组合原则回溯

从组合原则产生的背景和关键入手，分析和叙述了里兹的组合原则在光谱学上的重要意义，同时，也阐述了它与玻尔氢原子理论之间的关系。     

Resistivity exponent of two-dimensional lattice animals

We calculate the average resistanceR(L) of lattice animals spanningL×L cells on the square lattice using exact and Monte Carlo methods. The dynamical resistivity exponent, defined asR(L) L , is found to be =1.36±0.07. This contradicts the Alexander-Orbach conjecture, which predicts 0.8. Our value for differs from earlier measurements of this quantity by other methods yielding =1.17±0.05 and 1.22±0.08 by Havlin et al.On leave from the Institute of Theoretical Physics, Chinese Academy of Sciences, Beijing, China.     

光声光谱法研究光学薄膜的吸收特性

本文以“一维热流活塞模型”为基础,推导出薄膜光声表达式,光声信号的幅值正比于吸收率.测量了透明基底上光学薄膜的光声吸收谱,实验结果与理论一致.尤其是测量弱吸收薄膜的吸收谱时,具有较高的灵敏度和实用性.     

Image guide couplers with dielectric coupling elements and radiation reduction

Directional couplers in image guide technique for millimeter-wave circuits are discussed, and steps to improve their properties are demonstrated. The simple two-line-9 dB coupler with periodical coupling is compared to a design with an intermediate dielectric coupling element to reduce the frequency dependence. Radiation from the waveguide bends can be reduced significantly by inserting absorber materials at critical points. Experimental results for a-3 dB coupler are also given.     

SPS法研究ZnTPP对TiO_2的光谱敏化

本文利用表面光电压谱(Surface Photovohage spectroscopy,简称SPS)研究了ZnTPP对TiO_2粉末的光谱敏化,发现用ZnTPP修饰后的TiO_2(金红石和锐钛矿)粉末在可见区420、550和590nm附近有三个光伏响应带,它们分别对应于ZnTPP的Soret、Q(1,0)和Q(0,0)带。经过严格的实验和分析,证明这三个带是由ZnTPP对TiO_2的敏化光电压引起的,而不是ZnTPP自身的光伏响应。在敏化效果上,亚稳的锐钛矿优于金红石。同时,我们对这种光敏表面的光诱导电荷转移机制和SPS作为一种研究光谱敏化方法的可行性进行了讨论。     

Conformations, Energy and Spectral Characteristics of 2,3-Trimethylene- and 2,3-Pentamethylene-3,4-dihydro-4-quinazolinones

Quantum-chemical calculations and IR spectroscopy were used to study the conformations as well as the energy and spectral characteristics of 2,3-trimethylene- and 2,3-pentamethylene-3,4-dihydro-4-quinazolinones. The shift of -electron density from the heterocyclic system to the carbonyl group and, thus, the proton affinity of the oxygen atom of this group increase with expansion of the bond angle at the nitrogen atom in going from a five-membered to seven-membered ring.     

La2Zr2O7催化剂结构相变对甲烷氧化偶联反应性能的影响

采用共沉淀法并通过改变焙烧温度制备了一系列具有不同晶相结构的La₂Zr₂O₇催化剂，在微型固定床反应器上评价其甲烷氧化偶联反应性能，并利用XRD、Raman、CO₂-TPD、XPS等表征手段，探究催化剂的物相结构、表面碱性以及表面氧物种的变化规律。结果表明，随着焙烧温度从700℃逐渐升高到1200℃，La₂Zr₂O₇催化剂结晶度不断提高，晶相发生明显变化，从无定形结构逐渐向缺陷萤石结构过渡，最终转变成烧绿石结构。焙烧温度提高促使La₂Zr₂O₇晶相转变过程中，催化剂表面的碱性强度减弱，中等碱性位数量以及具有催化活性的表面氧物种O₂^2-和O₂^-的相对含量不断减少，致使催化剂的CH₄转化率和C₂₊选择性不断降低。其中，无定形LZO-CP-700催化剂表现出最佳的甲烷氧化偶联反应性能。     

Study of migration of active components of phosphorescent oxygen sensors for food packaging applications

A study of migration of the active components of oxygen sensors into food is presented. Six types of sensors, based on different oxygen sensitive dyes (two metalloporphyrins and one ruthenium dye), polymers (polystyrene and polysulfone) and support materials, were exposed to a number of standard ‘food simulants’ recommended by FDA/EU guidelines and then assayed for migration or sensor components and changes in oxygen calibration. Both metalloporphyrin sensor dyes leached only in olive oil and in 95% ethanol (used as a positive control), at maximum levels of 19.22 μg/dm² for PtOEPK and 113.96 μg/dm² for PtTFPP. The RuDPP dye showed maximum leaching in 95% ethanol (25.19 μg/dm²) while also migrating in an acidic aqueous simulant. Planar supports such as polyester tended to enhance the stability of the sensor. Migration of the styrene monomer from the polystyrene encapsulation medium was concluded to be low enough to be insignificant. Migration of sensor components was shown to correlate with the changes in sensor response to oxygen. Based on these results, sensor combinations were ranked on the basis of their resistance to leaching and their general stability, safety and suitability for use on a large scale in packaged foods and related food applications was proven.     

Properties of ITO films prepared by reactive magnetron sputtering

Indium tin oxide (ITO) thin films were deposited by mid frequency pulsed dual magnetron sputtering using a metallic alloy target with 10 wt.% tin in an atmosphere of argon and oxygen. The aim of the work was to study the interdependence of structural, electrical and optical properties of ITO films deposited in the reactive and transition target mode, respectively. The deposition rate in the transition mode exceeds the deposition rate in the reactive mode by a factor of six, a maximum value of 100 nm·m min⁻¹ could be achieved. This corresponds to a static deposition rate of 200 nm min⁻¹. The lowest electrical resistivity of 1.1·10⁻³ Ω cm was measured at samples deposited in the high oxygen flow range in the transition mode. The samples show a good transparency in the visible range corresponding to extinction coefficients being below 10⁻². X-ray diffraction was used to characterise crystalline structure as well as film stress. ITO films prepared in the transition mode show a slightly preferred orientation in (211) direction, whereas films deposited in the reactive mode are strongly (222) oriented. Compared to undoped In₂O₃ all samples have an enlarged lattice. The lattice strain perpendicular to the surface is about 0.8% and 2.0% for films grown in the transition and the reactive mode, respectively. Deposition in the transition mode introduces a biaxial film stress in the range of −300 MPa, while stress in reactive mode samples is −1500 MPa.