La1-xSrxYO3-α陶瓷的合成及电性能研究

本文采用高温固相法合成了La1-xSrxYO3-α(x=0.00,0.05,0.10,0.15)系列陶瓷样品,用XRD、SEM对样品进行了表征,并用交流阻抗谱、氢泵、氢浓差电池、氧浓差电池等系统地研究了该系列样品的电性能.结果表明,该系列陶瓷样品均为钙钛矿型单斜晶相结构:样品的氢浓差电池电动势的实测值和理论值吻合得很好,表明样品在氢气气氛中为纯离子导体;氢泵测试结果证实了样品在氢气气氛中基本上是质子导体;氧分压与电导率的关系表明样品在高氧分压气氛中是离子(质子+氧离子)和空穴的混合导体.在低氧分压气氛中是离子(质子+氧离子)导体;氧浓差电池测试结果表明样品在干燥的氧化性气氛中是氧离子和空穴的混合导体.     

Synthesis and characterization of mixing soft-segmented waterborne polyurethane polymer electrolyte with room temperature ionic liquid

Composite polymer electrolytes based on mixing soft-segment waterborne polyurethane(WPU)and 1-butyl-3-methylimidazolium bis[(trifluoromethyl)sulfonyl]imide(BMImTFSI)have been prepared and characterized.The addition of BMImTFSI results in an increase of the ionic conductivity.At high BMImTFSI concentration(BMImTFSI/WPU=3 in weight ratio),the ionic conductivity reaches 4.27×10~(-3)S/cm at 30℃.These composite polymer electrolytes exhibit good thermal and electrochemical stability,which are high enough to be...     

多巴胺改性聚苯醚基材的金属化

聚苯醚基材的对称、低活性分子结构使其具有十分稳定的化学性质,因此难以直接利用化学镀技术在基材表面沉积出高质量的金属层.针对此问题,文中采用化学蚀刻与多巴胺接枝相结合的方法对PPO基材进行表面改性处理,以调整表面粗糙度,改善表面亲水性.文中引入对Ag+具有吸附作用的活性官能团,提高了沉积金属层的导电性和附着力.各项表征测...     

预拉伸处理对聚吡咯弹性长丝导电及传感性能的影响

为探究预拉伸处理对聚吡咯弹性导电长丝导电及传感性能的影响，通过在吡咯聚合时对弹性长丝进行不同程度的预拉伸处理，得到具有不同增重率的聚吡咯涂层，通过扫描电镜观察其微观形貌，并进行电学及传感性能的测试分析。研究结果表明电阻会随着预伸长率增加(>70%)而降低，在预伸长率为10%时聚吡咯层较为光滑，但具有最好的应变传感性能：在0～2 cN范围内灵敏度高，可达7.68/N,超过2 cN后灵敏度降低并稳定在1/N左右。稳定性、重复性实验及手指弯曲测试都表明，预拉伸10%处理的导电长丝具有良好的灵敏度和传感稳定性，电阻变化率分别为24.71%和11.01%,因此，具有此结构的聚吡咯复合弹性丝有望应用于人体运动和生理信号的检测中。预伸长率较高的弹性导电纱表面具有褶皱结构，随着拉伸具有稳定的电阻值，可用于导线和电极中。