碘掺杂的3-乙基-5-[2-(3-乙基-2苯并噻唑啉基)亚乙基]罗丹宁的结构与电性能

The merocyanine dye 3-ethyl-5-(2-(3-ethyl-2-benzothiazolinylidene)-ethylidene)-rhodanine (BTER) known as Agfa-10 has been found to have a good photoconductivity as solution cast film. In this paper iodine-doped BTER was obtained by doping with iodine vapor. Its structure was investigated with the following characteristies. 1 The doped iodine had been excited as I_3~- anion. 2 Because the electron located on the sulphur atom was transferred to iodine, the charge transfer complex of (BTER-I_3) formed. 3 During the iodine doping process, BTER changed from α-form to β-modification. These had been identified by X-ray diffraction, VIS-absorption spectra and SEM picture.4 From the volt-Ampere curve obtained from sandwich cell, when E≤2.2×10~(-1) V·cm~(-1), the room temperature electrical conductivity of BTER and BTER-I_3 were found to be 2.22×10~(-10) s·cm~(-1) and 2.6×10~(-7) S·cm~(-1), respectively.     

溶胶—凝胶合成（Mg,Ca）O—SiO2：Eu^3＋,Bi^3＋发光体及其发光行为

以Ｍｇ（ＮＯ３）２，Ｃａ（ＮＯ３）２，Ｅｕ（ＮＯ３）３，Ｂｉ（ＮＯ３）３和Ｓｉ（ＯＣ２Ｈ５）４为反应物，采用溶胶－凝胶法，在比较低的温度，首次合成０．７０１ｍｏｌＭｇＯ－０．１７５ｍｏｌＣａＯ－１．２５ｍｏｌＳｉＯ２：０．０６ｍｏｌＥｕ＾３＋，０．００２ｍｏｌＢｉ＾３＋（加入Ｌｉ＾＋作为电荷补偿剂）发光体，得到了最佳合成条件，研究了由溶胶向凝胶转变和凝胶向发光晶体的转变过程，探讨了发光体在不同激光     

微波合成铝掺杂钻酸锂材料及性能研究

以LiOH·H2O，Al2O3和Co3O4为原料，微波加热合成Li离子电池正极材料LiAlxCo（1-x）O2．通过XRD测试表征了不同Al加入量时合成产物的晶体结构，确定当x≤0．4时，产物为单一相层状结构．计算了不同x时LiAlxCo（1-x）O2的晶胞参数，随着x的增大，a值减小，c值增大．对合成LiAlxCo（1-x）O2样品进行DSC—TGA测试，结果表明，当x不同时，合成样品的热稳定性不同．SEM测试表明，合成晶体粒度较均匀，粒径在5μm左右．电化学测试表明，LiAl0.2Co0.8O2的电化学性能最好，首次循环放电容量为127mAh／g，多次循环容量损失率小于LiCoO2．     

N掺杂可见光化催化剂的研究

The N-doped, yellow colored titanium oxide photocatalysts were prepared with Ti(SO4)2 and NH4HCO3 as precursors by precipitation method. The photocatalytic ability under the irradiation of UV or visible light for the catalysts prepared was studied by degradation of styphnic acid. The materials were characterized by EDS, XRD, FTIR, UV-Vis DRS, and XPS. The results indicate that the photocatalytic ability of catalysts is improved, especially the ability of visible light response. The results of UV-Vis DRS show that the response wavelength range of N-dopped nitrogen is red shifted, the absorption region is expanded to 476 nm.     

显微共焦拉曼光谱研究电化学合成聚苯胺膜

显微共焦拉曼技术被用来研究电化学合成的聚苯胺（PANI）膜. 研究结果表明：在不同的激发光聚焦深度，聚苯胺膜的拉曼光谱有明显变化.从而反映出聚苯胺膜的掺杂程度在膜生长过程中随膜厚度的增长而增加. 并由X射线电子能谱（XPS）和紫外吸收光谱（UV）分析证实.     

四氯化铂与铂氯酸掺杂聚乙炔的X射线光电子能谱研究

用 X 射线光电子能谱法对四氯化铂(PtCl_4)及铂氯酸(H_2PtCl_6·6H_2O)掺杂聚乙炔进行了研究.发现Pt4f 与 Cl2p 谱峰均由相距约1.5eV 的两组峰组成.Pt4f 高结合能端的组份可指认为四价铂,而低结合能端的组份为二价铂.对 Pt4f 及 Cl2p 峰积分强度的分析表明,对二价铂有:[Cl]/[pt~(2 )]=2,对四价铂有:[Cl]/[pt4~ ]=6.C 1s 峰也由两个分离约1eV 的峰组成,高结合能端的强度随掺杂浓度的增加而增加.这些结果说明铂盐掺杂聚乙炔通过由高分子链向掺杂剂的电荷转移而使部份高分子链被氧化,部份四价铂盐被还原成 PtCl_2.透射电镜形态观察及选区电子衍射证明膜上存在 PtCl_2的聚集.电荷转移链段在高分子链上的分布是无规的.并由此估计了电荷转移链段上每个碳原子的电荷约为 0.2|e|.由以上结果我们推断 PtCl_4与 H_2PtCl_6·6H_2O 的电荷转移过程可由下式表达.对 PtCl_4 掺杂:2PtCl_4 2e→PtCl_6~(2-) PtCl_2对 H_2PtCl_6掺杂:2H_2PtCl_6 2e→PtCl_6~(2-) PtCl_2 4HCl这两种掺杂剂的对阴离子均是 PtCl_6~(2-)离子.     

STUDY ON 1-HEXENE POLYMERIZATION BASED ON ZIEGLER-NATTA CATALYSTS WITH DOPED SUPPORT

A series of Ti/Mg supported catalysts are prepared by using ball-milled mixtures of MgCl2-ethanol adducts and NaCl as supports, and 1-hexene polymerizations catalyzed by the novel catalysts are studied. It is found that the molecular weight distribution of poly(1-hexene) becomes apparently narrower when catalysts with doped supports are used, indicating that changing the structure of the support is an effective way to regulate the active center distribution of heterogeneous Ziegler-Natta catalyst.     

复合氟化物中铕(II)f-f 跃迁发射的判据及其运用

建立了Eu^2^+离子f→f跃迁发射产生的判据运用这-判据预测, 设计并合成了近四十种掺Eu^2^+的复合氟化物, 在这些基质中均观察到Eu^2^+的f-f跃迁尖峰发射。本文对所提供的判据从化学键性质和晶场效应方面作了简要解析, 并对判据的运用条件作了讨论。     

纳米晶掺钇硬质合金粉末的制备

采用高能球磨法制备了纳米晶掺Y硬质合金粉末。用XRD，SEM和DTA等分析检测手段，研究了纳米晶掺Y硬质合金粉末的结构、形貌和相的变化。结果表明：高能球磨45h，可获得晶粒尺寸约为8nm的掺Y硬质合金粉末；微量Y的加入，有利于硬质合金粉末晶粒的细化；在25～45h范围内，随着高能球磨时间的延长，粉末晶粒尺寸减小，且掺Y硬质合金粉末的晶粒尺寸比未掺Y的硬质合金粉末晶粒尺寸要细一倍；高能球磨25h，粉末中Co的X射线衍射峰消失。高能球磨掺Y硬质合金粉末的DTA曲线在626℃出现了1个尖锐的放热峰。高能球磨掺Y硬质合金粉末固结之后，其合金晶粒细小，机械性能较好。