纳米级碳导电剂的种类对licoo2电化学性能的影响

碳纳米管;锂离子电池;正极;倍率容量;导电剂     

包覆Y(OH)3的球形Ni(OH)2的电化学性能

利用软嵌式粉末电极技术研究了Y(OH)3包覆对球形Ni(OH)2电化学性能的影响. 循环伏安结果表明, 在球形Ni(OH)2的氧化过程中存在Ni(Ⅲ)和Ni(Ⅳ)的两步氧化反应, 产生的Ni(Ⅳ)不稳定, 能分解产生NiOOH和氧气, 所以可将Ni(Ⅲ)→Ni(Ⅳ)看作副反应. Y(OH)3包覆层对Ni(OH)2氧化过程后期的副反应, 特别是Ni(Ⅲ)→Ni(Ⅳ)具有较好的抑制作用. 由包覆后的Ni(OH)2制成的模拟电池表现出很好的高温性能, 在1C充放电条件下, 当Y的摩尔分数为1.61%时, 在60 ℃时所对应的容量保持率可达到25 ℃的92.7％; 当Y的摩尔分数仅为0.55 %时, 在60 ℃时所对应的质量比容量也可达到241.3 mA·h/g.     

水相锌二次电池正极材料V2O5/C的电化学性能研究

采用溶胶－凝胶法合成了一种V₂O₅/C复合材料.扫描电镜（SEM）和红外光谱（FTIR）分析表明,这是一种外层V₂O₅胶体包覆内层乙炔分子的多孔复合材料.以V₂O₅/C作正极,锌片为负极,Zn(ClO₄)₂溶液为电解质组成水相锌二次电池,采用循环伏安（CV）和电化学阻抗谱（EIS）等方法研究发现:V₂O₅:C质量比为1:1时电极具有最好的电化学性能,电池开路电压达1.64 V; Zn^2＋能分别在1.01 V和1.26 V处分步嵌入V₂O₅/C结构中A、B两种位置,其嵌入电流密度峰值最高可达70 mA•g^－1,并且具有较好的循环充放电性能;在一定放电深度下,V₂O₅/C电极反应速率受Zn^2＋的扩散过程控制.     

Electrical Properties of Polycrystalline Lithium Chloroboracite Prepared by the Sol-Gel Method

The electrical properties of polycrystalline lithium chloroboracite, Li4B7O12Cl, prepared by the sol-gel method were investigated in connection with their structure. Li4B7O12Cl pellets were prepared with different amounts of hydrochloric acid or ammonium chloride. The kind and amount of the chlorine source affected the formation of by-products (Li2B4O7, LiCl, a glass phase) and the morphology of the Li4B7O12Cl pellets. Thus their conductivity, which is dominated by grain boundary response owing to the high porosity of the materials, was also affected. The formation of Li2B4O7 as a by-product led to a higher activation energy and lower conductivity. In those pellets in which Li2B4O7 did form, an increase of the amount of glass phase led to higher conductivities.     

偏钛酸型锂离子交换剂固相合成反应动力学

偏钛酸型锂离子交换剂固相合成反应动力学钟辉＊郭灵虹（成都理工学院应用化学系成都６１００５９）（四川联合大学分析测试中心成都）关键词偏钛酸锂，离子交换剂，合成，固相反应动力学１９９７－０８－２５收稿，１９９７－１２－１０修回四川省应用基础研究基金资助项...     

Molar volumes and ion pairing of lithium halides in alcohols

The concentration dependence of the apparent molar volumes of lithium halides (and electrolytes in general) in alcohols (and solvents permitting association in general) is, in the first instance, due to changes in the degree of association and to the inherent difference between the apparent molar volumes of the ions and of the ion pairs. Previous publications on the molar volumes of electrolytes in organic solvents, disregarding altogether ion pairing, appear to be incorrect. Data from the literature for lithium chloride and lithium bromide in normal primary alcohols and several branched alcohols from C₁ to C₈ and data from our laboratory for lithium halides in 1-hexanol and 2-ethyl-1-hexanol served for the determination of φ _V and φ _E . Electrical and structural contributions to the values of these functions for the ions and for the ion pairs are discussed.     

锂离子电池正极材料LiMn2O4的合成与晶体结构（英）

Spinel LiMn₂O₄ powders were prepared using two-step synthesis method consisting of solid-state reaction method and citrate modified sol-gel method. The effects of the calcination temperature and the Li/Mn ratio of raw materials were studied on the physicochemical and electrochemical properties of the spinel LiMn₂O₄ powders, such as crystallinity, lattice constant and density. The title compound was characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Polycrystalline LiMn₂O₄ powers calcined at 750 ℃ were found to be composed of very uniformly-sized microcrystal with an average particle size of 300 nm. The improvement in electrochemical properties was mainly attributed to the process of re-grinding by absolute alcohol.     

Mechanism of the thermal decomposition of hydrophosphites of lithium,sodium and potassium

The thermal decomposition of some M ₂ ^I HPO₃ (M-Li, Na, K) phosphites under nitrogen atmosphere was investigated. A stepwise mechanism of thermal decomposition has been proposed.

---

Zusammenfassung Es wurde die thermische Zersetzung von Phosphiten M ₂ ^I HPO₃ (M-Li, Na, K) in Stickstoffatmosphere untersucht. Die Schritte des Mechanismus der thermischen Zersetzung wurden vorgeschlagen.

     

Synthesis of Phosphaformamidines and Phosphaformamidinates

A large‐scale synthetic route to a variety of phosphaformamidines and phosphaformamidinates, a type of derivative that was not accessible by the methods previously known for preparing phosphaamidines and phosphaamidinates, is reported. Thermally stable ethyl N‐arylformimidates 1 (ArN?CH(OEt), Ar=2,4,6‐(Me)₃Ph or 2,6‐(iPr)₂Ph) readily reacted with lithium dialkyl‐ and diarylphosphanides to afford the corresponding N‐aryl phosphaformamidines in 80 and 60 % yield, respectively, whereas with lithium (aryl)(silyl)phosphanide, the N‐aryl‐N‐silylphosphaformamidine (60 % yield) was obtained. Addition of primary lithium arylphosphanides to 1 followed by addition of a stoichiometric amount of nBuLi gave rise to the respective phosphaformamidinates (70–88 % yield). Methanolysis of the products afforded the N‐aryl‐N‐hydrogenophosphaformamidines (90–95 % yield). The solid‐state structure of one of the phosphaformamidinates is also presented.