采用激励光源为514.5 nm的分幅扫描单光子计数荧光光谱装置对经20℃、42℃和48℃不同温度处理后的反应中心复合物CP47/D₁/D₂/Cyt b559的荧光光谱特性进行了研究.经解析,获得不同温度处理后,CP47/D₁/D₂/Cyt b559复合物最大峰值未发生变化,均在682 nm,说明Chla670的能量都由Chla682接收,但损耗愈来愈小,在48℃时,损耗程度最小,而其荧光百分比未发生多大变化.振动副带～700 nm和～740 nm的中心波长都发生蓝移,在不同温度下分别为:20℃ 703 nm,749 nm;42℃ 697 nm,744 nm;48℃ 694 nm,740 nm.因此可以推测温度的升高,影响了CP47/D₁/D₂/Cyt b559色素蛋白的二级结构以及色素分子的空间位置,使最大峰值处的荧光强度逐渐降低,振动副带逐渐蓝移.42℃的温度已造成影响,48℃影响较大.     

数码相机CMOS图像传感器的特性参数与选择

介绍了数码相机的核心器件———CMOS图像传感器的特性参数和在数码相机设计过程中CMOS图像传感器的选择。选择CMOS图像传感器,不仅需要考虑包括传感器的尺寸、像素总数和有效像素数、最小照度、动态范围、灵敏度、分辨力、光电响应不均匀性以及光谱响应等在内的特性参数,而且还要考虑电源管理和功耗、模数转换位数、开发的简便性以及成本等因素。     

Pyroelectricity and Spontaneous Polarization in [111] Oriented 0.955 Pb（Zn1/3Nb2/3）O3-0.045PbTiO3 Single Crystals

We report that the measurements of the pyroelectric current of the pre-poled [111]-oriented 0.955 Pb（Zn1/3Nb2/3） O3-0.045 PbTiO3 （PZN-4.5%PT） single crystals can shed some light on the phase transition and spontaneous polarization characters of this material in a similar way to measures of remanent polarization and dielectric properties. The pyroelectric current is measured and the corresponding spontaneous polarization is calculated as a function of temperature with various poling fields added during cooling the sample from 200℃ to room temperature. Critical electric field of 0.061 k V/cm is found to be essential to induce the intermediate ferroelectric orthorhombic phase between the ferroelectric rhombohedral and tetragonal phases. Below the critical field, the polarization increases almost linearly with the increase of poling field. At the critical field, the polarization at 30OC increases abruptly from 14μC/cm^2 for a poling field of O.06kV/cm to 29.5μC/cm^2 for a poling field of 0.061 kV/cm, and afterwards, increases slowly and saturates to 31 μC/cm^2 for poling fields beyond 0.55 kV/cm.     

Spectral Anomalies in the Fraunhofer Diffraction Pattern

We study the spectral characteristics theoretically and experimentally in the Fraunhofer diffraction pattern formed by the diffraction of a spatially coherent, polychromatic light through a slit. It is found that the spectrum in some diffraction directions close to the singular direction is redshifted, compared to the spectrum of the incident polychromatic light, and blueshifted in other directions, and splits into two lines at the singular direction. We show that the experimental results are consistent with the theoretical expectations.     

Temperature-Dependent Dynamic Properties of LixMn2O4 in Monte Carlo Simulations

Monte Carlo (MC) simulations are used to simulate the voltage profile and the ionic conductivity s of Li ions in LixMn2O4 and its dependence on the lithium concentration x. The open circuit potential shows clearly the two plateaus in the charge/discharge curve, which agrees well with the experimental results. The two plateaus become more and more steep when the temperature is increased. The simulated ionic conductivity shows an M-shaped curve in the plot of ionic conductivity cr versus x when the simulation temperature is low. Interestingly,the minimum valley, which lies at the middle single-phase area near x=0.5, disappears gradually when the temperature increases to 453K.     

高功率LDA紧密侧面抽运Nd:YLF两级双程离轴放大系统实验研究

 介绍了一台10mm口径两级双程离轴放大系统，实现了对5mm×5mm口径光束的激光放大，耦合系统采用高功率LDA紧密侧面直接抽运棒状Nd:YLF方式。分析并实验研究了在不同抽运电流、放大脉冲与放大器LDA抽运时刻的不同延时及不同注入能量条件下，放大系统及光束每次放大时放大特性的规律。实验得到：在放大系统5mm×5mm软光阑处注入1.58mJ能量时，放大系统可输出129.2mJ能量，能量提取效率达到19.5%，满足该系统的设计指标。     

离子束增强沉积VO2多晶薄膜的温度系数

用改进的离子束增强沉积方法和恰当的退火从V2O5粉末直接制备了VO2多晶薄膜.实验测试表明，薄膜的取向单一、相变特性显著、结构致密、界面结合牢固、工艺性能良好，薄膜的电阻温度系数（TCR）最高可达4.23%/K.从成膜机理出发，较详细地讨论了离子束增强沉积 VO2多晶薄膜的TCR高于VOx薄膜的TCR的原因.分析认为，单一取向的VO2结构使薄膜晶粒具有较高的电导激活能，致密的薄膜结构减少了氧空位和晶界宽度，使离子束增强沉积 VO2多晶薄膜结构比其他方法制备的VOx薄膜更接近于单晶VO2是其具有高TCR的原 关键词： VO2多晶薄膜 离子束增强沉积 热电阻温度系数     

多壁碳纳米管膜湿敏特性的研究

研究了多壁碳纳米管(MWNTs)薄膜的湿敏特性，实验所用的多壁碳纳米管是用热灯丝化学气相沉积法(CVD)合成的.分别对未修饰和修饰的多壁碳纳米管膜温度和湿度特性进行研究后发现，修饰的多壁碳纳米管对温度和湿度非常敏感，且对湿度的响应时间和恢复时间短，重复性好.而未修饰的多壁碳纳米管对温度和湿度不太敏感.对修饰多壁碳纳米管的湿敏特性进行了理论分析，给出了其理论表示式. 关键词： 多壁碳纳米管 化学修饰 湿敏特性 物理吸附     

Yb:FAP和Yb:C_3S_2-FAP晶体光谱的温度特性和选择激发

报导了Yb :FAP和Yb :C3S2 _FAP晶体在不同温度下的吸收光谱和荧光光谱实验结果 ,研究发现由于电子_声子近共振耦合作用 ,Yb :FAP和Yb :C3S2 _FAP晶体均存在有明显的振动谱 ,Yb :FAP晶体的零声子线在低温下还劈裂为相差 10cm- 1 的两条线 .采用激光选择激发技术研究了Yb3 离子在FAP和C3S2 _FAP晶体中的格位特征 ,结果表明Yb3 离子在这两种基质中都只占据Ca(Ⅱ )格位 ,但由于CaF2 的挥发 ,导致了Ca(Ⅱ )格位的局部畸变 .