demaraction line between the crystalline and amorphous scattering. The degree of crystallinity Xc is given by X_c-I_c/(I_c+KI_a),coefficient K is available by the values of Ic plotted against the values of Ia.For PBT/PET blends,we obtain that K is 0.95 and that correlation coefficient is 0.92 According to the method revieved above,we investi-gated the crystallinity of PBT/PET blends prepared by different ways.     

PEO／PBHE共混体系X射线散射研究

在聚环氧乙烷(PEO)/聚双酚A羟基醚(PBHE)共混体系中PEO是一个强质子受体,而PBHE是一个强质子给体,两者极易形成氢键,十分有利于形成互容对。笔者研究了PEO/PBHE共混体系的相容性,等温及非等温结晶动力学,本文根据Vonk提出的一维电子密度相关函数,分析了PEO/PBHE的SAXS现象,求得了共混体系的结晶度,片晶层厚度,过渡层厚度及长周期等结构参数。     

醋酸乙烯酯基桥连铁硫配合物(σ,π-μ-CH3CO2C=CH2)(μ-RS)Fe2CO)6的制备及结构鉴定

乙酰氯同Fe_3(CO)_(12),RSH,Et_3N所形成的盐[(μ-CO)(μ-RS)Fe_2(CO)_6]Et_3NH相作用,生成一类含醋酸乙烯酯基配体的桥连铁硫配合物(σ,π-μ-CH_3CO_2C=CH_2(μ-RS)Fe_2(CO)_6[R=Et,tert-Bu,Ph)。除用碳氢分析,IR,~1HNMR及X衍射技术表征这类配合物的结构和构象外,还对形成此类产物的过程进行了初步讨论。R=Ph配合物单晶的空间群为PI,晶胞参数a=7.087(3),b=8.824(2),c=15.740(3),α=76.20(1),β=88.15(2),γ=86.28(2)°,D_x=1.65g·cm~(-3),Z=2。醋酸乙烯酯基配体中带有醋酸根的硫与一个铁原子发生σ相互作用,而碳-碳双键与另一个铁原子则发生π相互作用。Fe—Fe键长为2.553(1))苯基与硫桥原子以e键相连。     

Crystal Structures and Magnetic Studies of Naphthalene Derivatives Containing Nitronly Nitroxides

Crystal structures of new nitronyl nitroxide derivatives 1, 2 and 3 were determined with X‐ray diffraction analysis: 1, monoclinic, C₂/c, a = 1.2404(5) nm, b = 0.9730(5) um, c = 2.7049(10) ran, β = 98.189(15)°, V = 3.2315(24) nm³, Z = 8; 2, or‐thorhombic, Pbca, a = 0.61262(2) nm, b = 1.11426(6) nm, c = 2.30543(13) nm, V = 1.57373(13) nm³, Z = 4; 3, monoclinic, P2(1)/n, a=0.64253(4) nm, b=2.55003(17) nm, c = 1.15497(6) nm, β = 95.000(3)°, V = 1.8852(2) nm³, Z = 4. Their magnetic properties were measured with SQUID and analyzed based on their crystal structures with simple singlet‐triplet, modified one dimensional antiferromagnetic chain and modified singlet‐triplet models respectively: 1, J/k_b= ?2.5 K; 2, J/k_b = 7.8 K, θ = 2.8 K; 3, J/k_b = ?0.96 K, θ = 0.21 K.     

氧化锰团簇粒子在有序多孔氧化锆孔道中的组装及其特殊性能研究

利用醇溶液浸渍法及后续的热处理工艺成功实现了氧化锰团簇粒子在有序多孔氧化锆孔道中的组装，借助XRD，TEM，UV-vis，EPR以及O~2-TPD等分析手段进行样品结构表征及性能分析。研究表明，氧化锰团簇粒子能比较均匀地分散于规则的孔道中；团簇粒子的生长随着热处理温度的提高受到孔道大小的限制；孔道中的氧化锰团簇粒子能显示出与较大尺寸氧化锰粒子完全不同的强顺磁信号，并且还具有优异的表面氧吸附特性。     

三苯基锡硫代苯甲酸酯的合成、性质和晶体结构

用三苯基氯化锡与硫代苯甲酸在三乙胺存在下反应，合成了三苯基锡硫代苯甲 酸酯，并进行了红外光谱及核磁共振氢谱表征。X射线单晶衍射表明，化合物属正 交晶系，空间群P2_12_12_1，晶胞参数：a = 0.8306(3) nm, b = 1.6906(5) nm, c = 3.1459(10)) nm, V = 4.417(2) nm~3, Z = 8, D_c = 1.465 g/cm~3, R_1 = 0.0472, wR_2 = 0.1012。该化合物的晶体是由孤立的分子所组成，四配位的锡 原子呈畸变的四面体构型，配体羧基上的氧原子和锡原子之间存在弱的配位作用。     

Ni-B和Ni-Ce-B超细非晶态合金的退火晶化及其催化性能

 采用XAFS,XRD和DTA方法研究了Ni－B和Ni－Ce－B超细非晶态合金在退火过程中的结构变化及其结构与催化性能的关系．活性结果表明,在退火温度为623K时,Ni－B和Ni－Ce－B样品的苯加氢催化反应转化率最高,分别为63％和81％,0．3％Ce的掺入提高了Ni－Ce－B的催化活性．DTA结果表明,Ni－B超细非晶态合金在598和653K有两个晶化峰,而Ni－Ce－B样品有548,603,696和801K四个晶化峰．XAFS和XRD结果进一步说明,在573K退火时,Ni－B样品晶化生成晶态Ni3B和纳米晶Ni,此时Ni－Ce－B仅有少量晶态Ni3B生成．在673K退火时,Ni－B样品中的Ni3B开始分解生成晶态Ni,同时纳米晶Ni聚集并形成大颗粒晶态Ni,而Ni－Ce－B样品晶化生成晶态Ni3B和纳米晶Ni．在773K和更高的温度退火处理后,Ni－B样品中Ni的局域环境结构与金属Ni箔基本一致,但Ni－Ce－B样品晶化生成的Ni晶格有较大畸变,同时Ni3B并未分解．说明0．3％的Ce对提高Ni－Ce－B样品的稳定性有显著作用．本文首次报道了Ni－B和Ni－Ce－B超细非晶态合金中苯加氢催化活性中心为纳米晶Ni和类似于金属Ni的Ni－B非晶态合金．     

The Adsorption of NOx on Magnesium Aluminium Hydrotalcite

Magnesium aluminium hydrotalcite (Mg-Al-HT) with molar ratio of Mg-to-Al of 3 to 1 was prepared and characterized by X-ray diffraction (XRD) and infrared spectra (IR). The performances of Mg-Al-HT for the adsorption and desorption of NOx were studied. The results indicated that the adsorption capacity of the hydrotalcite for NOx was 1398.2mg/g, and it was higher than the acticarbon‘s. The adsorption capacities depended on adsorption time and temperature.Mg-Al-HT could be regenerated by thermal decomposition, and the adsorption efficiency had not changed markedly after three cycles.