Hydroxyapatite coating on porous silicon substrate obtained by precipitation process

Hydroxyapatite Ca₁₀(PO₄)₆(OH)₂ (HAP) is known as a bioactive and biocompatible material, HAP coatings were used to improve the biocompatible of substrate by many researcher, In this work, HAP thin films on porous silicon (PS) substrates have been prepared by aqueous precipitation method with rapid thermal annealing (RTA) processes. The HAP films had been prepared under the annealing temperature ranging from 300 to 1000 °C. By the measurement of X-ray diffraction (XRD), it was found that for the crystallinity optimization, the heat-treatment at 850–950 °C for 1 h would be favorable. Atomic force microscopy (AFM) and scanning electron microscope (SEM) measurements reveal a dense and smooth surface of the HAP film, and tightly adherence of the coating on porous silicon substrate after sintered. Thus, by this method, porous silicon could be increased its bioactivity and so that could be used in the biomedical area.     

Thickness of a silica-tethered poly(ethylene oxide) layer measured by spin labeling

EPR spectroscopy of labeled poly(ethylene oxide) (PEO) grafted on silica has been used to characterize the conformation and local dynamics of the chains. Grafted molecules of MW 2000 with grafting ratios of 0.045, 0.057, 0.126, and 0.42 molecules/nm² were in contact with benzene. The mobility of the label was compared with that observed for solution of PEO from very diluted to highly concentrated and even bulk PEO. Thus, the concentration inside the grafted layer could be evaluated and also the thickness, which evolves rather linearly with the grafting ratio. © 1995 John Wiley & Sons, Inc.     

A comparative XPS and UPS study of VOx layers on mineral TiO2(001)‐anatase supports

Four vanadium oxide layers on mineral TiO₂(001)‐anatase supports with different thickness (3–33 Å) were prepared with reactive d.c. magnetron sputtering and were extensively studied with photoelectron spectroscopy. Al Kα radiation and 150 eV synchrotron radiation were used as excitation sources. The evolution of the 2p, 3s and 3p core level line shapes of V and Ti as a function of the vanadium oxide thickness was studied, as well as the O1s and O2s core lines and the valence band. All the V2p spectra of the deposited vanadium oxide layers consist of at least 60% V⁵⁺, the rest being V⁴⁺. The V3p region is complicated by multiplet splitting, which prevents the determination of the vanadium oxidation state. The V3p multiplet splitting is different for the two excitation energies. No reduction of the titania support surface due to the vanadium oxide deposition was observed. Copyright © 2006 John Wiley & Sons, Ltd.     

Heterograft copolymers of poly(ε‐caprolactone) prepared by combination of ATRA “grafting onto” and ATRP “grafting from” processes

This paper aims at reporting on the synthesis of a heterograft copolymer by combining the “grafting onto” process based on atom transfer radical addition (ATRA) and the “grafting from” process by atom transfer radical polymerization (ATRP). The statistical copolymerization of ε‐caprolactone (εCL) and α‐chloro‐ε‐caprolactone (αClεCL) was initiated by 2,2‐dibutyl‐2‐stanna‐1,3‐dioxepane (DSDOP), followed by ATRA of parts of the chlorinated units of poly(αClεCL‐co‐εCL) on the terminal double bond of α‐MeO,ω‐CH₂?CH? CH₂? CO₂‐poly(ethylene oxide) (PEO). The amphiphilic poly(εCL‐g‐EO) graft copolymer collected at this stage forms micelles as supported by dynamic light scattering (DLS) and transmission electron microscopy (TEM). The unreacted pendant chloro groups of poly(εCL‐g‐EO) were used to initiate the ATRP of styrene with formation of copolymer with two populations of randomly distributed grafts, that is PEO and polystyrene. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6015–6024, 2006     

Synthesis of new thermosetting poly(2,6‐dimethyl‐1,4‐phenylene oxide)s containing epoxide pendant groups

A new class of thermosetting poly(2,6‐dimethyl‐1,4‐phenylene oxide)s containing pendant epoxide groups were synthesized and characterized. These new epoxy polymers were prepared through the bromination of poly(2,6‐dimethyl‐1,4‐phenylene oxide) in halogenated aromatic hydrocarbons followed by a Wittig reaction to yield vinyl‐substituted polymer derivatives. The treatment of the vinyl‐substituted polymers with m‐chloroperbenzoic acid led to the formation of epoxidized poly(2,6‐dimethyl‐1,4‐phenylene oxide) with variable pendant ratios, and the structures and properties were studied with nuclear magnetic resonance spectroscopy, Fourier transform infrared spectroscopy, differential scanning calorimetry, thermogravimetric analysis, and gel permeation chromatography. The ratios of pendant functional groups were tailored for the polymer properties, and the results showed that the glass‐transition temperatures increased as the benzylic protons were replaced by bromo‐, vinyl‐, or epoxide‐functional groups, whereas the thermal stability decreased in comparison with the original polymer. Within a molar fraction of 20–50%, the degree of functionalization had little effect on the glass‐transition temperature; however, it correlated inversely with the thermal stability of each functionalized polymer. The thermal curing behavior of the epoxide‐functionalized polymer was enhanced by the increment of the pendant functionality, which resulted in a significant increase in the glass‐transition temperature as well as the thermal stability after the curing reaction. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5875–5886, 2006     

Synthesis of poly(ethylene oxide) with pending 2,2,6,6‐tetramethylpiperidine‐1‐oxyl groups and its further initiation of the grafting polymerization of styrene

A new stratagem for the synthesis of amphiphilic graft copolymers of hydrophilic poly(ethylene oxide) as the main chain and hydrophobic polystyrene as the side chains is suggested. A poly(ethylene oxide) with pending 2,2,6,6‐tetramethylpiperidine‐1‐oxyls [poly(4‐glycidyloxy‐2,2,6,6‐tetramethylpiperidine‐1‐oxyl‐co‐ethylene oxide)] was first prepared by the anionic ring‐opening copolymerization of ethylene oxide and 4‐glycidyloxy‐2,2,6,6‐tetramethylpiperidine‐1‐oxyl, and then the graft copolymerization of styrene was completed with benzoyl peroxide as the initiator in the presence of poly(4‐glycidyloxy‐2,2,6,6‐tetramethylpiperidine‐1‐oxyl‐co‐ethylene oxide). The polymerization of styrene was under control, and comblike, amphiphilic poly(ethylene oxide)‐g‐polystyrene was obtained. The copolymer and its intermediates were characterized with size exclusion chromatography, ¹H NMR, and electron spin resonance in detail. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3836–3842, 2006     

Structural, morphological, wettability and thermal resistance properties of hydro-oleophobic thin films prepared by a wet chemical process

The structural properties of fluorine containing polymer compounds make them highly attractive materials for hydro-oleophobic applications. However, most of these exhibit low surface energy and poor adhesion on the substrates. In the present investigation, crack free, smooth and uniform thin films of poly[4,5-difluoro-2,2-bis(trifluoromethyl)-1,3-dioxole]-co-tetrafluoroethylene (TFD-co-TFE) with good adhesion have been deposited by wet chemical spin-coating technique on polished AISI 440C steel substrates. The as-deposited films (xerogel films) have been subjected to annealing for 1 h at different temperatures ranging from 100 to 500 °C in an argon atmosphere. The size growth of the nano-hemispheres increased from 8 nm for xerogel film to 28 nm for film annealed at 400 °C. It was found that as the annealing temperature increased from 100 to 400 °C, nano-hemisphere-like structures were formed, which in turn have shown increase in the water contact angle from 122° to 147° and oil (peanut) contact angle from 85° to 96°. No change in the water contact angle (122°) has been observed when the films deposited at room temperature were heated in air from 30 to 80 °C as well as exposed to steam for 8 days for 8 h/day indicating thermal stability of the film.     

Infrared combination and difference bands of the NO dimer

The mid-infrared (1500-3800 cm⁻¹) absorption spectrum of gaseous nitric oxide has been studied at low temperature (99 K) with a long absorption path (160 m) in order to observe weak combination, difference, and overtone bands of the NO dimer. About ten new bands were assigned with greater or lesser certainty. Combined with previous results, they lead to a set of 12 secure and 7 tentative vibrational term values for (NO)₂, essentially doubling our knowledge of NO dimer vibrational states. The strongest non-fundamental bands in this region, other than the ν₁ (symmetric N-O stretch) + ν₅ (asymmetric N-O stretch) overtone, involve combinations of ν₅ with ν₃ (intermolecular stretch). Excitation of ν₅ results in increased frequencies for the intermolecular modes ν₂, ν₃, and ν₄. A new value of 155.5 cm⁻¹ was obtained for ν₄, the elusive infrared-inactive out-of-plane fundamental vibration.     

气密性碳涂覆光纤筛选强度与电阻关系研究

通过实验分析确立了把光纤电阻作为衡量气密性碳涂覆光纤通过２％应变筛选的过渡标准。要拉制２％应变筛选的碳涂覆光纤，其电阻值应小于３０ｋΩ／ｃｍ。     

Characterization of nonstoichiometric nickel manganite spinels NixMn3−x□3δ/4O4+δ by temperature programmed reduction

Cation deficient spinels Ni_xMn_3−x□_3δ/4O_4+δ (0≤x≤1) have been prepared by thermal decomposition of mixed oxalates Ni_x/3Mn_(3−x)/3(C₂O₄)·nH₂O in air at 623 K. They have been characterised by temperature programmed reduction (TPR) under H₂, the reaction being followed by gravimetric and powder X-ray diffraction measurements. It has been shown that TPR proceeds in several steps. The first steps correspond to the loss of nonstoichiometric oxygen leading to the formation of a stoichiometric oxide. During the following stages the manganese cations are reduced, causing the spinel structure to be destroyed, and the formation of solid solution of NiO in a cubic MnO. Subsequently, Ni²⁺ cations undergo a reduction to metallic nickel, and, finally, a mixture of nonstoichiometric MnO_1−δ and metallic nickel is formed. These oxides contain a high level of vacancies which vary with the nickel content with a maximum of δ≈1 near x=0.6. This nonstoichiometry is ascribed both to the presence of Ni³⁺ and excess of Mn⁴⁺.