Laser induced copper electroless plating on polyimide with Q-switch Nd:YAG laser

The results of laser induced deposition of copper on polyimide substrate from copper electrolyte solution are reported. Unlike most work reported in the literatures where CW Ar⁺ lasers were used, a second harmonic (532 nm wavelength) Q-switch Nd:YAG laser was used for our experiments. The deposition process was conducted by laser-catalyzing of the polyimide surface and subsequent photothermal-accelerated reduction of copper-complex ions in an alkaline reducing environment. The characteristics of the deposited copper line were investigated in terms of laser beam scanning speed, and the number of scans. The surface morphology and chemical composition of the deposited copper were analyzed using field emission scanning electron microscope (FESEM) and energy dispersive spectrometer (EDX). The optimum processing conditions have been identified. The copper deposit was found to adhere well to the substrate.     

非晶金刚石膜的性能及其应用

非品金刚石薄膜具有超高硬度等一系列优异的特殊性能，为工程界孜孜追求的材料表面镀膜。用百纳科技公司研发制造的过滤阴极真空电弧离子镀膜机镀制的非晶金刚石薄膜，SP^3金刚石结构量≥80％，硬度高，膜／基结合力高，摩擦系数小，耐磨损，耐腐蚀，透光率高，在电子，机械，光学，生物医学上有广泛应用前景。我们已在视窗玻璃，丝锥，模具，硬质合金刀头等产品上成功应用。     

脉冲电镀最佳参数之探索和优化

本文利用正交实验法对脉冲电镀各控制参数进行试验,对影响分散能力、镀层可靠性及外观质量的各种因素进行探讨,寻找影响外观质量的显著因子并加以控制,同时进一步优化脉冲电镀的工艺参数。     

图形电镀铜的常见缺陷及故障排除

本文主要阐述印制电路板生产中图形电镀铜常见缺陷及成因,查找影响其品质的因素和工序并结合相关生产制定相应的预防措施,有效提高产品质量。     

Preparation and microwave absorption properties of electroless Co-Ni-P coated strontium ferrite powder

A new type of Co-Ni-P coated strontium ferrite nanocomposite was prepared with electroless plating enhanced by ultrasonic wave at room temperature. The plating process was studied carefully. The morphology, crystal structure and microwave absorption properties of the Co-Ni-P coated powder were studied with field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), energy dispersive analysis of X-rays (EDX) and vector network analyzer. The results show that the strontium ferrite powder was successfully coated with Co-Ni-P alloy and possesses excellent microwave absorption properties. The maximum microwave loss of the composite powder reaches −44.12 dB. The bandwidth with the loss above −10 dB exceeds 13.8 GHz.     

STM/AFM studies of the evolution of morphology of electroplated Ni/W alloys

The surface morphology evolution of Ni/W alloys was studied, as a function of the alloy composition. Using the modified plating baths developed in our laboratory recently, electroplated Ni/W alloys with different W content, in the range of 7–67 atom percent (a/o), can be obtained. This was found to lead to different structures, ranging from polycrystalline fcc-Ni type structure to amorphous, followed by orthorhombic with increasing W content in the alloy. Powder XRD was studied to determine the crystal structures. Ex situ STM, AFM and SEM were used to study in detail the surface morphologies of the different alloys, and their evolution with increasing W content.

The important findings are that a mixture of two crystalline forms can give rise to an amorphous structure. Hillocks that are usually a characteristic of epitaxial growth can also exist in the amorphous alloys. Oriented scratches caused by stress can also be formed.

Up to 20 a/o of W is deposited in the alloys in crystalline form, with the fcc-Ni type structure. Between 20 and about 40 a/o an amorphous structure is observed, and above that an orthorhombic crystal structure is seen, which is characteristic of the NiW binary alloy. Careful choice of the composition of the plating bath allowed us to deposit an alloy containing 67 a/o W, which corresponds to the composition NiW₂.     

Electrical conductivity of chromate conversion coating on electrodeposited zinc

For certain applications of galvanized steel protected with conversion coatings it is important that the surface is electrically conductive. This is especially important with mating surfaces for electromagnetic compatibility. This paper addresses electrical conductivity of chromate conversion coatings. A cross-matrix study using different zinc plating techniques by different labs showed that the main deciding factor is the type of zinc-plating bath used rather than the subsequent chromating process. Thus, chromated zinc plate electrodeposited from cyanide baths is non-conductive while that from alkaline (non-cyanide) and acid baths is conductive, even though the plate from all the bath types is conductive before conversion coating. The results correlate well with the microscopic structure of the surfaces as observed with scanning electron microscopy (SEM) and could be further corroborated and rationalized using EDX and Auger spectroscopies.     

反应离子镀光学薄膜的微观结构分析

用反应离子镀方法制备了ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜，用透射电子显微镜分别观察了由反应离子镀方法及传统蒸镀法二种不同工艺制得的ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜的断面结构，并对ＴｉＯ２单层膜进行了喇曼分析和卢瑟福背散射分析。     

化学镀工艺在微电子材料中的研究和应用

简要综述了化学镀工艺在微电子材料中的应用,讨论了影响化学镀镍、铜、锡、钴和贵金属等的主要因素,阐述了化学镀微电子材料的特性、存在问题及研究动态。     

图形电镀中抗镀现象——凹坑的原因剖析

该文通过对本公司在图形电镀时出现的凹坑现象,进行了一个简要的分析探讨,供大家参考。