Preparation of coatings from a series of silicone/fluorine‐functionalized polyacrylates via electrophoretic deposition

Silicone/fluorine‐functionalized polyacrylates were synthesized and subsequently used to prepare corrosion‐resistant transparent coatings via electrophoretic deposition. The coated tin plate with the functionalized polyacrylate had a gloss value higher than 95.0 GU and resisted rust after immersion in a 5 wt% NaCl solution for 10 days. In addition, these coatings remained adhered strongly to the tin plates even after they were bent. It is hoped that this work will provide useful experimental data and assist researchers with the design of applicable coatings with desirable properties. Copyright © 2015 John Wiley & Sons, Ltd.     

激光诱导沉积银膜制备新型光纤SERS传感器

利用激光诱导沉积的方法直接在光纤端面沉积了银纳米膜,并用SERS光谱监测了这一沉积过程,在光纤端面上生成的银膜出现了“年轮”状宏观形貌,这种形貌与激光在光纤中的干涉与衍射条纹分布相一致,证明了这种现象是由激光诱导反应引发的. 结合实验结果进一步讨论了银纳米膜的形成机理. 在光纤上沉积的银纳米膜作为光纤SERS传感器的基底与其它制备基底的方法比较也具有实验操作简便,耗时短,重现性好,SERS增强效果强等诸多优点,是一种非常好的制备光纤SERS传感器基底的方法.     

二甲醚燃料电池复合镍阳极的研究

制备并表征了二甲醚(DME)固体氧化物燃料电池(SOFCs)系列Ni-Fe-La0.8Sr0.2Ga0.8Mg0.115Co0.085O3(LSGMC8.5) 复合阳极, 电极中Ni与Fe的摩尔比分别为9:1、8:2、7:3、5:5, 电极中Ni-Fe的总质量分数为75%. 利用多种技术考察了电极的物相组成, 电极以及电极/电解质界面的微观结构, 电极/电解质界面上进行的DME电化学氧化反应. 结果表明, 复合阳极中Fe含量的增加促进了电极的烧结, 同时改变了电极/电解质界面的微观结构. 电极催化DME电化学氧化的活性依赖于Ni、Fe的比例, Ni、Fe的摩尔比为8:2的电极具有最高的电化学活性. Ni-Fe-LSGMC8.5电极具有较高的催化DME氧化反应的活性与稳定性, 没有观察到电极中存在明显的积碳现象.     

高度分散的Pt/TiO2的制备及光催化活性

用柠檬酸作为空穴捕获剂和分散剂,在温和条件下用光催化还原法将3nm金属铂沉积在7nm的锐钛矿相及介孔二氧化钛纳米晶表面,TEM观察显示铂的负载量为w=1．0％时,多数二氧化钛纳米晶表面沉积了岛状的铂团簇,XPS和电子衍射结果表明铂以游离态存在．负载w=1．0％～2．0％铂的TiO2在苯酚光氧化反应中活性显著提高,Pt/TiO2在氨气中经550℃氮化,可制得氮掺杂的Pt／TiO2可见光光催化剂,氮化过程中铂团簇没有烧结和显著长大。     

碳包覆纳米金属颗粒的合成研究进展

碳包覆纳米金属颗粒是继富勒烯和碳纳米管之后的又一新型纳米碳材料,在许多领域具有广泛应用前景。本文综述了碳包覆纳米金属颗粒的合成方法,包括：电弧放电法、化学气相沉积法、热解法、液相浸渍炭化法和炭凝胶爆炸法等,简述了形成机理,总结了各自的优缺点,并指出将来的发展方向。     

减压化学气相沉积法制备规则螺旋状纳米碳管

以硅胶负载的Co纳米颗粒为催化剂,在低流量的减压体系中通过化学气相沉积法制备了规则螺旋状的纳米碳管.通过TEM和HRTEM研究了螺旋碳管的形貌、尺度分布以及管身、曲面和节点处的晶型;讨论了催化剂制备中pH值对催化剂的尺寸、规则程度和存在形态以致对螺旋碳管产量、管径厚度以及螺旋管的相对比例的影响;此外,还分析了反应压力对碳管生长的影响.     

化学气相淀积法合成氮化铝薄膜及其工艺设计

对ＡｌＢｒ３－ＮＨ３－Ｎ２体系化学气相淀积法合成Ａ１Ｎ膜进行了热力学分析和工艺设计，研究了在不同淀积温度和体系总压时，体系中主要气态物种的平衡分压和Ａ１Ｎ膜的理论淀积速率与源温和载气流量的关系，并与微波等离子体化学气相淀积Ａ１Ｎ膜的实验结果进行了比较。     

氯参与的化学气相淀积金刚石的热力学分析

用非平衡热力学耦合模型研究了金刚石在CHCl体系中的生长,计算所得CHCl体系的金刚石生长的相图与大量实验结果符合良好.通过热力学分析讨论了氯的添加对提高金刚石薄膜生长速率及其质量的影响以及降低淀积温度的作用.     

Process study of thermal plasma chemical vapor deposition of diamond,part I: Substrate material,temperature, and methane concentration

Effects of process parameters on diamond film synthesis in DC thermal plasma jet reactors are discussed including substrate material, methane concentration and substrate temperature. Diamond has been deposited on silicon, molybdenum, tungsten, tantalum, copper, nickel, titanium, and stainless steel. The adhesion of diamond film to the substrate is greatly affected by the type of substrate used. It has been found that the methane concentration strongly affects the grain size of the diamond films. Increased methane concentrations result in smaller grain sizes due to the increased number of secondary nucleations on the existing facets of diamond crystals. Substrate temperature has a strong effect on the morphology of diamond films. With increasing substrate temperature, the predominant orientation of the crystal growth planes changes from the (111) to the (100) planes. Studies of the variation of the film quality across the substrate due to the nonuniformity of thermal plasma jets indicate that microcrystalline graphite formation starts at the corners and edges of diamond crystals when the conditions become unfavorable for diamond deposition.     

稀土掺杂PbO2电极的制备及催化性能研究

以SnCl4.5H2O,Sb2O3,La（NO3）3（或Nd（NO3））为前驱体（摩尔比分别为Sn∶Sb∶La（Nd）=100∶6∶（0.5,1,2）,制备稀土（La,Nd）掺杂Sn,Sb溶胶,以钛电极为基体,用溶胶-凝胶法制备稀土（La,Nd）掺杂SnO2中间层,热处理温度为450和500℃,热处理时间共5 h;采用电沉积法制备PbO2表面层,得到改性PbO2阳极,优化了制备改性PbO2电极的稀土掺杂量。以含油污水为目标有机物,借助于CODCr去除情况分析电极的电催化氧化能力;分析了电极结构与电催化特性之间的关系。采用SEM和XRD分析了制备电极的表面形貌、晶体结构并通过电化学工作站对其析氧电位进行了表征分析。结果表明,中间层掺杂La元素的电极,掺杂比为Sn∶Sb∶La=100∶6∶1时电极性能最好;而中间层掺杂Nd元素,掺杂比为Sn∶Sb∶Nd=100∶6∶2时电极的性能最好,此比例时电极对目标有机物CODCr去除率分别为91.90%和90.93%。