反应离子镀光学薄膜的微观结构分析

用反应离子镀方法制备了ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜，用透射电子显微镜分别观察了由反应离子镀方法及传统蒸镀法二种不同工艺制得的ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜的断面结构，并对ＴｉＯ２单层膜进行了喇曼分析和卢瑟福背散射分析。     

Magnetic pole pinning at rectangular defects on MnAs/GaAs(0 0 1)

Strong magnetic poles at characteristic rectangular defects have been observed using a magnetic force microscope on a MnAs(  1 0 0) thin film with the thickness of 30 nm. The MnAs thin film was epitaxially grown on a GaAs(0 0 1) substrate. The magnetic poles were in one-arranging direction, being independent of the magnetization direction of the film. The poles were pinned at the edges of the rectangular defects until just below the Curie temperature, and formed a stable magnetic-field loop on the MnAs surface. The stability of the magnetic pole pinning shows the distinctive feature of the magnetic domain structure on the surface with a strong anisotropy, which was built in the heterostructure of MnAs and GaAs.     

Titanium carbonitride films on cemented carbide cutting tool prepared by pulsed high energy density plasma

Hard films prepared by pulsed high energy density plasma (PHEDP) are characterized by high film/substrate adhesive strength, and high wear resistance. Titanium carbonitride (TiCN) films were deposited onto YG11C (ISO G20) cemented carbide cutting tool substrates by PHEDP at room temperature. XRD, XPS, SEM, AES, etc. were adopted to analyze the phases (elements) composition, microstructure and the interface of the films, respectively. The results show that, the uniform dense films are composed of grains ranging from 70 to 90 nm. According to the AES result, there is a broad transition layer between the film and the substrate, due to the ion implantation effect of the PHEDP. The transition layer is favorable for the film/substrate adhesion.     

CRYSTAL STRUCTURE AND MORPHOLOGY OF NASCENT SAMPLES OF SYMMETRIC AROMATIC POLYESTERS——Ⅱ. POLY(p-PHENYLENE 2,6-NAPHTHALATE)

Confined thin film melt polymerization (CTFMP) of naphthalene chloride/hydroquinone (NCMQ, 1/1, molar)mixtures at polymerization temperatures (T_p) below ca. 300℃ resulted in relatively thick, elongated crystals. Polymerizationof NC/HQ above 300℃ between glass yielded well-formed lamellar crystals ca. 100 A thick. Phase Ⅰ and Ⅱ [001] EDpatterns were obtained for all T_p, the relative amount of phase Ⅰ increasing with T_p. Polymerization of naphthalenedicarboxylic acid/hydroquinione diacetate 1/1 mixtures at high T_p also yielded lamellar crystals that "curled up" off of thesubstrate. When the high temperature CTFMP polymerization was conducted between mica, aggregates of lamellae on-edgedeveloped but epitaxial growth did not occur. Epitaxial growth of lamellae between mica could be obtained, however, byconfined thin film solution polymerization, with both of the latter samples yielding apparently related ED patterns from adifferent unit cell than phase Ⅰ or Ⅱ. Fiber patterns, obtained from sheared samples, indicated considerably greater crystaldisorder than in the nascent crystals. Refinement of the phase Ⅰ unit cell parameters, based on the [001] and [01 1] EDpatterns, with modeling based on Cerius~2, suggests a monoclinic phase Ⅰ unit cell with a = 7.76, b = 5.71, c = 14.99 A, α = γ= 90°, β= 99.7°, ρ = 1.47 g/cm~3, space group P12_1/al.     

Dialdehyde starch‐crosslinked chitosan films and their antimicrobial effects

For improved mechanical and water‐swelling properties of chitosan films, a series of transparent films were prepared with dialdehyde starch as a crosslinking agent. Fourier transform infrared and X‐ray analysis results demonstrated that the formation of Schiff's base disturbed the crystallization of chitosan. The mechanical properties and water‐swelling properties of the films were significantly improved. The best values of the tensile strength and breaking elongation were 113.1 MPa and 27.0%, respectively, when the dialdehyde starch content was 5%. All the crosslinked films still retained obvious antimicrobial effects toward S. aureus and E. coli, and they showed potential for biomedical applications. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 993–997, 2003     

Coupled lubrication and Stokes flow finite elements

A method is developed for performing a local reduction of the governing physics for fluid problems with domains that contain a combination of narrow and non‐narrow regions, and the computational accuracy and performance of the method are measured. In the narrow regions of the domain, where the fluid is assumed to have no inertia and the domain height and curvature are assumed small, lubrication, or Reynolds, theory is used locally to reduce the two‐dimensional Navier–Stokes equations to the one‐dimensional Reynolds equation while retaining a high degree of accuracy in the overall solution. The Reynolds equation is coupled to the governing momentum and mass equations of the non‐narrow region with boundary conditions on the mass and momentum flux. The localized reduction technique, termed ‘stitching,’ is demonstrated on Stokes flow for various geometries of the hydrodynamic journal bearing—a non‐trivial test problem for which a known analytical solution is available. The computational advantage of the coupled Stokes–Reynolds method is illustrated on an industrially applicable fully‐flooded deformable‐roll coating example. The examples in this paper are limited to two‐dimensional Stokes flow, but extension to three‐dimensional and Navier–Stokes flow is possible. Copyright © 2003 John Wiley & Sons, Ltd.     

Properties of sol-gel dip-coated zinc oxide thin films

Zinc oxide (ZnO) films were deposited on glass substrates by the sol-gel dip coating method using acrylamide route. The films were characterized by X-ray diffraction studies which indicated wurtzite structure. Optical absorption measurements indicated band gap in the range 3.17-3.32 eV. XPS studies indicated the formation of ZnO. The resistivity of the films were in the range 1000-10,000 ohm cm.     

Thickness dependence of free‐standing thin films

Below a critical thickness, of about 60 nm, the glass transition temperature of polystyrene (PS) films decreases with film thickness, as demonstrated using free‐standing films. A geometrical model is developed here describing this phenomenon in the case of ideal (Gaussian) chains. This model, which can be considered as an application of the free volume model, assumes that the decrease of the glass transition temperature from thick to ultrathin films is due to the modification of the interpenetration between neighboring chains. The theoretical curve deduced from the model is in excellent agreement with the PS experimental results, without using any adjustable parameters. From these results, it can be concluded that new chain motions, usually buried in bulk samples, are expressed by the presence of the surface. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 10–17, 2007     

用电泳技术制备YBCO高温超导厚膜

介绍了电泳技术制备YBCO高温超导厚膜的实验方法和YBCO高温超导厚膜的电学性质测量 ,讨论了在学生小型科研实验或设计实验中开展此实验的学时安排、注意事项和实验内容的扩展 .     

微型网状结构支架的力学性能研究

冠状动脉支架为圆柱形微型网状结构，直径1mm，厚度0．1mm，长度10～16mm。在经皮冠状动脉介入PCI治疗中由球囊充气撑开到直径为2．5～3．5mm的支架，在血管内承受血管壁回弹压力。为了保持血液流通支架必须保持其几何圆形。这是一个结构弹塑性稳定性问题。但是目前国际上对于支架的力学性能质量指标主要以强度性能评定而不涉及支架屈曲性能是不妥的。本文对于支架的强度和屈曲性能进行了全面的理论分析和实验研究，自行研制了智能式电子检测仪成功地对微型网状结构支架的强度和屈曲性能实现了实测实验研究。由于微型支架的离散型网状结构的特点，在实验中出现一些特殊的屈曲现象。本文研究结果对于支架的形状与性能设计的改进和力学性能质量标准规范的制订具有重要意义。